Al-4.9 Fe-4.9 Ni alloy powders have been synthesized by mechanical alloying. The rnechanically alloyed powders are consolidated by hot hydrostatic extrusion. The results show that extrusion tempereture. extrusion rati...Al-4.9 Fe-4.9 Ni alloy powders have been synthesized by mechanical alloying. The rnechanically alloyed powders are consolidated by hot hydrostatic extrusion. The results show that extrusion tempereture. extrusion ratio and lubricant have great effects on the quality of extruded rods and their mechanical properties, The mixture of graphite and glass powders as lubricant can prevent the oxidization of cold compacted billet by cladding the billet with this lubricant before heating. This technique greatly simplifies the conventional densification process of powders展开更多
Fine Ni powder is often added to Co and bronze-based metal binder powders for diamond tool segments.Ni is a lower cost substitute for extra-fine Co powder and increases the toughness of Co-Fe diamond binders at the ex...Fine Ni powder is often added to Co and bronze-based metal binder powders for diamond tool segments.Ni is a lower cost substitute for extra-fine Co powder and increases the toughness of Co-Fe diamond binders at the expense of lower hardness and bend strength.In bronze-based diamond binder segments,Ni increases hardness and yield strength.Several grades of Ni powder are used commercially with both Co and bronze-based diamond binders.This paper compares properties of diamond binders containing carbonyl Ni powders including standard Inco(?) T255,T123 PM and T 110 PM.Binder materials were made by ball milling or dry mixing of the fine carbonyl Ni and Fe powders with either XF Co or air atomized bronze(90/10 Cu/Sn) powders.Co-based powder blends were hot pressed at 20～35 MPa and 700℃to 900℃.Bronze-based powder blends were cold pressed and sintered at 840℃.Apparent density,apparent hardness and bend strength(TRS) were compared for different binder compositions and processing conditions.展开更多
Nickel is a heavy metal which has the potential threaten to human's health and attracts public concern recently. The carbonized leaf powder is expected as suitable adsorbent for Ni(II) removal became of the compos...Nickel is a heavy metal which has the potential threaten to human's health and attracts public concern recently. The carbonized leaf powder is expected as suitable adsorbent for Ni(II) removal became of the composition of some beneficial groups. In this work, carbonized leaf powder was evaluated for its adsorption performance towards Ni(II). According to the results, adsorbent component, dosage, initial solute concentration, solution p H, temperature and contact time can significantly affect the efficiency of Ni(II) removal. Sips model fits the test results best, and the adsorption capacity towards Ni(II) is determined around 37.62 mg/g. The thermodynamic behaviors reveal the endothermic and spontaneous nature of the adsorption. The free adsorption energy(fluctuate around 8 k J/mol) predicted by D-R model indicates that the adsorption capacity originated from both physical and chemical adsorption. Room temperature(15-25 °C) is suitable for Ni(II) removal as well as low energy consumption for temperature enhancement. Further conclusions about the mechanism of chemical adsorption are obtained through analysis of the FT-IR test and XRD spectra, which indicates that the adsorption process occurs predominantly between amine, carbonate, phosphate and nickel ions.展开更多
The brown metallic luster La-Ni alloy powders were prepared by potentiostatic electrolysis technique in dimethylsulfoxide solution at room temperature. The atomic rate of La and Ni in alloy powders are 11∶1 and 10∶1...The brown metallic luster La-Ni alloy powders were prepared by potentiostatic electrolysis technique in dimethylsulfoxide solution at room temperature. The atomic rate of La and Ni in alloy powders are 11∶1 and 10∶1. The size of metal grains is about 0.1 to 100 μm. It shows that the micrometer powders of rare earth alloys can be obtained by controlling electrodeposition conditions. The peak potentials of -2.81 and 1.75 V are attributed to reduction of La 3+ and Ni 3+ ions, respectively. The peak potentials at -2.20 and -0.168 V are the oxidation peaks of lanthanum and nickel, respectively. When potential is more negative than -1.74 V, La(Ⅲ) and Ni(Ⅱ) will codeposit. Increasing cyclic times, the value of peak current is decreasing, and the reduction peak of La(Ⅲ) was finally disappeared.展开更多
