A reasonable pre-treatment and an ultrasonic pre-plating Cu film were applied for sintering NdFeB permanent magnet. The samples were then plated in neutral bath (PH=7) for 40min and in acidic bath (PH=4.8～5.1) for 2h...A reasonable pre-treatment and an ultrasonic pre-plating Cu film were applied for sintering NdFeB permanent magnet. The samples were then plated in neutral bath (PH=7) for 40min and in acidic bath (PH=4.8～5.1) for 2h. A composite electroless plating with different phosphor content was obtained. The results show that the composite plating coatings are dense and have a strong bond with the substrate, which contribute to the excellent corrosion resistance of the plating coating.展开更多
The Ni-P/TiO2 composite film on sintered NdFeB permanent magnet was investigated by X-ray diffraction （XRD）,environmental scanning electron microscopy （ESEM）,and energy dispersive X-ray spectrometer （EDX）. The c...The Ni-P/TiO2 composite film on sintered NdFeB permanent magnet was investigated by X-ray diffraction （XRD）,environmental scanning electron microscopy （ESEM）,and energy dispersive X-ray spectrometer （EDX）. The corrosion resistance of Ni-P/TiO2 film coated on NdFeB magnet,in 0.5 mol/L NaCl solution,was studied by potentiodynamic polarization,salt spray test and electrochemical impedance spectroscopy （EIS） techniques. The self-corrosion current density （icorr） and the polarization resistance （Rp） of Ni-P/TiO2 film are 0.22 μA/cm2 （about 14% of that of Ni-P coating）,and 120 kΩ·cm2 （about 2 times of that of Ni-P coating）,respectively. The anti-salt spray time of Ni-P/TiO2 film is about 2.5 times of that of the Ni-P coating. The results indicate that Ni-P/TiO2 film has a better corrosion resistance than Ni-P coating,and the composite film increases the corrosion resistance of NdFeB magnet markedly.展开更多
研究了粘结NdFeB永磁体化学镀Ni Cu P合金防护层的工艺过程。研究表明:粘结磁体经碱性去油、缓蚀酸洗、镀前隔离与活化处理后再进行化学镀Ni Cu P,可获得镀层光亮平整,结合力好,孔隙率为每平方厘米0.5个,腐蚀速率为0.07mg·cm-2...研究了粘结NdFeB永磁体化学镀Ni Cu P合金防护层的工艺过程。研究表明:粘结磁体经碱性去油、缓蚀酸洗、镀前隔离与活化处理后再进行化学镀Ni Cu P,可获得镀层光亮平整,结合力好,孔隙率为每平方厘米0.5个,腐蚀速率为0.07mg·cm-2·h-1的耐蚀性镀层,该镀层对磁体磁性能无不良影响。展开更多
文摘A reasonable pre-treatment and an ultrasonic pre-plating Cu film were applied for sintering NdFeB permanent magnet. The samples were then plated in neutral bath (PH=7) for 40min and in acidic bath (PH=4.8～5.1) for 2h. A composite electroless plating with different phosphor content was obtained. The results show that the composite plating coatings are dense and have a strong bond with the substrate, which contribute to the excellent corrosion resistance of the plating coating.
基金Sponsored by Hi-Tech Research and Development Program of China (2003AA305120)
文摘The Ni-P/TiO2 composite film on sintered NdFeB permanent magnet was investigated by X-ray diffraction （XRD）,environmental scanning electron microscopy （ESEM）,and energy dispersive X-ray spectrometer （EDX）. The corrosion resistance of Ni-P/TiO2 film coated on NdFeB magnet,in 0.5 mol/L NaCl solution,was studied by potentiodynamic polarization,salt spray test and electrochemical impedance spectroscopy （EIS） techniques. The self-corrosion current density （icorr） and the polarization resistance （Rp） of Ni-P/TiO2 film are 0.22 μA/cm2 （about 14% of that of Ni-P coating）,and 120 kΩ·cm2 （about 2 times of that of Ni-P coating）,respectively. The anti-salt spray time of Ni-P/TiO2 film is about 2.5 times of that of the Ni-P coating. The results indicate that Ni-P/TiO2 film has a better corrosion resistance than Ni-P coating,and the composite film increases the corrosion resistance of NdFeB magnet markedly.
文摘研究了粘结NdFeB永磁体化学镀Ni Cu P合金防护层的工艺过程。研究表明:粘结磁体经碱性去油、缓蚀酸洗、镀前隔离与活化处理后再进行化学镀Ni Cu P,可获得镀层光亮平整,结合力好,孔隙率为每平方厘米0.5个,腐蚀速率为0.07mg·cm-2·h-1的耐蚀性镀层,该镀层对磁体磁性能无不良影响。