Chemicals Used in Polymeric Material Coated Waste Paper Composites

In this research, at different quantities as fillers, Boric Acid, Calcite (CaCO3), SPT (Sodium Perborate Tetrahydrate) and as coupling matters, 3%, MAPE (Maleic Anhydride Grafted Polyethylene), Titanate and Silanyl (Vinyltriethoxysilane) were added waste paper. Composite boards were pressed and cut in 1 × 30 × 30 cm. In order to identify some properties of the produced boards, experimental works were applied according to the standards. In conclusion, bending stress reduced with filler materials and chemicals was reduced even more than the bending stress except for some experimental groups. In addition, it was observed that the coupling chemicals increased the bending strength and modulus of elasticity compared to the fillers.

Material Selection of a Natural Fibre Reinforced Polymer Composites using an Analytical Approach

Material selection has become a critical part of design for engineers,due to availability of diverse choice of materials that have similar properties and meet the product design specification.Implementation of statistical analysis alone makes it difficult to identify the ideal composition of the final composite.An integrated approach between statistical model and micromechanical model is desired.In this paper,resultant natural fibre and polymer matrix from previous study is used to estimate the mechanical properties such as density,Young’s modulus and tensile strength.Four levels of fibre loading are used to compare the optimum natural fibre reinforced polymer composite(NFRPC).The result from this analytical approach revealed that kenaf/polystyrene(PS)with 40%fibre loading is the ideal composite in automotive component application.It was found that the ideal composite score is 1.156 g/cm^(3),24.2 GPa and 413.4 MPa for density,Young’s modulus and tensile strength,respectively.A suggestion to increase the properties on Young’s modulus are also presented.This work proves that the statistical model is well incorporated with the analytical approach to choose the correct composite to use in automotive application.

A Comparative Investigation of the Biodegradation Behaviour of Linseed Oil-Based Cross-Linked Composites Filled with Industrial Waste Materials in Two Different Soils

The biodegradation of polymeric biocomposites formed from epoxidized linseed oil and various types of fillers(pine needles,pine bark,grain mill waste,rapeseed cake)and a control sample without filler was studied during 180 days of exposure to two types of forest soil:deciduous and coniferous.The weight loss,morphological,and structural changes of polymer composites were noticed after 180 days of the soil burial test.The greatest weight loss of all tested samples was observed in coniferous forest soil(41.8%–63.2%),while in deciduous forest soil,it ranged between 37.7%and 42.3%.The most significant changes in the intensities of the signals evaluated by attenuated total reflectance infrared spectroscopy,as well as morphological changes determined by scanning electron microscopy,were assessed for polymer composite with rapeseed cake and specimen without filler in coniferous forest soil and are in a good agreement with weight loss results.Whereas significantly lower changes in weight loss,morphology,and structure of polymeric film with pine bark were noticed in both soils.It was suggested that fungi of Trichoderma,Penicillium,Talaromyces and Clonostachys genera are the possible soil microorganisms that degrade linseed oil-based cross-linked polymer composites.Moreover,the novel polymer composites have the potential to be an environmentally friendly alternative to petroleum-based mulching films.

The Packaging Materials with Carbon Nanotube/Polymer Composites

A polymer-based carbon nano-tubes (CNTs) composite with high electromagnetic (EM) wave shielding effectiveness (SE) and with high mechanical property is developed for packaging of electronic modulus or devices.The liquid crystal polymers (LCP) and melamine formaldehydes (MF) polymer are used to study the orientation effect of CNTs in various polymeric matrix.The influences of orientation,aspect ratio,and mass fraction of CNTs upon the shielding effectiveness (SE) of CNTs-composites are investigated.The higher the orientation,aspect ratio,and weight percentages of nano-materials are, the higher the SE of the carbon composites.The highest SE for the CNTs/LCP nano composite obtained is more than 62 dB. This results may lead to the developing for CPU IC chip packaging.

