Effect of electromagnetic stirring in mold on the macroscopic quality of high carbon steel billet

An industrial plant trial for optimizing the process parameters in a round billet continuous casting mold with electromagnetic stirring （M-EMS） was performed, in which the influences of stirring parameters with M-EMS on the solidification macrostructure of high carbon steel were investigated. The results show that the billet quality is not well controlled under the condition of working current and frequency with EMS, in which the subsurface crack of grade 1.0-2.0 ups to 38.09%, the central pipe of grade 1.0-1.5 reaches to 14.28%, and the central porosity of grade 1.5 is 14.29%. The parameters of current 260 A and frequency 8 Hz as the final optimum scheme has a remarkable effect for improving the macroscopic quality of billet, in which the subsurface crack, central pipe and skin blowhole are all disappeared, and the central porosity and carbon segregation are also well improved.

Apparent Morphologies and Nature of Packet Martensite in High Carbon Steels

The apparent morphologies of packet martensite in eight high carbon steels were researched by using optical microscope, scanning electron microscope, and transmission electron microscope. It was found that the apparent morphologies, substructures, and habit plane of packet martensite in high carbon steels are entirely different from that in low carbon steels; the substructures of packet martensite in high carbon steels possess fully twinned structure, while the substructures of individual coarse martensite plates in these steels bear both fully and partially twinned structures. The formation reason for apparent morphologies, substructures and two habit planes （i. e, { 111 }, and { 225}r） of high carbon martensite were discussed in detail.

Effect of Cr/Mn segregation on pearlite–martensite banded structure of high carbon bearing steel

The effect of Cr/Mn segregation on the abnormal banded structure of high carbon bearing steel was studied by reheating and hot rolling.With the use of an optical microscope, scanning electron microscope, transmission electron microscope, and electron probe microanalyzer, the segregation characteristics of alloying elements in cast billet and their relationship with hot-rolled plate banded structure were revealed.The formation causes of an abnormal banded structure and the elimination methods were analyzed.Results indicate the serious positive segregation of C, Cr, and Mn alloy elements in the billet.Even distribution of Cr/Mn elements could not be achieved after 10 h of heat preservation at 1200℃, and the spacing of the element aggregation area increased, but the segregation index of alloy elements decreased.Obvious alloying element segregation characteristics are present in the banded structure of the hot-rolled plate.This distinct white band is composed of martensitic phases.The formation of this abnormal pearlite–martensite banded structure is due to the interaction between the undercooled austenite transformation behavior of hot-rolled metal and the segregation of its alloying elements.Under the air cooling after rolling, controlling the segregation index of alloy elements can reduce or eliminate the abnormal banded structure.

WELDING BETWEEN HIGH MANGANESE STEEL AND HIGH CARBON STEEL

Manuscript received 30 July 1999 Abstract The shielded metal arc welding (SMAW) of a manganese steel part as a crossing of railway track to a carbon steel part as the rails of the railroad is the welding of dissimilar steel. It are was known that it is not possible to the the rail of railroad directly to the cross- ing of railway track made from a steel containing about 14% of manganese (wt. ) because of so many differences between the two kinds of steels such as composition, microstructure,mechanical properties and weldability.A method was used to solve the problem by presetting an intermediate layer on each side of the joint and other special procedures were used.The result of test indicated that a good weld joint was obtained.

Study on the Interaction between Rare Earth and Carbon in High Carbon Steel

A certain quantity of RE is dissolved in high-carbon steel. The dissolved RE not only segregates on grain boundary, but also exists in grains. It exists in cementite much more than in ferrite. RE makes the carbides spheroidal and fine, and the carbides distribute uniformly. RE also changes the morphology of pearlite. By means of the analysis of Auger energy spectrum, we find that RE, which is dissolved in cementite, changes the composition and structure of cementite. In the case of higher content of RE and carbon, RE carbide can be formed.

Effect of quenching-partitioning treatment on the microstructure, mechanical and abrasive properties of high carbon steel

The present work employed the X-ray diffraction, scanning electron microscopy, electron backscattered diffraction, and electron probe microanalysis techniques to identify the microstructural evolution and mechanical and abrasive behavior of high carbon steel during quenching-partitioning treatment with an aim to enhance the toughness and wear resistance of high carbon steel.Results showed that, with the increase in partitioning temperature from 250 to 400℃, the amount of retained austenite(RA) decreased resulting from the carbide precipitation effect after longer partitioning times.Moreover, the stability of RA generally increased because of the enhanced degree of carbon enrichment in RA.Given the factors affecting the toughness of high carbon steel, the stability of RA associated with size, carbon content, and morphology plays a significant role in determining the toughness of high carbon steel.The analysis of the wear resistance of samples with different mechanical properties shows that hardness is the primary factor affecting the wear resistance of high carbon steel, and the toughness is the secondary one.

