Nd^3＋： Gd3Ga5O12（Nd ： GGG） nanopowder for transparent laser ceramics was synthesized using sol-gel method. XRD, SEM, and fluorescence spectrum were used to study the properties of Nd^3＋ ：Gd3Ga5O12 nanopowder. X...Nd^3＋： Gd3Ga5O12（Nd ： GGG） nanopowder for transparent laser ceramics was synthesized using sol-gel method. XRD, SEM, and fluorescence spectrum were used to study the properties of Nd^3＋ ：Gd3Ga5O12 nanopowder. XRD patterns of samples show that it has a cubic structure. Meanwhile, pure Nd：GGG crystals were obtained at 1000 ℃ for 12 h. SEM photographs show that dispersed, uniform, ball-like Nd：GGG nanopowder is obtained. Both XRD and SEM results show that the crystallization degree and the grain size increase with the increase in calcining temperature. Analysis of fluorescence spectrum shows that fluorescence emission occurs at 1062.7 nm, which is the result of Nd^3＋ （^4F3/2→^4I11/2） transition. Homogenous Nd ： GGG nanopewder with a small grain size synthesized using the sol-gel method is favorable for sintering the transparent ceramic, which proves that the nanopewder obtained is suitable as a precursor for preparing GGG transparent ceramics.展开更多
Preparation of Nd3+:Gd3Ga5O12 polycrystalline material by sol-gel method was preparated in this paper.The structure and the pattern of the sample were analyzed by thermogravimetric analysis and differential thermal an...Preparation of Nd3+:Gd3Ga5O12 polycrystalline material by sol-gel method was preparated in this paper.The structure and the pattern of the sample were analyzed by thermogravimetric analysis and differential thermal analysis（TG-DTA）,Infrared spectrum,XRD,TEM and electron spectrum,which indicated that the powder with good characteristics of 70-100 nm can be obtained by sintering at 1 000℃.It was shown that the chemical composition of the sample was agreed with experimental requirements by electron spectrum analysis.展开更多
基金Project supported bythe Nature Science Foundation of Jilin Province (20000516)
文摘Nd^3＋： Gd3Ga5O12（Nd ： GGG） nanopowder for transparent laser ceramics was synthesized using sol-gel method. XRD, SEM, and fluorescence spectrum were used to study the properties of Nd^3＋ ：Gd3Ga5O12 nanopowder. XRD patterns of samples show that it has a cubic structure. Meanwhile, pure Nd：GGG crystals were obtained at 1000 ℃ for 12 h. SEM photographs show that dispersed, uniform, ball-like Nd：GGG nanopowder is obtained. Both XRD and SEM results show that the crystallization degree and the grain size increase with the increase in calcining temperature. Analysis of fluorescence spectrum shows that fluorescence emission occurs at 1062.7 nm, which is the result of Nd^3＋ （^4F3/2→^4I11/2） transition. Homogenous Nd ： GGG nanopewder with a small grain size synthesized using the sol-gel method is favorable for sintering the transparent ceramic, which proves that the nanopewder obtained is suitable as a precursor for preparing GGG transparent ceramics.
文摘Preparation of Nd3+:Gd3Ga5O12 polycrystalline material by sol-gel method was preparated in this paper.The structure and the pattern of the sample were analyzed by thermogravimetric analysis and differential thermal analysis（TG-DTA）,Infrared spectrum,XRD,TEM and electron spectrum,which indicated that the powder with good characteristics of 70-100 nm can be obtained by sintering at 1 000℃.It was shown that the chemical composition of the sample was agreed with experimental requirements by electron spectrum analysis.