Durability Testing of Composite Aerospace Materials Based on a New Polymer Carbon Fiber-Reinforced Epoxy Resin

In this study,the durability of a new polymer carbonfiber-reinforced epoxy resin used to produce composite material in the aerospacefield is investigated through analysis of the corrosion phenomena occurring at the microscopic scale,and the related infrared spectra and thermal properties.It is found that light and heat can con-tribute to the aging process.In particular,the longitudinal tensile strength displays a non-monotonic trend,i.e.,itfirst increases and then decreases over time.By contrast,the longitudinal compressive and inter-laminar shear strengths do not show significant changes.It is also shown that the inter-laminar shear strength of carbonfiber/epoxy resin composites with inter-laminar hybrid structure is better than that of pure carbonfiber materials.The related resistance to corrosion can be improved by more than 41%.

A review on machinability of carbon fiber reinforced polymer(CFRP)and glass fiber reinforced polymer(GFRP)composite materials

Fiber reinforced polymer(FRP) composite materials are heterogeneous and anisotropic materials that do not exhibit plastic deformation. They have been used in a wide range of contemporary applications particularly in space and aviation,automotive,maritime and manufacturing of sports equipment. Carbon fiber reinforced polymer(CFRP) and glass fiber reinforced polymer(GFRP) composite materials,among other fiber reinforced materials,have been increasingly replacing conventional materials with their excellent strength and low specific weight properties. Their manufacturability in varying combinations with customized strength properties,also their high fatigue,toughness and high temperature wear and oxidation resistance capabilities render these materials an excellent choice in engineering applications.In the present review study,a literature survey was conducted on the machinability properties and related approaches for CFRP and GFRP composite materials. As in the machining of all anisotropic and heterogeneous materials,failure mechanisms were also reported in the machining of CFRP and GFRP materials with both conventional and modern manufacturing methods and the results of these studies were obtained by use of variance analysis(ANOVA),artificial neural networks(ANN) model,fuzzy inference system(FIS),harmony search(HS) algorithm,genetic algorithm(GA),Taguchi's optimization technique,multi-criteria optimization,analytical modeling,stress analysis,finite elements method(FEM),data analysis,and linear regression technique. Failure mechanisms and surface quality is discussed with the help of optical and scanning electron microscopy,and profilometry. ANOVA,GA,FEM,etc. are used to analyze and generate predictive models.

Design Details of Low-Energy and Passive Houses Using Composites from Waste Raw Materials

The article deals with potential use of waste materials in construction industry, specifically use of high density polyethylene （HDPE）. The article is focused in particular on recycled polyethylene application in products designed for construction industry, especially for passive houses. Currently certain building details of passive houses are not perfect or their solution results in higher economic demands related to house purchase and its further use. For the purpose of this thesis details of windows installation in external walls and elimination of thermal bridges in wall footing have been chosen. Products were subject to mathematic modelling of thermal technique and statics. The executed mathematic models documented that products are fully functional and that the suggested product successfully eliminate insufficiencies of some currently applied solutions.

Synthesis, properties, and applications of large-scale two-dimensional materials by polymer-assisted deposition

Two-dimensional(2D) materials have attracted considerable attention because of their novel and tunable electronic,optical, ferromagnetic, and chemical properties. Compared to mechanical exfoliation and chemical vapor deposition, polymer-assisted deposition(PAD) is more suitable for mass production of 2D materials owing to its good reproducibility and reliability. In this review, we summarize the recent development of PAD on syntheses of 2D materials. First, we introduce principles and processing steps of PAD. Second, 2D materials, including graphene, MoS2, and MoS2/glassy-graphene heterostructures, are presented to illustrate the power of PAD and provide readers with the opportunity to assess the method. Last, we discuss the future prospects and challenges in this research field. This review provides a novel technique for preparing 2D layered materials and may inspire new applications of 2D layered materials.