The Ni_3B phase was formed when boron (0.5 at. pct B) was added to the intermetallic of sto- ichiometric and off-stoichiometric (Ni-24 at. pct Al) compounds. In the alloy of stoichiometric composition the particles o...The Ni_3B phase was formed when boron (0.5 at. pct B) was added to the intermetallic of sto- ichiometric and off-stoichiometric (Ni-24 at. pct Al) compounds. In the alloy of stoichiometric composition the particles of Ni_3B phase has the size around 0.1μm and is located on the grain boundary of the main phase. The decreasing of concentrations of Al in the ofF-stoichiometric alloy leads to increase in the degree of the long-range order parameter, increasing the concen- trations of boron in the solid solution and decreasing its localization on the grain boundary. Microalloying of boron leads to increasing in the fraction of grain monodomains with disloca- tions up to 0.7 in the alloy of the off-stoichiometric composition and up to 1 in the alloy of the stoichiometric composition. It was established the correlation between the degree of the concentration inhomogeneity, average density of the dislocations and the average long range-order parameter.展开更多
It was shown by TEM and X-ray analysis that there are four types of grains of the main Ni3Al phase in the structure of the intermetallic obtained by the self-propagation high temperature method (SHS). Every type of gr...It was shown by TEM and X-ray analysis that there are four types of grains of the main Ni3Al phase in the structure of the intermetallic obtained by the self-propagation high temperature method (SHS). Every type of grains has its own domain and dislocation structure. There are mono- and polydomains with and without dislocations. The grains of the main phase of monoand polydomains without dislocations and polydomains with dislocations were formed by diffusion in the solid phase. In these conditions NiAl3 phase is located on the grain boundary of the main phase. The Ni2Al3 phase is located at the triple joints of the main phase.展开更多
This study aimed to investigate the biosorption potential of Na2CO3-modified Aloe barbadensis Miller (Aloe vera) leaf (MABL) powder for removal of Ni(II) ions from a synthetic aqueous solution. Effects of various proc...This study aimed to investigate the biosorption potential of Na2CO3-modified Aloe barbadensis Miller (Aloe vera) leaf (MABL) powder for removal of Ni(II) ions from a synthetic aqueous solution. Effects of various process parameters (pH, equilibrium time, and temperature) were investigated in order to optimize the biosorptive removal. The maximum biosorption capacity of MABL was observed to be 28.986 mg/g at a temperature of 303 K, a biosorbent dose of 0.6 g, a contact time of 90 min, and a pH value of 7. Different kinetic models (the pseudo-first-order, pseudo-second-order, Elovich, and intraparticle diffusion models) were evaluated. The pseudo-second-order kinetic model was found to be the best fitted model in this study, with a coefficient of determination of R^2 =0.974. Five different isotherm models (the Langmuir, Freundlich, Temkin, Dubinin-Radushkevich, and Brunauer-Emmett-Teller (BET) models) were investigated to identify the best-suited isotherm model for the present system. Based on the minimum chi-square value (X^2 =0.027) and the maximum coefficient of determination (R^2 =0.996), the Langmuir isotherm model was found to represent the system well, indicating the possibility of monolayer biosorption. The sticking probability (S*) was found to be 0.41, suggesting a physisorption mechanism for biosorption of Ni(II) on MABL. The biosorbent was characterized using Fourier-transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), zeta potential, and BET surface area, in order to understand its morphological and functional characteristics.展开更多
Ni/C core-shell composite powders were prepared by electroless nickel-plating. The effects of concentration of NiSO4,bathing temperature,ratio of hydrazine hydrate to NiSO4,pH of the solution,amounts of complexing rea...Ni/C core-shell composite powders were prepared by electroless nickel-plating. The effects of concentration of NiSO4,bathing temperature,ratio of hydrazine hydrate to NiSO4,pH of the solution,amounts of complexing reagent and surfactant,bath load of activated carbon and reaction time,and so on,on the preparation of Ni/C core-shell composite powders were studied. The results show that the principal factors for Ni/C composite powders preparation are bathing temperature,ratio of hydrazine hydrate to NiSO4 and pH of the solution. The optimum conditions are plating at 90 ℃ with pH10.7 and molar ratio of N2H4·H2O to Ni2+of 3.0. The plated nickel powders are observed to be sphere-like in morphology with size about 100 nm. The maximum dielectric loss of Ni/C core-shell composite powders is about 0.35,and its magnetic loss was low with value about 0 in 2-16 GHz.展开更多
