Biodegradable magnesium-based alloys are very promising materials for temporary implants. Laser welding is an important joining method in such application. In this study, the as-rolled AZ31B magnesium alloy sheets of ...Biodegradable magnesium-based alloys are very promising materials for temporary implants. Laser welding is an important joining method in such application. In this study, the as-rolled AZ31B magnesium alloy sheets of 1 mm in thickness were successfully joined by Nd : YAG laser welding. The microstructure and properties of the welded joint were investigated. The result shows that the welded joint is characterized by a narrow heat-affected zone, finer grains and a large number of precipitates distribute in the matrix in the weld. Microhardness of the weld is significantly improved to 72 HV 0. 05 as compared to 55 HV 0. 05 of the base metal. Tensile strength of butt-welded joint is 180. 24 MPa, which is 76. 8% that of the base metal. The electrochemical corrosion experiment shows that the corrosion resistance of laser welded joint is significantly improved in a 3.5 wt. % NaCl solution.展开更多
A novel flat-flat resonator consisting of two crystals(Nd:YAG + Nd:YVO4) is established for power scaling in a diode-end-pumped solid-state laser. We systematically compare laser characteristics between multi-seg...A novel flat-flat resonator consisting of two crystals(Nd:YAG + Nd:YVO4) is established for power scaling in a diode-end-pumped solid-state laser. We systematically compare laser characteristics between multi-segmented(Nd:YAG + Nd:YVO4) and conventional composite(Nd:YAG + Nd:YAG) crystals to demonstrate the feasibility of spectral line matching for output power scale-up in end-pumped lasers. A maximum continuous-wave output power of 79.2 W is reported at 1064 nm, with Mx2= 4.82, My2= 5.48, and a pumping power of 136 W in the multi-segmented crystals(Nd:YAG + Nd:YVO4). Compared to conventional composite crystals(Nd:YAG + Nd:YAG), the optical-optical conversion efficiency of multi-segmented crystals(Nd:YAG + Nd:YVO4) from 808 nm to 1064 nm is enhanced from 30% to 58.8%,while the laser output sensitivity as affected by the diode-laser temperature is reduced from 55% to 9%.展开更多
基金The work was supported by the National Natural Science Foundation of China ( Grant No. 51305292 ) and the Aviation Science Foundation ( Grant No. 20105429001 ).
文摘Biodegradable magnesium-based alloys are very promising materials for temporary implants. Laser welding is an important joining method in such application. In this study, the as-rolled AZ31B magnesium alloy sheets of 1 mm in thickness were successfully joined by Nd : YAG laser welding. The microstructure and properties of the welded joint were investigated. The result shows that the welded joint is characterized by a narrow heat-affected zone, finer grains and a large number of precipitates distribute in the matrix in the weld. Microhardness of the weld is significantly improved to 72 HV 0. 05 as compared to 55 HV 0. 05 of the base metal. Tensile strength of butt-welded joint is 180. 24 MPa, which is 76. 8% that of the base metal. The electrochemical corrosion experiment shows that the corrosion resistance of laser welded joint is significantly improved in a 3.5 wt. % NaCl solution.
基金Project supported by the National Defense Pre-Research Foundation of China(Grant No.9140A020105)
文摘A novel flat-flat resonator consisting of two crystals(Nd:YAG + Nd:YVO4) is established for power scaling in a diode-end-pumped solid-state laser. We systematically compare laser characteristics between multi-segmented(Nd:YAG + Nd:YVO4) and conventional composite(Nd:YAG + Nd:YAG) crystals to demonstrate the feasibility of spectral line matching for output power scale-up in end-pumped lasers. A maximum continuous-wave output power of 79.2 W is reported at 1064 nm, with Mx2= 4.82, My2= 5.48, and a pumping power of 136 W in the multi-segmented crystals(Nd:YAG + Nd:YVO4). Compared to conventional composite crystals(Nd:YAG + Nd:YAG), the optical-optical conversion efficiency of multi-segmented crystals(Nd:YAG + Nd:YVO4) from 808 nm to 1064 nm is enhanced from 30% to 58.8%,while the laser output sensitivity as affected by the diode-laser temperature is reduced from 55% to 9%.