A nickel-based coating was deposited on the pure Al substrate by immersion plating,and the Al/Cu bimetals were prepared by diffusion bonding in the temperature range of 450-550 ℃.The interce microstructure and fractu...A nickel-based coating was deposited on the pure Al substrate by immersion plating,and the Al/Cu bimetals were prepared by diffusion bonding in the temperature range of 450-550 ℃.The interce microstructure and fracture surface of Al/Cu joints were studied by scanning electron microscopy（SEM） and X-ray diffraction（XRD）.The mechanical properties of the Al/Cu bimetals were measured by tensile shear and microhardness tests.The results show that the Ni interiayer can effectively eliminate the formation of Al-Cu intermetallic compounds.The Al/Ni interface consists of the Al3Ni and Al3Ni2 phases,while it is Ni-Cu solid solution at the Ni/Cu interce.The tensile shear strength of the joints is improved by the addition of Ni interiayer.The joint with Ni interiayer annealed at 500 ℃ exhibits a maximum value of tensile shear strength of 34.7 MPa.展开更多
The interfacial interaction existing in the Ni ZrO 2 composite plating has been investigated. The experimental results show that no new phases were formed in the interfacial regions between matrix Ni and ZrO 2 part...The interfacial interaction existing in the Ni ZrO 2 composite plating has been investigated. The experimental results show that no new phases were formed in the interfacial regions between matrix Ni and ZrO 2 particles, but an orbital interaction through the mutual overlap of the d orbits does exist in the interfacial regions between Ni atoms and Zr 3+ ions.展开更多
The geometries of the molecules of eight organic additives were optimized and the net charge,E HOMO andE LUMO were obtained using AM method, respectively. The result shows that there is the correlation between the lev...The geometries of the molecules of eight organic additives were optimized and the net charge,E HOMO andE LUMO were obtained using AM method, respectively. The result shows that there is the correlation between the leveling property and the frontier orbital energy levels of these additives, and the adsorption models and leveling mechanics were discussed. The rule between the frontier orbital energy levels and the leveling property is verified by the experiments.展开更多
The composition of magnesium alloys is greatly associated with initial deposition behavior of electroless Ni-P coatings.Thus,the initial deposition behavior of electroless Ni–P coatings on ZK60 and ME20 alloys was in...The composition of magnesium alloys is greatly associated with initial deposition behavior of electroless Ni-P coatings.Thus,the initial deposition behavior of electroless Ni–P coatings on ZK60 and ME20 alloys was investigated.The results indicated that differences in the alloy compositions significantly influenced the initial deposition process and the adhesive strength,corrosion resistance,and crystal structure.The initial deposition of coatings on ZK60 and ME20 alloys preferentially occurred on the precipitates.The precipitates in ZK60 alloy had higher chemical activity after HF activation and controlled the initial deposition rate of the coating.The initial deposition rate of the coating on ME20 alloy mainly depended on the density of the Mg F2 film formed by HF activation rather than on the precipitates.Owing to differences in the initial deposition process,the coating on ZK60 alloy had higher adhesive strength and better corrosion resistance than that on ME20 alloy.The coatings on ZK60 and ME20 alloys mainly had crystalline structures,and the coating on ME20 alloy had also a slight microcrystalline structure.展开更多
A Ni-P coating was deposited on Cu substrate by electroless plating and the Al/Cu bimetal was produced by solid？liquid compound casting technology. The microstructure, mechanical properties and conductivity of Al/Cu ...A Ni-P coating was deposited on Cu substrate by electroless plating and the Al/Cu bimetal was produced by solid？liquid compound casting technology. The microstructure, mechanical properties and conductivity of Al/Cu joints with different process parameters （bonding temperature and preheating time） were investigated. The results showed that intermetallics formed at the interface and the thickness and variety increased with the increase of bonding temperature and preheating time. The Ni？P interlayer functioned as a diffusion barrier and protective film which effectively reduced the formation of intermetallics. The shear strength and conductivity of Al/Cu bimetal were reduced by increasing the thickness of intermetallics. In particular, the detrimental effect of Al2Cu phase was more obvious compared with the others. The sample preheated at 780 ℃ for 150 s exhibited the maximum shear strength and conductivity of 49.8 MPa and 5.29×10^5 S/cm, respectively.展开更多
