It is known that in B (un)doped Ni 3Al polycrystals, the dependence of yield strength on grain size follows the Hall Petch relationship: σ y= σ 0+ K y d -1/2 , and the slope K y can be reduced by B doping owing to t...It is known that in B (un)doped Ni 3Al polycrystals, the dependence of yield strength on grain size follows the Hall Petch relationship: σ y= σ 0+ K y d -1/2 , and the slope K y can be reduced by B doping owing to the lowering of grain boundary resistance to slip transmission. If the intergranular cracking in polycrystalline Ni 3Al occurs from the microcavity along the grain boundaries, the effective external tensile stress for the propagation of the crack like microcavity along the grain boundaries can be deduced as: σ f= σ i+ K u d -1/2 , where K u reflects the effects of such factors as environment, strain rate, boron doping and the orientation of the grain boundary on the trend of intergranular cracking. For loaded polycrystalline Ni 3Al, it should be competitive between the intergranular cracking and slip transmission across the grain boundary. Therefore, comparing the varieties of both σ y and σ f with grain size, the dependence of ductile brittle transition on grain size, and the effects of the above factors on ductile brittle transition can be expected. The model also predicts that there exists a critical grain size for the ductile brittle transition of polycrystalline Ni 3Al alloys, and B doping can increase the critical grain size due to the reduction of the slope K y and the increase of K u. The reported experimental results verified the above model.展开更多
The electrochemical corrosion behavior of the two Cu-40Ni-20Cr alloys prepared by conventional casting(CA) and mechanical alloying(MA) with the different grain sizes was studied by using open-circuit potential(OCP), p...The electrochemical corrosion behavior of the two Cu-40Ni-20Cr alloys prepared by conventional casting(CA) and mechanical alloying(MA) with the different grain sizes was studied by using open-circuit potential(OCP), potentiodynamic polarization and electrochemical impedance spectroscopy(EIS) methods in solutions containing chloride ions. The results show that the free corrosion potentials of the two alloys move towards negative values, corrosion currents increase and therefore corrosion rates become faster with the increase of chloride ion concentrations. EIS plots of CACu-40Ni-20Cr alloy are composed of single capacitive loop, while EIS plots of MACu-40Ni-20Cr alloy are composed of double capacitive loops in solution containing lower chloride ion concentrations. EIS plots of the two alloys have Warburg impedance with the increase of chloride ion concentrations. Corrosion rates of MACu-40Ni-20Cr alloy become faster than those of CACu-40Ni-20Cr alloy obviously in solutions containing the same chloride ion concentrations because MACu-40Ni-20Cr alloy is able to produce large concentrations of grain boundaries in the course of reduction in grain size by mechanical alloying.展开更多
Nanocrystalline (NC) and coarse-grained Ni with different grain sizes (from 16 nm to 2 μm) were fabricated by direct current electrodeposition. Effect of grain size on the electrochemical corrosion behavior of these ...Nanocrystalline (NC) and coarse-grained Ni with different grain sizes (from 16 nm to 2 μm) were fabricated by direct current electrodeposition. Effect of grain size on the electrochemical corrosion behavior of these Ni deposits in different corrosion media was characterized by using potentiodynamic polarization test, electrochemical impedance spectroscopy (EIS), X-ray photoelectron spectroscopy (XPS) and immersion corrosion test. Results show that in the NaOH or NaCl solution, the NC Ni exhibits improved corrosion resistance with the decrease of grain size. But in H2SO4 solution, the higher grain boundary density accelerates corrosion due to no passive process and the corrosion resistance of NC Ni decreases with refining grain size. The distinct experimental results of NC Ni in corrosion behavior can be reasonably explained by the positive or negative effect of high-density grain boundaries in different corrosion media.展开更多
Fluxing of 5 g bulk melt Ni77Si13B10 permits high undercoolings to be attained prior to nu-cleation onset.Investigations of grain refinement in the bulk undercooled alloy as a function ofundercooling,recalescence beha...Fluxing of 5 g bulk melt Ni77Si13B10 permits high undercoolings to be attained prior to nu-cleation onset.Investigations of grain refinement in the bulk undercooled alloy as a function ofundercooling,recalescence behavior and cooling rate have been reported.A significant inhomo-geneity of reduction in grain size of a bulk sample is observed,which is caused by the different so-lidification conditions:(1)recalescence process,and(2)the followed plateau in which the heatrelease and extraction rates are equal.It is concluded that the homogeneous refined microstructurecan be achieved if the initial undercooling prior to nucleation,or cooling rate after recalescence isfurther increased.展开更多
The fatigue-creep interaction behaviour of superalloy GH698 with different grain sizes has been studied at 700℃.The results show that three zones,F,C and FC,can be distinguished at the fatigue-creep interaction curve...The fatigue-creep interaction behaviour of superalloy GH698 with different grain sizes has been studied at 700℃.The results show that three zones,F,C and FC,can be distinguished at the fatigue-creep interaction curves.In zones FC and C,the presence of alternative stresses inhibits the creep deformation process therefore delays the fracture of the alloy.This effect will be enhanced by grain refining.However,in zone F,grain refining exhibits an inverse ef fect under large alternative stresses.展开更多
The diffusivity of hydrogen in two Ni3Al alloys (No.1 and No.2) has been measured in the temperature range of 100 degreesC to 420 degreesC using an ultrahigh vacuum gaseous permeation technique. The diffusivity data f...The diffusivity of hydrogen in two Ni3Al alloys (No.1 and No.2) has been measured in the temperature range of 100 degreesC to 420 degreesC using an ultrahigh vacuum gaseous permeation technique. The diffusivity data fall into two segments, in which the hydrogen diffusivity adheres to the Arrhenius form, respectively. From the hydrogen diffusivity, it is conjectured that the hydrogen diffusivity reflects the hydrogen transportation along the grain boundaries at lower temperature and the hydrogen transportation in the lattice at higher temperature. The intergranular fracture of Lit-type intermetallics induced by hydrogen at relative low temperature results from hydrogen transportation along the grain boundaries and not in the lattice.展开更多
文摘It is known that in B (un)doped Ni 3Al polycrystals, the dependence of yield strength on grain size follows the Hall Petch relationship: σ y= σ 0+ K y d -1/2 , and the slope K y can be reduced by B doping owing to the lowering of grain boundary resistance to slip transmission. If the intergranular cracking in polycrystalline Ni 3Al occurs from the microcavity along the grain boundaries, the effective external tensile stress for the propagation of the crack like microcavity along the grain boundaries can be deduced as: σ f= σ i+ K u d -1/2 , where K u reflects the effects of such factors as environment, strain rate, boron doping and the orientation of the grain boundary on the trend of intergranular cracking. For loaded polycrystalline Ni 3Al, it should be competitive between the intergranular cracking and slip transmission across the grain boundary. Therefore, comparing the varieties of both σ y and σ f with grain size, the dependence of ductile brittle transition on grain size, and the effects of the above factors on ductile brittle transition can be expected. The model also predicts that there exists a critical grain size for the ductile brittle transition of polycrystalline Ni 3Al alloys, and B doping can increase the critical grain size due to the reduction of the slope K y and the increase of K u. The reported experimental results verified the above model.