文摘Al-4.9 Fe-4.9 Ni alloy powders have been synthesized by mechanical alloying. The rnechanically alloyed powders are consolidated by hot hydrostatic extrusion. The results show that extrusion tempereture. extrusion ratio and lubricant have great effects on the quality of extruded rods and their mechanical properties, The mixture of graphite and glass powders as lubricant can prevent the oxidization of cold compacted billet by cladding the billet with this lubricant before heating. This technique greatly simplifies the conventional densification process of powders
文摘Fine Ni powder is often added to Co and bronze-based metal binder powders for diamond tool segments.Ni is a lower cost substitute for extra-fine Co powder and increases the toughness of Co-Fe diamond binders at the expense of lower hardness and bend strength.In bronze-based diamond binder segments,Ni increases hardness and yield strength.Several grades of Ni powder are used commercially with both Co and bronze-based diamond binders.This paper compares properties of diamond binders containing carbonyl Ni powders including standard Inco(?) T255,T123 PM and T 110 PM.Binder materials were made by ball milling or dry mixing of the fine carbonyl Ni and Fe powders with either XF Co or air atomized bronze(90/10 Cu/Sn) powders.Co-based powder blends were hot pressed at 20～35 MPa and 700℃to 900℃.Bronze-based powder blends were cold pressed and sintered at 840℃.Apparent density,apparent hardness and bend strength(TRS) were compared for different binder compositions and processing conditions.
基金Projects(5117916851308310)supported by the National Natural Science Foundation of China+1 种基金Project(LQ13E080007)supported by Zhejiang Provincial Natural Science Foundation,ChinaProject supported by the Scientific Research Foundation for the Returned Overseas Chinese Scholars of Jiangsu Province,China
文摘Nickel is a heavy metal which has the potential threaten to human's health and attracts public concern recently. The carbonized leaf powder is expected as suitable adsorbent for Ni(II) removal became of the composition of some beneficial groups. In this work, carbonized leaf powder was evaluated for its adsorption performance towards Ni(II). According to the results, adsorbent component, dosage, initial solute concentration, solution p H, temperature and contact time can significantly affect the efficiency of Ni(II) removal. Sips model fits the test results best, and the adsorption capacity towards Ni(II) is determined around 37.62 mg/g. The thermodynamic behaviors reveal the endothermic and spontaneous nature of the adsorption. The free adsorption energy(fluctuate around 8 k J/mol) predicted by D-R model indicates that the adsorption capacity originated from both physical and chemical adsorption. Room temperature(15-25 °C) is suitable for Ni(II) removal as well as low energy consumption for temperature enhancement. Further conclusions about the mechanism of chemical adsorption are obtained through analysis of the FT-IR test and XRD spectra, which indicates that the adsorption process occurs predominantly between amine, carbonate, phosphate and nickel ions.
文摘The brown metallic luster La-Ni alloy powders were prepared by potentiostatic electrolysis technique in dimethylsulfoxide solution at room temperature. The atomic rate of La and Ni in alloy powders are 11∶1 and 10∶1. The size of metal grains is about 0.1 to 100 μm. It shows that the micrometer powders of rare earth alloys can be obtained by controlling electrodeposition conditions. The peak potentials of -2.81 and 1.75 V are attributed to reduction of La 3+ and Ni 3+ ions, respectively. The peak potentials at -2.20 and -0.168 V are the oxidation peaks of lanthanum and nickel, respectively. When potential is more negative than -1.74 V, La(Ⅲ) and Ni(Ⅱ) will codeposit. Increasing cyclic times, the value of peak current is decreasing, and the reduction peak of La(Ⅲ) was finally disappeared.