In-Situ Composition and Luminescence of Europium and Terbium Coordination Polymers/PEMA Hybrid Thick Films

Europium and terbium coordination polymers of pyridine-3-carboxylic acid were in-situ composed with ethyt methacrylate （ EMA ）. With the polymerization of EMA monomer and the formation of europium and terbium coordination polymers of pyridiae- 3-carboxylic acid, the transparent hybrid thick fihns composed of [ Eu（ NIC ）3 ]n （ [ Tb（ NIC）3 ]n ） and poly ethyl mettuwrylate （ PEMA ） have been prepared. The luminescence properties and energy transfer of these polymeric composites were studied with absorption spectra, fluorescent excitation trod emission spectra in detail. All the hybrid thick films composed of terbium coordination polymer show the characteristic strong green emission of terbium ions, which implies the same energy transfer mechanism as the pure complex and the hybrid composite film is a suitable sabstrate for the luminescence of terbium ions. In the range of camposing concentration of luminescent species （0.01,0.025,0.05,0.1 mmol /15 mL EMA ）, emission intensities increase with the increasing of corresponding composing concentration and the concentration quenching effect does not take place.

Anisotropic Thermally-Accessible Lattice Distortion of a Cu（ll）-Cr（VI） Complex Bimetallic Oxide by Adsorbing a Chiral One-Dimensional Cu（ll）-Cr（VI） Coordination Polymer

The authors have prepared and characterized a chiral one-dimensional Cu（II）-Cr（VI） coordination polymer, [CuL2][Cr207] （L = （IR, 2R）-diaminocyclohexane）, which exhibited intense d-d bands as well as charge transfer bands in the solid state electronic and CD spectra. Thermally-accessible lattice distortion was observed along the crystallographic a axis, which corresponded to Jahn-Teller distortion of Cu（II） chromophores. After firing [CuL2][Cr207], they could obtain a Cu（II）-Cr（VI） complex bimetallic oxide showing ferromagnetism and isotropic thermally-accessible lattice distortion. Preparation of composite materials of the coordination polymers and a complex bimetallic oxide could be confirmed by IR spectra and magnetic properties. It should be noted that the complex bimetallic oxide as the composite exhibited anisotropic thermally-accessible lattice distortion by adsorption of the chiral one-dimensional coordination polymer.

Mechanically Strong and Highly Stiff Supramolecular Polymer Composites Repairable at Ambient Conditions

It is a formidable challenge to fabricate healable polymeric materials with high mechanical strength and stiffness due to the highly suppressed diffusion of their polymer chains.Herein,a high-strength,highly stiff,andrepairable/healable supramolecular polymercomposite was fabricatedby complexingpoly(acrylic acid)(PAA)and poly(allylamine hydrochloride)(PAH)in aqueous solutions,followed by molding into desired shapes.Exquisitely tuning the electrostatic and H-bonding interactions between PAA and PAH led to associative phase-separation and in situ formation of nanostructures in the resultant PAA–PAH composites.

Effects of Content of Chopped Glass Fibers on the Properties of Silica Filled PTFE Composites

In this work, the polytetrafluoroethylene (PTFE)-based composite substrates were manufactured by mixing, calendering, hot-pressing sintering. The composition of all the samples was PTFE, SiO2 and chopped E-glass fibers. The effects of content of E-glass fibers on the properties of the SiO2 filled PTFE composites were investigated, including density, water absorption, dielectric properties (εr, tanδ), coefficient of thermal expansion (CTE) and temperature coefficient of dielectric constant (τε). The compositions of inorganic materials mixture are (62 ? x) % SiO2 + x % E-glass fiber (x: mass ratio to composites, x = 0, 1, 1.5, 2, 2.5, 3). The results show that as the content of E-glass fibers is 2.5 wt.%, this composite obtains optimal properties, including excellent dielectric properties (εr^2.9123, tanδ~0.0011), acceptable water absorption of 0.075%, temperature coefficient of dielectric constant of 10 ppm/?C and coefficient of thermal expansion of 15.87 ppm/?C.

