Hydride ion(H-)conductors have drawn much attention due to their potential applications in hydrideion-based devices.Rare earth metal hydrides(REH_(x))have fast H-conduction which,unfortunately,is accompanied by detrim...Hydride ion(H-)conductors have drawn much attention due to their potential applications in hydrideion-based devices.Rare earth metal hydrides(REH_(x))have fast H-conduction which,unfortunately,is accompanied by detrimental electron conduction preventing their application as ion conductors.Here,REH_(x)(RE=Nd,Ce,and Pr)with varied grain sizes,rich grain boundaries,and defects have been prepared by ball milling and subsequent sintering.The electronic conductivity of the ball-milled REH_(x)samples can be reduced by 2-4 orders of magnitude compared with the non-ball-milled samples.The relationship of electron conduction and miscrostructures in REH_(x)is studied and discussed based on experimental data and previously-proposed classical and quantum theories.The H-conductivity of all REH_(x)is about 10^(-4)to 10^(-3)S cm^(-1)at room temperature,showing promise for the development of H-conductors and their applications in clean energy storage and conversion.展开更多
Given the carbon peak and carbon neutrality era,there is an urgent need to develop high-strength steel with remarkable hydrogen embrittlement resistance.This is crucial in enhancing toughness and ensuring the utilizat...Given the carbon peak and carbon neutrality era,there is an urgent need to develop high-strength steel with remarkable hydrogen embrittlement resistance.This is crucial in enhancing toughness and ensuring the utilization of hydrogen in emerging iron and steel materials.Simultaneously,the pursuit of enhanced metallic materials presents a cross-disciplinary scientific and engineering challenge.Developing high-strength,toughened steel with both enhanced strength and hydrogen embrittlement(HE)resistance holds significant theoretical and practical implications.This ensures secure hydrogen utilization and further carbon neutrality objectives within the iron and steel sector.Based on the design principles of high-strength steel HE resistance,this review provides a comprehensive overview of research on designing surface HE resistance and employing nanosized precipitates as intragranular hydrogen traps.It also proposes feasible recommendations and prospects for designing high-strength steel with enhanced HE resistance.展开更多
Living in a world of heavy industrialization and confronted by the ever-deteriorating environment,the human race is now undertaking serious efforts to reach the target of carbon neutrality.One major step is to promote...Living in a world of heavy industrialization and confronted by the ever-deteriorating environment,the human race is now undertaking serious efforts to reach the target of carbon neutrality.One major step is to promote the development of sustainable electrochemical energy storage and conversion technologies based on green resources instead of the traditional nonreusable petroleum-based technologies.As an almost inexhaustible bioresource,nanocellulose derived from natural biomass exhibits outstanding physiochemical properties that could be well leveraged to bring about numerous opportunities for electrochemical processes.Through structure engineering,nanocellulose with a width of a few tens of nanometers and a length of up to micrometers could be realized.The drastic reduction in dimensions leads to superior mechanical,optical,and functional properties inaccessible to the bulky cellulose counterpart.In this review,different types of nanocellulose with distinctive physiochemical properties and their respective preparation methods are first examined.This is followed by a detailed and insightful analysis of the superiority and unprecedented performance gains that nanocellulose imparts to different electrochemical energy storage and conversion applications as a result of nanosizing.Finally,we humbly put forward our perspectives on the problems regarding current studies as well as on the future research direction for nanocellulose-mediated electrochemical processes to enable practical applications.This review is intended as guidance to initiate cross-disciplinary research effort in this engaging field and help evoke inspiration to effect solutions to critical energy issues of the day.展开更多
Gas drainage is an efective technology for gas control in coal mines.A high borehole-sealing quality is the fundamental precondition for efcient gas drainage.The expansibilities of cement pastes used in borehole-seali...Gas drainage is an efective technology for gas control in coal mines.A high borehole-sealing quality is the fundamental precondition for efcient gas drainage.The expansibilities of cement pastes used in borehole-sealing processes are critical for the borehole-sealing efect.Nanosized magnesia expansive agents are used to improve the expansibilities of cement pastes and improve the borehole-sealing efect.Nuclear magnetic resonance spectrometry and scanning electron microscopy were adopted to study the efects of nanosized magnesia on the hydration of borehole-sealing cements used with diferent preparation methods.The results showed that an increase in the mass fraction of the nanosized magnesia promoted cement hydration,and the mass fraction was positively correlated with the promotion efect.The use of diferent preparation methods did not change the water-phase distribution in the cement.When using the wet-mixing preparation method,nanosized magnesia promoted the induction,acceleration,and deceleration periods of hydration;when using the dry-mixing preparation method,the nanosized magnesia promoted the induction period of cement hydration,and the promotion efect was less obvious than that seen when using the wet-mixing method.When using the wet-mixing preparation method,the nanosized magnesia was uniformly dispersed,thus enlarging the surface area of the reaction,which provided more nucleation sites for the hydration products of the cement