A reasonable pre-treatment and an ultrasonic pre-plating Cu film were applied for sintering NdFeB permanent magnet. The samples were then plated in neutral bath (PH=7) for 40min and in acidic bath (PH=4.8～5.1) for 2h...A reasonable pre-treatment and an ultrasonic pre-plating Cu film were applied for sintering NdFeB permanent magnet. The samples were then plated in neutral bath (PH=7) for 40min and in acidic bath (PH=4.8～5.1) for 2h. A composite electroless plating with different phosphor content was obtained. The results show that the composite plating coatings are dense and have a strong bond with the substrate, which contribute to the excellent corrosion resistance of the plating coating.展开更多
Anisotropic NdFeB/SmCoCuFeZr composite bonded magnets were prepared by warm compaction process. The effects of adding SmCoCuFeZr magnetic powder on the properties of anisotropic bonded NdFeB magnet were investigated i...Anisotropic NdFeB/SmCoCuFeZr composite bonded magnets were prepared by warm compaction process. The effects of adding SmCoCuFeZr magnetic powder on the properties of anisotropic bonded NdFeB magnet were investigated in this work. The results show that, both magnetic properties and temperature stability of the bonded magnet can be improved by adding fine SmCoCuFeZr magnetic powder. In the present study, the optimal content of SmCoCuFeZr magnetic powder was about 20 wt.%, in this case, the Br, Hcj, and（BH）maxof the NdFeB/SmCoCuFeZr composite magnet achieved 0.943 T, 1250 kA/m, and168 kJ/m^3, respectively.展开更多
文摘A reasonable pre-treatment and an ultrasonic pre-plating Cu film were applied for sintering NdFeB permanent magnet. The samples were then plated in neutral bath (PH=7) for 40min and in acidic bath (PH=4.8～5.1) for 2h. A composite electroless plating with different phosphor content was obtained. The results show that the composite plating coatings are dense and have a strong bond with the substrate, which contribute to the excellent corrosion resistance of the plating coating.
基金Project supported by the Natural Science Foundation of Jiangsu Province,China(BK20171408)the Graduate Student Innovation Foundation of Jiangsu Province(201711276005Z)Scientific Foundation of Nanjing Institute of Technology(CKJB201402,and YKJ201506)
文摘Anisotropic NdFeB/SmCoCuFeZr composite bonded magnets were prepared by warm compaction process. The effects of adding SmCoCuFeZr magnetic powder on the properties of anisotropic bonded NdFeB magnet were investigated in this work. The results show that, both magnetic properties and temperature stability of the bonded magnet can be improved by adding fine SmCoCuFeZr magnetic powder. In the present study, the optimal content of SmCoCuFeZr magnetic powder was about 20 wt.%, in this case, the Br, Hcj, and（BH）maxof the NdFeB/SmCoCuFeZr composite magnet achieved 0.943 T, 1250 kA/m, and168 kJ/m^3, respectively.