To ensure the infiltration of spiro-OMeTAD into the quantum dot-sensitized photoanode and to consider the limit of the hole diffusion length in the spiro-OMeTAD layer, a rutile TiO2 nanorod array with a length of 200 ...To ensure the infiltration of spiro-OMeTAD into the quantum dot-sensitized photoanode and to consider the limit of the hole diffusion length in the spiro-OMeTAD layer, a rutile TiO2 nanorod array with a length of 200 nm, a diameter of 20 nm and an areal density of 720 ram 2 was successfully prepared using a hydrothermal method with an aqueous-grown solution of 38 mM titanium isopropoxide and 6 M hydrochloric acid at 170 ℃ for 75 min. PbS quantum dots were deposited by a spin coating-assisted successive ionic layer adsorption and reaction (spin-SILAR), and all solid-state PbS quantum dot-sensitized TiO2 nanorod array solar cells were fabricated using spiro-OMeTAD as electrolytes. The results revealed that the average crystal size of PbS quantum dots was -78 nm using Pb(NO3)2 as the lead source and remain unchanged with the increase of the number of spin-SILAR cycles. The all solid-state PbS quantum dot-sensitized TiO2 nanorod array solar cells with spin-SILAR cycle numbers of 20, 30 and 40 achieved the photoelectric conversion efficiencies of 3.74%, 4.12% and 3.11%, respectively, under AM 1.5 G illumination (100 mW/cm2).展开更多
Cable-like Au@SiO2 Janus composite nanorods with PS and PEG grafting on both ends respectively are fabricated by skiving in combination of a post favorable modification. The cable-like Au@SiO2 composite nanofibers are...Cable-like Au@SiO2 Janus composite nanorods with PS and PEG grafting on both ends respectively are fabricated by skiving in combination of a post favorable modification. The cable-like Au@SiO2 composite nanofibers are synthesized in the channel of porous anodic aluminium oxide (AAO) membrane. After skiving, the corresponding composite nanorods are obtained. Following, PEG-SH and PS-SH are conjugated onto the two ends of the nanorods by a selective partial modification, respectively. Length and diameter of the Au@SiO2 Janus composite nanorods can be tuned controllably. It can be extended to fabricate a variety of different Janus nanorods with different compositions and microstructures.展开更多
基金supported by the National Natural Science Foundation of China(51272061,51472071)
文摘To ensure the infiltration of spiro-OMeTAD into the quantum dot-sensitized photoanode and to consider the limit of the hole diffusion length in the spiro-OMeTAD layer, a rutile TiO2 nanorod array with a length of 200 nm, a diameter of 20 nm and an areal density of 720 ram 2 was successfully prepared using a hydrothermal method with an aqueous-grown solution of 38 mM titanium isopropoxide and 6 M hydrochloric acid at 170 ℃ for 75 min. PbS quantum dots were deposited by a spin coating-assisted successive ionic layer adsorption and reaction (spin-SILAR), and all solid-state PbS quantum dot-sensitized TiO2 nanorod array solar cells were fabricated using spiro-OMeTAD as electrolytes. The results revealed that the average crystal size of PbS quantum dots was -78 nm using Pb(NO3)2 as the lead source and remain unchanged with the increase of the number of spin-SILAR cycles. The all solid-state PbS quantum dot-sensitized TiO2 nanorod array solar cells with spin-SILAR cycle numbers of 20, 30 and 40 achieved the photoelectric conversion efficiencies of 3.74%, 4.12% and 3.11%, respectively, under AM 1.5 G illumination (100 mW/cm2).
基金supported by the National Natural Science Foundation of China(Nos. 51233007 and 51622308)
文摘Cable-like Au@SiO2 Janus composite nanorods with PS and PEG grafting on both ends respectively are fabricated by skiving in combination of a post favorable modification. The cable-like Au@SiO2 composite nanofibers are synthesized in the channel of porous anodic aluminium oxide (AAO) membrane. After skiving, the corresponding composite nanorods are obtained. Following, PEG-SH and PS-SH are conjugated onto the two ends of the nanorods by a selective partial modification, respectively. Length and diameter of the Au@SiO2 Janus composite nanorods can be tuned controllably. It can be extended to fabricate a variety of different Janus nanorods with different compositions and microstructures.