Creep testing and viscous behavior research on carbon constructional quality steel under high temperature

Creep tests under at a certain temperature and different stress levels were performed on two carbon constructional quality steels at a certain stress level and different temperatures,and their creep curves at high temperature were obtained based on analyzing the testing data.Taking 45 steel at a certain temperature and stress as the example,the integral creep constitutive equation and the differential stress-strain constitutive relationship were established based on the relevant rheological model,and the integral core function was also obtained.Simultaneously,the viscous coefficients denoting the viscous behavior in visco-plastic constitutive equation were determined by taking use of the creep testing data.Then the viscous coefficients of three carbon steels(20 steel,35 steel and 45 steel) were compared and analyzed.The results show that the viscosity is different due to different materials at the same temperature and stress.

EFFECT OF CARBON CONTENT ON MICROSTRUCTURE AND PROPERTIES OF HIGH STRENGTH AND HIGH ELONGATION STEELS

The micro structure and mechanical properties of new kind of hot-rolled high strength and high elongation steels with retained austenite were studied by discussing the influence of different carbon content. The research results indicate that carbon content has a significant effect on retaining austenite and consequently resulting in high elongation. Besides, new findings about relationship between carbon content and retained austenite as well as properties were discussed in the paper.

Microstructural morphology of the semi-solid high carbon steel T12 before and after rheo-rolling

The semi-solid high carbon steel T12 was rolled in a closed box groove under a certain condition by the rheo-rolling equipment, and the microstructural morphology of the semi-solid T12 before and after deformation was investigated by optical mi- croscope to analyze and summarize the microstructure evolution law of T12 deformed in semi-solid state. The experiment results show that the grain shape before deformation of the semi-solid T12 steel displays globule or ellipse by the electromagnetic stirring, the distribution of solid and liquid phases is homogeneous. But the microstructure of semi-solid product after rheo-rolling exhibits macrosegregation that the distribution of liquid and solid phases changes, the liquid phases divorce from the solid phases. In the transverse section, most of the solid phases get together in the center of the specimen, the liquid phases flow to the surface or the edge of the specimen, and the grains occur plastic deformation while reduction increased. In longitudinal section, the middle micro- structure of the specimen is more homogeneous than that at the head or tail, the head microstructure is similar to the tail and the size of the grains is not homogeneous.

Effect of casting technology on microstructure and phases of high carbon high speed steel

The as-cast microstructures of high carbon high speed steels （HC-HSS） made by sand casting, centrifugal casting and electromagnetic centrifugal casting, respectively, were studied by using of optical microscopy （OM） and D/max2200pc X-ray diffraction. The results show that the microstructure of as-cast HC- HSS is dominated by alloy carbides （W2C, VC, Cr7C3）, martensite and austenite. The centrifugal casting and electromagnetic centrifugal casting apparently improve the solidification structure of HCoHSS. With the increase of magnetic intensity （B）, the volume fraction of austenite in the HC-HSS solidification structure increases significantly while the eutectic ledeburite decreases. Moreover, the secondary carbides precipitated from the austenite are finer with more homogeneous distribution in the electromagnetic centrifugal castings. It has also been found that the lath of eutectic carbide in ledeburite becomes finer and carbide phase spacing in eutectic ledeburite increases along with the higher magnetic field strength.

New Spheroidizing Technique of Ultra-High Carbon Steel With Aluminum Addition

A new spheroidizing process of ultra-high carbon steel （UHCS） containing C 1.55%, Cr 1.45%, and Al 1.5% in mass percent has been proposed. The effect of processing parameters on the microstructure was analyzed. The UHCS produced by this new process has a microstructure with recrystallized ferrite matrix and fine and uniform carbide particles. After this spheroidizing, the UHCS exhibits good mechanical properties at ambient temperature, for example σb= 1 100 MPa, σs =915 MPa, δ=8% and high ratio of σs/σb.

Effect of High Pressure Heat Treatment on Microstructure and Compressive Properties of Low Carbon Steel

The effect of high pressure heat treatment on microstructure and compressive properties of low carbon steel were investigated by optical microscope,transmission electron microscope,hardness tester and compression test methods.The results show that martensite appears in low carbon steel at 1-5GPa GPa and 950°C for 15 minutes treatment,high pressure heat treatment can improve the hardness and compressive properties of the steel,the yield strength of the steel increases with increasing pressure,and its compressive properties are better than that treated under normal pressure quenching.

High Carbon Alloy Steels with Multiple Types of Ultra-fine Carbides and Their Characteristics

Under normal forging and annealing conditions, there are different ultra fine carbides (M3C, M23C6, M7Cj, M6C and MC) in high carbon alloy steels when alloy composition design is carried out properly. On the basis of carbides transformation orderliness, the alloy composition design of the high carbon alloy steels is conducted by phase-equilibrium thermodynamic calculation for Fe-Cr-W-Mo-V-C system. The nucleation and growth of new carbides, dissolution of previous partial carbides in these steels during annealing process, all these lead to ultra-fine distribution of carbides. Due to different crystal structures of carbides and different thermodynamics as well dynamics parameters of the carbides dissolution and precipitation, the range of quenching temperature of these steels is widened, and the good temper-resistance is obtained. The characteristics of heat treatment process and microstructure variance, and the carbides transformation for different temperature are explained by the phase-equilibrium component satisfactorily. Their bend and yield strength, flexibility and toughness all are advanced markedly comparing with that of kindred steels. Results of the applications have proved that the microstructure of ultra-fine carbides in these steels played importance roles in the enhancement of edginess and fatigue crack resistance of the die and knives.