and therefore accelerated the hydration reaction.When using the dry-mixing preparation method,the nanosized magnesia powders were dispersed nonuniformly and aggregated.Under these conditions,only a few nanosized magnesia particles on the surfaces of the aggregated clusters took part in hydration,so only a small number of nucleation sites were provided for the hydration products of cement.This led to inconsistent hydration of cement pastes prepared using the dry-mixing method.The surface porosity of the cement prepared with the wet-mixing preparation method frst decreased and then increased with increases in the mass fraction of the nanosized magnesia.The cement surface exhibited compact hydration products and few pores,and the surface was relatively smooth.In comparison,the surface porosity of the cement prepared using the dry-mixing method fuctuated with increasing mass fraction of the nanosized magnesia,resulting in a rough cement surface and microfractures on some surfaces.The two preparation methods both reduced the surface porosity of the cement.The wet-mixing preparation was more efective and consistent in improving the compactness of the cement than the dry-mixing preparation.These results provide important guidance on the addition of nanosized magnesia in borehole-sealing engineering and the selection of cement preparation methods,and they also lay a solid foundation for realizing safe and efcient gas drainage.展开更多
The development of highly effective metal-zeolite bifunctional catalysts for the hydroisomerization of n-alkanes is a paramount strategy to produce second-generation biofuels with high quality.In this study,polyhexame...The development of highly effective metal-zeolite bifunctional catalysts for the hydroisomerization of n-alkanes is a paramount strategy to produce second-generation biofuels with high quality.In this study,polyhexamethylene biguanide hydrochloride(PHMB)is precisely added to the initial gel to synthesize nanosized ZSM-23 zeolites(Z23-x PH).Due to orientation adsorption and steric hindrance effects of PHMB,each sample of Z23-x PH demonstrates enhanced mesoporosity in comparison with the conventional Z23-C zeolite.Furthermore,the Bronsted acid density of the Z23-x PH samples is also signifi cantly reduced due to a reduction in the distribution of framework Al at T2-T5 sites.The corresponding Pd/23-C and Pd/Z23-x PH bifunctional catalysts with 0.5 wt%Pd loading for n-hexadecane hydroisomerization are prepared by incorporating ZSM-23 zeolites as acid supports.According to the catalytic test results,the suitable addition of PHMB can effectively promote the iso-hexadecane yield.The Pd/Z23-2PH catalyst with an n_(PHMB)/n(_Si)molar ratio of 0.002 demonstrates the highest maximum iso-hexadecane yield of 74.1%at an n-hexadecane conversion of 88.3%.Therefore,the employment of PHMB has provided a simple route for the development of highly effective Pd/ZSM-23 catalysts for n-alkane hydroisomerization.展开更多
The plasma catalytic degradation of o-xylene in simulated air was improved by loading low amounts of Pt,Pd,or Au onto Co_(3)O_(4).At room temperature,o-xylene conversion and CO_(x)selectivity using a0.1 wt%Pt/Co_(3)O_...The plasma catalytic degradation of o-xylene in simulated air was improved by loading low amounts of Pt,Pd,or Au onto Co_(3)O_(4).At room temperature,o-xylene conversion and CO_(x)selectivity using a0.1 wt%Pt/Co_(3)O_(4)catalyst reached 98.9%and 80%,and the energy efficiency was at the top level in comparison with values in the literature.A stable o-xylene degradation performance could be obtained by online regenerating the heat-insulated reactor with a high energy density.After characterization,it was found that the loading of nanosized Pt not only increased the Co^(3+)/Co^(2+)ratio,where the Co^(3+)benefitted the formation of reactive oxygen species,but also conduced Pt^(0)to oxygen activation,resulting in effective promotion of complete o-xylene oxidation.Operando plasma diffuse reflectance infrared Fourier transform spectroscopy demonstrated the complete o-xylene oxidation and proved that Pt played a key role in the complete oxidation of o-xylene.展开更多
Nanosized NaY crystals have been prepared from metakaolin and sodium silicate by confined space synthesis with starch additive. It is found that the product has a narrow crystal size distribution (50-100 nm), high Si...Nanosized NaY crystals have been prepared from metakaolin and sodium silicate by confined space synthesis with starch additive. It is found that the product has a narrow crystal size distribution (50-100 nm), high Si/Al ratio (Si/Al=4.6-6.1), high surface area (1090 m2/g) and the average diameter of nanosized NaY (75 nm) synthesized is 30 nm, it is smaller than that of without starch additive.展开更多
基金supported by the National Key Research and Development Program of China(2021YFB4000602)the National Natural Science Foundation of China(21988101,22279130,21633011)+1 种基金the Dalian Science and Technology Innovation Fund(2023RJ016)the Liaoning Revitalization Talents Program(x LYC2002076)。
文摘Hydride ion(H-)conductors have drawn much attention due to their potential applications in hydrideion-based devices.Rare earth metal hydrides(REH_(x))have fast H-conduction which,unfortunately,is accompanied by detrimental electron conduction preventing their application as ion conductors.Here,REH_(x)(RE=Nd,Ce,and Pr)with varied grain sizes,rich grain boundaries,and defects have been prepared by ball milling and subsequent sintering.The electronic conductivity of the ball-milled REH_(x)samples can be reduced by 2-4 orders of magnitude compared with the non-ball-milled samples.The relationship of electron conduction and miscrostructures in REH_(x)is studied and discussed based on experimental data and previously-proposed classical and quantum theories.The H-conductivity of all REH_(x)is about 10^(-4)to 10^(-3)S cm^(-1)at room temperature,showing promise for the development of H-conductors and their applications in clean energy storage and conversion.