文摘The Ni_3B phase was formed when boron (0.5 at. pct B) was added to the intermetallic of sto- ichiometric and off-stoichiometric (Ni-24 at. pct Al) compounds. In the alloy of stoichiometric composition the particles of Ni_3B phase has the size around 0.1μm and is located on the grain boundary of the main phase. The decreasing of concentrations of Al in the ofF-stoichiometric alloy leads to increase in the degree of the long-range order parameter, increasing the concen- trations of boron in the solid solution and decreasing its localization on the grain boundary. Microalloying of boron leads to increasing in the fraction of grain monodomains with disloca- tions up to 0.7 in the alloy of the off-stoichiometric composition and up to 1 in the alloy of the stoichiometric composition. It was established the correlation between the degree of the concentration inhomogeneity, average density of the dislocations and the average long range-order parameter.
文摘It was shown by TEM and X-ray analysis that there are four types of grains of the main Ni3Al phase in the structure of the intermetallic obtained by the self-propagation high temperature method (SHS). Every type of grains has its own domain and dislocation structure. There are mono- and polydomains with and without dislocations. The grains of the main phase of monoand polydomains without dislocations and polydomains with dislocations were formed by diffusion in the solid phase. In these conditions NiAl3 phase is located on the grain boundary of the main phase. The Ni2Al3 phase is located at the triple joints of the main phase.
文摘This study aimed to investigate the biosorption potential of Na2CO3-modified Aloe barbadensis Miller (Aloe vera) leaf (MABL) powder for removal of Ni(II) ions from a synthetic aqueous solution. Effects of various process parameters (pH, equilibrium time, and temperature) were investigated in order to optimize the biosorptive removal. The maximum biosorption capacity of MABL was observed to be 28.986 mg/g at a temperature of 303 K, a biosorbent dose of 0.6 g, a contact time of 90 min, and a pH value of 7. Different kinetic models (the pseudo-first-order, pseudo-second-order, Elovich, and intraparticle diffusion models) were evaluated. The pseudo-second-order kinetic model was found to be the best fitted model in this study, with a coefficient of determination of R^2 =0.974. Five different isotherm models (the Langmuir, Freundlich, Temkin, Dubinin-Radushkevich, and Brunauer-Emmett-Teller (BET) models) were investigated to identify the best-suited isotherm model for the present system. Based on the minimum chi-square value (X^2 =0.027) and the maximum coefficient of determination (R^2 =0.996), the Langmuir isotherm model was found to represent the system well, indicating the possibility of monolayer biosorption. The sticking probability (S*) was found to be 0.41, suggesting a physisorption mechanism for biosorption of Ni(II) on MABL. The biosorbent was characterized using Fourier-transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), zeta potential, and BET surface area, in order to understand its morphological and functional characteristics.
基金Project (0512002400) supported by Science Fund for Distinguished Young Scholars of Henan Province, China
文摘Ni/C core-shell composite powders were prepared by electroless nickel-plating. The effects of concentration of NiSO4,bathing temperature,ratio of hydrazine hydrate to NiSO4,pH of the solution,amounts of complexing reagent and surfactant,bath load of activated carbon and reaction time,and so on,on the preparation of Ni/C core-shell composite powders were studied. The results show that the principal factors for Ni/C composite powders preparation are bathing temperature,ratio of hydrazine hydrate to NiSO4 and pH of the solution. The optimum conditions are plating at 90 ℃ with pH10.7 and molar ratio of N2H4·H2O to Ni2+of 3.0. The plated nickel powders are observed to be sphere-like in morphology with size about 100 nm. The maximum dielectric loss of Ni/C core-shell composite powders is about 0.35,and its magnetic loss was low with value about 0 in 2-16 GHz.