基金Projects (51274054,51375070,51271042) supported by the National Natural Science Foundation of ChinaProjects (2013M530913) supported by the China Postdoctoral Science Foundation
文摘A nickel-based coating was deposited on the pure Al substrate by immersion plating,and the Al/Cu bimetals were prepared by diffusion bonding in the temperature range of 450-550 ℃.The interce microstructure and fracture surface of Al/Cu joints were studied by scanning electron microscopy（SEM） and X-ray diffraction（XRD）.The mechanical properties of the Al/Cu bimetals were measured by tensile shear and microhardness tests.The results show that the Ni interiayer can effectively eliminate the formation of Al-Cu intermetallic compounds.The Al/Ni interface consists of the Al3Ni and Al3Ni2 phases,while it is Ni-Cu solid solution at the Ni/Cu interce.The tensile shear strength of the joints is improved by the addition of Ni interiayer.The joint with Ni interiayer annealed at 500 ℃ exhibits a maximum value of tensile shear strength of 34.7 MPa.
文摘The interfacial interaction existing in the Ni ZrO 2 composite plating has been investigated. The experimental results show that no new phases were formed in the interfacial regions between matrix Ni and ZrO 2 particles, but an orbital interaction through the mutual overlap of the d orbits does exist in the interfacial regions between Ni atoms and Zr 3+ ions.
基金The National Natural Science Foundation of China(59331030)
文摘The geometries of the molecules of eight organic additives were optimized and the net charge,E HOMO andE LUMO were obtained using AM method, respectively. The result shows that there is the correlation between the leveling property and the frontier orbital energy levels of these additives, and the adsorption models and leveling mechanics were discussed. The rule between the frontier orbital energy levels and the leveling property is verified by the experiments.
文摘The composition of magnesium alloys is greatly associated with initial deposition behavior of electroless Ni-P coatings.Thus,the initial deposition behavior of electroless Ni–P coatings on ZK60 and ME20 alloys was investigated.The results indicated that differences in the alloy compositions significantly influenced the initial deposition process and the adhesive strength,corrosion resistance,and crystal structure.The initial deposition of coatings on ZK60 and ME20 alloys preferentially occurred on the precipitates.The precipitates in ZK60 alloy had higher chemical activity after HF activation and controlled the initial deposition rate of the coating.The initial deposition rate of the coating on ME20 alloy mainly depended on the density of the Mg F2 film formed by HF activation rather than on the precipitates.Owing to differences in the initial deposition process,the coating on ZK60 alloy had higher adhesive strength and better corrosion resistance than that on ME20 alloy.The coatings on ZK60 and ME20 alloys mainly had crystalline structures,and the coating on ME20 alloy had also a slight microcrystalline structure.
基金Project(51571080)supported by the National Natural Science Foundation of China
文摘A Ni-P coating was deposited on Cu substrate by electroless plating and the Al/Cu bimetal was produced by solid？liquid compound casting technology. The microstructure, mechanical properties and conductivity of Al/Cu joints with different process parameters （bonding temperature and preheating time） were investigated. The results showed that intermetallics formed at the interface and the thickness and variety increased with the increase of bonding temperature and preheating time. The Ni？P interlayer functioned as a diffusion barrier and protective film which effectively reduced the formation of intermetallics. The shear strength and conductivity of Al/Cu bimetal were reduced by increasing the thickness of intermetallics. In particular, the detrimental effect of Al2Cu phase was more obvious compared with the others. The sample preheated at 780 ℃ for 150 s exhibited the maximum shear strength and conductivity of 49.8 MPa and 5.29×10^5 S/cm, respectively.