基金Project(50771068) supported by the National Natural Science Foundation of ChinaProject(20062049) supported by Natural Science Foundation of Liaoning Province, China
文摘The electrochemical corrosion behavior of the two Cu-40Ni-20Cr alloys prepared by conventional casting(CA) and mechanical alloying(MA) with the different grain sizes was studied by using open-circuit potential(OCP), potentiodynamic polarization and electrochemical impedance spectroscopy(EIS) methods in solutions containing chloride ions. The results show that the free corrosion potentials of the two alloys move towards negative values, corrosion currents increase and therefore corrosion rates become faster with the increase of chloride ion concentrations. EIS plots of CACu-40Ni-20Cr alloy are composed of single capacitive loop, while EIS plots of MACu-40Ni-20Cr alloy are composed of double capacitive loops in solution containing lower chloride ion concentrations. EIS plots of the two alloys have Warburg impedance with the increase of chloride ion concentrations. Corrosion rates of MACu-40Ni-20Cr alloy become faster than those of CACu-40Ni-20Cr alloy obviously in solutions containing the same chloride ion concentrations because MACu-40Ni-20Cr alloy is able to produce large concentrations of grain boundaries in the course of reduction in grain size by mechanical alloying.
基金Project(2004CB619301) supported by the National Basic Research Program of ChinaProject(50871046) supported by the National Natural Science Foundation of ChinaProject supported by 985-Automotive Engineering of Jilin University, China
文摘Nanocrystalline (NC) and coarse-grained Ni with different grain sizes (from 16 nm to 2 μm) were fabricated by direct current electrodeposition. Effect of grain size on the electrochemical corrosion behavior of these Ni deposits in different corrosion media was characterized by using potentiodynamic polarization test, electrochemical impedance spectroscopy (EIS), X-ray photoelectron spectroscopy (XPS) and immersion corrosion test. Results show that in the NaOH or NaCl solution, the NC Ni exhibits improved corrosion resistance with the decrease of grain size. But in H2SO4 solution, the higher grain boundary density accelerates corrosion due to no passive process and the corrosion resistance of NC Ni decreases with refining grain size. The distinct experimental results of NC Ni in corrosion behavior can be reasonably explained by the positive or negative effect of high-density grain boundaries in different corrosion media.
基金Financilly suported by the National Natural Science Foundation of China
文摘Fluxing of 5 g bulk melt Ni77Si13B10 permits high undercoolings to be attained prior to nu-cleation onset.Investigations of grain refinement in the bulk undercooled alloy as a function ofundercooling,recalescence behavior and cooling rate have been reported.A significant inhomo-geneity of reduction in grain size of a bulk sample is observed,which is caused by the different so-lidification conditions:(1)recalescence process,and(2)the followed plateau in which the heatrelease and extraction rates are equal.It is concluded that the homogeneous refined microstructurecan be achieved if the initial undercooling prior to nucleation,or cooling rate after recalescence isfurther increased.
文摘The fatigue-creep interaction behaviour of superalloy GH698 with different grain sizes has been studied at 700℃.The results show that three zones,F,C and FC,can be distinguished at the fatigue-creep interaction curves.In zones FC and C,the presence of alternative stresses inhibits the creep deformation process therefore delays the fracture of the alloy.This effect will be enhanced by grain refining.However,in zone F,grain refining exhibits an inverse ef fect under large alternative stresses.
文摘The diffusivity of hydrogen in two Ni3Al alloys (No.1 and No.2) has been measured in the temperature range of 100 degreesC to 420 degreesC using an ultrahigh vacuum gaseous permeation technique. The diffusivity data fall into two segments, in which the hydrogen diffusivity adheres to the Arrhenius form, respectively. From the hydrogen diffusivity, it is conjectured that the hydrogen diffusivity reflects the hydrogen transportation along the grain boundaries at lower temperature and the hydrogen transportation in the lattice at higher temperature. The intergranular fracture of Lit-type intermetallics induced by hydrogen at relative low temperature results from hydrogen transportation along the grain boundaries and not in the lattice.