The Polymeric Heterogemeous Matrix for Carbon and Glass Reinforced Plastic

This article presents the results of deformation-strength properties measurement and microstructural analysis of heterogeneous polymer matrix consisting of thermoset and thermoplastic polymers. Thermosetting material is a diamino-diphenil sulfon-cured epoxy oligomer. Polysulfone was used as thermoplastic material. Two different technological processes were used to obtain heterogeneous polymer matrix: the material was mixed in the block, or layered material was produced in which a layer of thermoplastic material alternated with a layer of epoxy oligomer.

Study on Polymer Films with Thermal Stability

New polymer film materials with good properties are reported. The difference between positive and negative coronas is also given. The films have good transmittance, excellent thermal and long-term stability, low dielectric constant, and high glass transition temperature.

Predictions of Storage Modulus of Glass Bead-Filled Low-Density-Polyethylene Composites

The factors affecting storage modulus (Ec') and quantitative characterization of polymer composites filled with inorganic particles were discussed in this paper. On the basis of Eshelby’s method and Mori’s work, an equation describing the relationship between the Ec' and the filler volume fraction, particle geometry as well as interfacial morphology was proposed. The Ec' of the glass bead filled low-density-polyethylene (LDPE/GB) composites was estimated by means of this equation under experimental conditions with temperature range of –150-100?C, frequency of 1 Hz and the amplitude of 0.6 mm, and compared with other equations proposed in literature. The results showed that the predictions for this equation were close to the measured data from the LDPE/GB composites.

Research Progress on the Preparation of Inorganic/Natural Materials Composite Microspheres

Microspheres are a new type of drug carrier with great potential for development and application.Natural polymers have good biocompatibility,biodegradability,and are easily dispersed in living organisms,making them suitable for preparing microspheres.Inorganic materials(mainly inorganic minerals)have excellent mechanical properties and are inexpensive and easy to obtain.Through the coupling and hybridization of natural polymers and inorganic materials,they can complement each other's advantages and synergistically enhance efficiency,resulting in many excellent physical and chemical properties.Inorganic materials/natural polymer composite microspheres can be prepared by modifying natural polymers with inorganic materials through various methods such as emulsification crosslinking,solution mixing,in-situ synthesis,extrusion,etc.The application of inorganic materials/natural polymer composite microspheres in drug delivery systems has significant sustained-release effects,is safe and non-toxic,and the cost of carrier materials is relatively low,which has certain significance for the development of new drug carriers.This article reviews the recent research on the preparation,drug loading and release properties of inorganic material/natural polymer composite microspheres,analyzes the advantages and disadvantages of commonly used preparation methods,and looks forward to the development direction of composite microspheres.

Branched Fluorine/Adamantane Interfacial Compatibilizer for PBO Fibers/Cyanate Ester Wave-Transparent Laminated Composites

Comprehensive Summary Branched fluorine/adamantane PBO precursor(preFABPBO),synthesized via random co-condensation between 2,2-bis(3-amino-4-hydroxyphenyl)hexafluoro propane,1,3-adamantanedicarbonyl dichloride,and trimesoyl chloride,is performed as interfacial compatibilizer,bisphenol A dicyanate ester(BADCy)resin as polymer matrix,and poly(p-phenylene-2,6-benzobisoxazole)(PBO)fibers as reinforcements to prepare PBO fibers/FABPBO-BADCy wave-transparent laminated composites by high temperature molding.The mechanical properties,wave-transparent performances,and heat resistances of PBO fibers/BADCy composites are simultaneously improved by the addition of preFABPBO.The interlaminar shear strength(ILSS)and flexural strength of PBO fibers/FABPBO-BADCy composites are 48.9 and 665.3 MPa,respectively,increased by 33.2%and 13.3%compared to those of PBO fibers/BADCy composites(36.7 and 587.4 MPa).The dielectric constant and dielectric loss values at 106 Hz are 2.53 and 0.003,respectively,lower than those of PBO fibers/BADCy composites(3.06 and 0.006),and the corresponding wave transmission efficiency is 94.8%,which also presents excellent stability over the wide temperature(25-200℃)and frequency range(103-107 Hz and 8.2-12.4 GHz).Meanwhile,the heat resistance index and glass transition temperature are 229.9℃and 247.5℃,also better than those of PBO fibers/BADCy composites(229.6℃and 247.1℃).

