NbCrAl coatings in the presence or absence of Al outer layer were prepared on C103 Nb based alloy and alumina substrate by direct current magnetron sputtering technique. The oxidation performance of coating systems wa...NbCrAl coatings in the presence or absence of Al outer layer were prepared on C103 Nb based alloy and alumina substrate by direct current magnetron sputtering technique. The oxidation performance of coating systems was evaluated by isothermal oxidation tests. The element diffusion and oxidation behavior of the coating systems were investigated. The results indicate that the mass gains of NbCrAl and Al/NbCrAl coatings are 2.02 mg/cm^2 and 0.79 mg/cm^2 at 1 000 ℃ for short time. Al/NbCrAl coatings exhibit more effective protection than NbCrAl coatings. The addition of Al layer can improve the oxidation resistance of NbCrAl coatings, which is attributed to the Al layer offering enough Al content to react with oxygen to form a continuous and dense Al_2O_3 scale on NbCrAl coating and it can inhibit the further internal oxidation.展开更多
基金Funded by the National Natural Science Foundation of China(51371059)the Guangxi Natural Science Foundation(2016GXNSFDA380022,AA17204100,AA18118030)+1 种基金the Project of Development of Science and Technology of Nanning(20181191-2)the High-Level Innovative Team and Outstanding School Program in Guangxi Colleges(the Second Batch)
文摘NbCrAl coatings in the presence or absence of Al outer layer were prepared on C103 Nb based alloy and alumina substrate by direct current magnetron sputtering technique. The oxidation performance of coating systems was evaluated by isothermal oxidation tests. The element diffusion and oxidation behavior of the coating systems were investigated. The results indicate that the mass gains of NbCrAl and Al/NbCrAl coatings are 2.02 mg/cm^2 and 0.79 mg/cm^2 at 1 000 ℃ for short time. Al/NbCrAl coatings exhibit more effective protection than NbCrAl coatings. The addition of Al layer can improve the oxidation resistance of NbCrAl coatings, which is attributed to the Al layer offering enough Al content to react with oxygen to form a continuous and dense Al_2O_3 scale on NbCrAl coating and it can inhibit the further internal oxidation.