基金the National Key Research and Development Program of China(No.2022YFB3709000)the National Natural Science Foundation of China(Nos.52201060 and 51922002)+2 种基金the China Postdoctoral Science Foundation(Nos.BX20220035 and 2022M710347)Science Center for Gas Turbine Project(No.P2022-B-IV-008-001)the Open Fund of State Key Laboratory of New Metal Materials,University of Science and Technology Beijing(No.2022Z-18)。
文摘Given the carbon peak and carbon neutrality era,there is an urgent need to develop high-strength steel with remarkable hydrogen embrittlement resistance.This is crucial in enhancing toughness and ensuring the utilization of hydrogen in emerging iron and steel materials.Simultaneously,the pursuit of enhanced metallic materials presents a cross-disciplinary scientific and engineering challenge.Developing high-strength,toughened steel with both enhanced strength and hydrogen embrittlement(HE)resistance holds significant theoretical and practical implications.This ensures secure hydrogen utilization and further carbon neutrality objectives within the iron and steel sector.Based on the design principles of high-strength steel HE resistance,this review provides a comprehensive overview of research on designing surface HE resistance and employing nanosized precipitates as intragranular hydrogen traps.It also proposes feasible recommendations and prospects for designing high-strength steel with enhanced HE resistance.
基金supported by the National Natural Science Foundation of China(Nos.51933007,51673123,51803141)National Key R&D Program of China(No.2017YFE0111500).
文摘Living in a world of heavy industrialization and confronted by the ever-deteriorating environment,the human race is now undertaking serious efforts to reach the target of carbon neutrality.One major step is to promote the development of sustainable electrochemical energy storage and conversion technologies based on green resources instead of the traditional nonreusable petroleum-based technologies.As an almost inexhaustible bioresource,nanocellulose derived from natural biomass exhibits outstanding physiochemical properties that could be well leveraged to bring about numerous opportunities for electrochemical processes.Through structure engineering,nanocellulose with a width of a few tens of nanometers and a length of up to micrometers could be realized.The drastic reduction in dimensions leads to superior mechanical,optical,and functional properties inaccessible to the bulky cellulose counterpart.In this review,different types of nanocellulose with distinctive physiochemical properties and their respective preparation methods are first examined.This is followed by a detailed and insightful analysis of the superiority and unprecedented performance gains that nanocellulose imparts to different electrochemical energy storage and conversion applications as a result of nanosizing.Finally,we humbly put forward our perspectives on the problems regarding current studies as well as on the future research direction for nanocellulose-mediated electrochemical processes to enable practical applications.This review is intended as guidance to initiate cross-disciplinary research effort in this engaging field and help evoke inspiration to effect solutions to critical energy issues of the day.
基金supported by“Overall Rationing System”Project of Chongqing Talent Program(cstc2022ycjh-bgzxm0077)the National Natural Science Foundation of China(52074041)+1 种基金Natural Science Foundation of Chongqing,China(cstc2020jcyj-msxmX0836)Fundamental Research Funds for the Central Universities(2020CDJ-LHZZ-002),which are gratefully acknowledged.