Temperature and strain registration by fibre-optic strain sensor in the polymer composite materials manufacturing

The presence of process-induced strains induced by various manufacturing and operational factors is one of the characteristics of polymer composite materials(PCM).Conventional methods of registration and evaluation of process-induced strains can be laborious,time-consuming and demanding in terms of technical applications.The employment of embedded fibre-optic strain sensors(FOSS)offers a real prospect of measuring residual strains.This paper demonstrates the potential for using embedded FOSS for recording technological strains in a PCM plate.The PCM plate is manufactured from prepreg,using the direct compression-moulding method.In this method,the prepared reinforcing package is placed inside a mould,heated,and then exposed to compaction pressure.The examined technology can be used for positioning FOSS between the layers of the composite material.Fibre-optic sensors,interacting with the material of the examined object,make it possible to register the evolution of the strain process during all stages of polymer-composite formation.FOSS data were recorded with interrogator ASTRO X 327.The obtained data were processed using specially developed algorithms.

Regulatable Orthotropic 3D Hybrid Continuous Carbon Networks for Efficient Bi-Directional Thermal Conduction

Vertically oriented carbon structures constructed from low-dimen-sional carbon materials are ideal frameworks for high-performance thermal inter-face materials(TIMs).However,improving the interfacial heat-transfer efficiency of vertically oriented carbon structures is a challenging task.Herein,an orthotropic three-dimensional(3D)hybrid carbon network(VSCG)is fabricated by depositing vertically aligned carbon nanotubes(VACNTs)on the surface of a horizontally oriented graphene film(HOGF).The interfacial interaction between the VACNTs and HOGF is then optimized through an annealing strategy.After regulating the orientation structure of the VACNTs and filling the VSCG with polydimethylsi-loxane(PDMS),VSCG/PDMS composites with excellent 3D thermal conductive properties are obtained.The highest in-plane and through-plane thermal conduc-tivities of the composites are 113.61 and 24.37 W m^(-1)K^(-1),respectively.The high contact area of HOGF and good compressibility of VACNTs imbue the VSCG/PDMS composite with low thermal resistance.In addition,the interfacial heat-transfer efficiency of VSCG/PDMS composite in the TIM performance was improved by 71.3%compared to that of a state-of-the-art thermal pad.This new structural design can potentially realize high-performance TIMs that meet the need for high thermal conductivity and low contact thermal resistance in interfacial heat-transfer processes.

含氟高分子材料包覆铝核壳材料研究进展

金属铝(Al)具有高燃烧热值、高密度、低耗氧量等优异性能,是固体复合推进剂领域最受青睐的金属添加剂。为了提高固体复合推进剂的性能,有必要采取措施对Al进行包覆改性。近年来含氟高分子包覆Al因其优异的综合性能而受到广泛关注。介绍了不同种类的含氟高分子包覆金属Al核壳材料、不同包覆方法、Al核壳材料的性能以及含氟高分子与Al的作用机理,总结发现通过Al核壳结构设计、含氟高分子引入和Al颗粒表面的自活化策略等途径,含氟高分子与氧化铝层之间的表面发生剧烈的氧化过程,增强Al核壳材料点火和燃烧性能,显著改善推进剂的燃烧团聚和燃烧效率。但目前含氟高分子包覆Al核壳材料研究过程仍存在许多不足,如缺乏新型多元含氟高分子包覆Al的能量性能的研究;缺乏Al颗粒与包覆层在高升温速率下作用机理的认识;包覆效率和批量制备能力低,阻碍了其实际应用等。未来可从进一步增强朝着研发新型含氟聚合物、研究对反应历程中产物的实时捕捉和开发工业化生产制造技术等方向发展。