Spheroidization and Ostwald Growth of Carbide in Isothermal Process of Hot-Deformed High Carbon Chromium Cast Steel

In isothermal spheroidizing process,the spheroidization and growth of the carbide formed in hot-deformed high-carbon chromium cast steel at high temperature were investigated.The results showed that the spheroidizing growth of carbide proceeds in such a way that the bigger carbide particles swallow the smaller ones,and the short rhabdoid carbides dissolve and are spheroidized by itself.When the samples were held at 720℃ for more than 3 h,the spheroidization is not obvious.The feature of the process is the size increment and the amount decrement of carbide particles.The empirical equation for growth rate of carbides was obtained.The volume fraction of carbides keeps constant.The growth process agrees well with Ostwald Ripening Law.

Evolution of carbides and carbon content in matrix of an ultra-high carbon sintered steel during heat treatment process

DTA, thermal expansion, XRD, and SEM were used to evaluate the effect of quenching temperature on the mechanical properties and microstructure of a novel sintered steel Fe-6Co-1Ni-5Cr-5Mo-1C. Lattice parameters and the mass fraction of carbon dissolved in the matrix of the steel quenched were investigated. It is discovered that the hardness of the steel increases with quenching temperature in the range of 840-900℃ and remains constant in the range of 900 to 1100℃. It decreases rapidly when the temperature is higher than 1100℃. The mass fraction of carbon dissolved in the matrix of the steel quenched at 840℃ is 0.38, but when the quenching temperature is increased to 1150℃, it increases to 0.98. The carbides formed during sintering are still present at grain boundaries and in the matrix of the steel quenched at low quenching temperatures, such as 840℃. When the quenching temperature is increased to 1150℃, most of the carbides at grain boundaries are dissolved with just a small amount of spherical M23C6 existing in the matrix of the quenched steel.

Effect of Fast Cooling Rate on the Microstructure and Mechanical Properties of Low-Carbon High-Strength Steel Annealed in the Intercritical Region

The effect of fast cooling rate on the microstructure and mechanical properties of low-carbon high-strength steel annealed in the intercritical region was investigated using a Gleeble 1500 thermomechanical simulator and a continuous annealing thermomeehanical simulator. The results showed that the microstructure consisted of ferrite and bainite as the main phases with a small amount of retained austenite and martensite islands at cooling rate of 5 and 50 ℃/s, respectively. Fast cooling after continuous annealing affected all constituents of the microstructure. The mechanical properties were improved considerably. Ultimate tensile strength （U-TS） increased and total elongation （TEL） decreased with increasing cooling rate in all specimens. The specimen 1 at a cooling rate of 5 ℃/s exhibited the maximum TEL and UTSxTEL （20% and 27 200 MPa%, respectively） because of the competition between weakening by presence of the retained austenite plus the carbon indigence by carbide precipitation, and strengthening by martensitic islands and precipitation. The maximum UTS and YS （1 450 and 951 MPa, respectively） were obtained for specimen 2 at a cooling rate of 50 ℃/s. This is attributed to the effect of dispersion strengthening of finer martensite islands and the effect of precipitation strengthening of carbide precipitates.

Spheroidization process in large-deformed high-carbon steel

In this study,the spheroidization process of large-deformed steel under various conditions was researched.Steel with a high carbon content （1.0％ C） was first treated thermomechanically using multipass rolling.Then it underwent spheroidization treatments at different heating temperatures,using various heating times and cooling rates.Spheroidization processes with a lower heating temperature,shorter heating time,or faster cooling rate than those of the traditional process all showed good results,indicating that the spheroidization process was promoted significantly by the large deformation process.Grain refinement and fragmentation of cementite,along with the large deformation process,promoted this spheroidization process.

Microstructure and Property of High Carbonic-Chromium Cast Steel with Different Hot Deformation Ratio

The microstructure and properties of high carbonic-chromium cast steel subjected to different hot deformation ratios were studied.The experimental results show that the microstructure and properties of high carbonic-chromium cast steel are obviously improved after hot deformation,and the best mechanical properties of the cast steel can be obtained under hot deformation ratio of 40 %-50 %,which leads to the morphology change of eutectic carbide and the precipitation of granular carbides.

Effect of Boron on Delayed Fracture Resistance of Medium-Carbon High Strength Spring Steel

The delayed fracture behavior of medium carbon high strength spring steel containing different amounts of boron （0. 000 5%, 0. 001 6 %） was studied using sustained load delayed fracture test. The results show that delayed fracture resistance of boron containing steels is higher than that of conventional steel 60Si2MnA at the same strength level and it increases with the increase of boron eontent from 0. 000 5% to 0. 001 6%. The delayed fracture mode is mainly intergranular in the boron containing steels tempered at 350℃, which indicates that the addition of boron does not change the fracture character. However, the increase of boron content enlarges the size of the crack initia tion area. Further study of phase analysis indicates that most boron is in solid solution, and only a very small quantity of boron is in the M3 （C, B） phase.