文摘Gas drainage is an efective technology for gas control in coal mines.A high borehole-sealing quality is the fundamental precondition for efcient gas drainage.The expansibilities of cement pastes used in borehole-sealing processes are critical for the borehole-sealing efect.Nanosized magnesia expansive agents are used to improve the expansibilities of cement pastes and improve the borehole-sealing efect.Nuclear magnetic resonance spectrometry and scanning electron microscopy were adopted to study the efects of nanosized magnesia on the hydration of borehole-sealing cements used with diferent preparation methods.The results showed that an increase in the mass fraction of the nanosized magnesia promoted cement hydration,and the mass fraction was positively correlated with the promotion efect.The use of diferent preparation methods did not change the water-phase distribution in the cement.When using the wet-mixing preparation method,nanosized magnesia promoted the induction,acceleration,and deceleration periods of hydration;when using the dry-mixing preparation method,the nanosized magnesia promoted the induction period of cement hydration,and the promotion efect was less obvious than that seen when using the wet-mixing method.When using the wet-mixing preparation method,the nanosized magnesia was uniformly dispersed,thus enlarging the surface area of the reaction,which provided more nucleation sites for the hydration products of the cement and therefore accelerated the hydration reaction.When using the dry-mixing preparation method,the nanosized magnesia powders were dispersed nonuniformly and aggregated.Under these conditions,only a few nanosized magnesia particles on the surfaces of the aggregated clusters took part in hydration,so only a small number of nucleation sites were provided for the hydration products of cement.This led to inconsistent hydration of cement pastes prepared using the dry-mixing method.The surface porosity of the cement prepared with the wet-mixing preparation method frst decreased and then increased with increases in the mass fraction of the nanosized magnesia.The cement surface exhibited compact hydration products and few pores,and the surface was relatively smooth.In comparison,the surface porosity of the cement prepared using the dry-mixing method fuctuated with increasing mass fraction of the nanosized magnesia,resulting in a rough cement surface and microfractures on some surfaces.The two preparation methods both reduced the surface porosity of the cement.The wet-mixing preparation was more efective and consistent in improving the compactness of the cement than the dry-mixing preparation.These results provide important guidance on the addition of nanosized magnesia in borehole-sealing engineering and the selection of cement preparation methods,and they also lay a solid foundation for realizing safe and efcient gas drainage.
基金funded by the National Key Research and Development Project,Intergovernmental International Science and Technology Innovation Cooperation Key Project(No.2018YFE0108800)National Natural Science Foundation of China(No.22278115)Heilongjiang Province Natural Science Foundation(No.YQ2021B010).
文摘The development of highly effective metal-zeolite bifunctional catalysts for the hydroisomerization of n-alkanes is a paramount strategy to produce second-generation biofuels with high quality.In this study,polyhexamethylene biguanide hydrochloride(PHMB)is precisely added to the initial gel to synthesize nanosized ZSM-23 zeolites(Z23-x PH).Due to orientation adsorption and steric hindrance effects of PHMB,each sample of Z23-x PH demonstrates enhanced mesoporosity in comparison with the conventional Z23-C zeolite.Furthermore,the Bronsted acid density of the Z23-x PH samples is also signifi cantly reduced due to a reduction in the distribution of framework Al at T2-T5 sites.The corresponding Pd/23-C and Pd/Z23-x PH bifunctional catalysts with 0.5 wt%Pd loading for n-hexadecane hydroisomerization are prepared by incorporating ZSM-23 zeolites as acid supports.According to the catalytic test results,the suitable addition of PHMB can effectively promote the iso-hexadecane yield.The Pd/Z23-2PH catalyst with an n_(PHMB)/n(_Si)molar ratio of 0.002 demonstrates the highest maximum iso-hexadecane yield of 74.1%at an n-hexadecane conversion of 88.3%.Therefore,the employment of PHMB has provided a simple route for the development of highly effective Pd/ZSM-23 catalysts for n-alkane hydroisomerization.
基金supported by National Natural Science Foundation of China(No.12075037)Research and Application Service Platform Project of API Manufacturing Environmental Protection and Safety Technology in China(No.2020-0107-3-1)。
文摘The plasma catalytic degradation of o-xylene in simulated air was improved by loading low amounts of Pt,Pd,or Au onto Co_(3)O_(4).At room temperature,o-xylene conversion and CO_(x)selectivity using a0.1 wt%Pt/Co_(3)O_(4)catalyst reached 98.9%and 80%,and the energy efficiency was at the top level in comparison with values in the literature.A stable o-xylene degradation performance could be obtained by online regenerating the heat-insulated reactor with a high energy density.After characterization,it was found that the loading of nanosized Pt not only increased the Co^(3+)/Co^(2+)ratio,where the Co^(3+)benefitted the formation of reactive oxygen species,but also conduced Pt^(0)to oxygen activation,resulting in effective promotion of complete o-xylene oxidation.Operando plasma diffuse reflectance infrared Fourier transform spectroscopy demonstrated the complete o-xylene oxidation and proved that Pt played a key role in the complete oxidation of o-xylene.
文摘Nanosized NaY crystals have been prepared from metakaolin and sodium silicate by confined space synthesis with starch additive. It is found that the product has a narrow crystal size distribution (50-100 nm), high Si/Al ratio (Si/Al=4.6-6.1), high surface area (1090 m2/g) and the average diameter of nanosized NaY (75 nm) synthesized is 30 nm, it is smaller than that of without starch additive.