In order to improve the low ductility of the Mo-Ni alloy,Fe is added and the effects of Ni/Fe mass ratio on the densification behavior,microstructure evolution and mechanical properties of alloy were investigated.The ...In order to improve the low ductility of the Mo-Ni alloy,Fe is added and the effects of Ni/Fe mass ratio on the densification behavior,microstructure evolution and mechanical properties of alloy were investigated.The experimental results show that when iron is added to 95Mo-5Ni alloy,the formation of brittle intermetallic phaseδ-MoNi at the grain boundary is avoided.Meanwhile,the grain growth of Mo is also effectively inhibited in the sintering process.However,the addition of iron reduces the degree of densification of alloy since the activation effect of Ni is superior to that of Fe.From the experimental results,it could be concluded that the maximum hardness and bending strength are achieved by 95Mo-1.5Ni-3.5Fe alloy,which are HV 614 and 741 MPa,respectively.Combined with the analyses of bending fracture mechanism,the improvement relative to Mo-Ni alloy is likely attributed to the inhibition of the brittle phase.展开更多
The precursor prepared by coordinated co-precipitation was direct reduced by hydrogen to ultra-fine fibrous Fe-Ni alloy powder. The effects of concentrations of reactants, pH value, reaction temperature and additive o...The precursor prepared by coordinated co-precipitation was direct reduced by hydrogen to ultra-fine fibrous Fe-Ni alloy powder. The effects of concentrations of reactants, pH value, reaction temperature and additive on the preparation of precursor were systematically investigated. The structures, thermal decomposition processes and morphologies of the precursors were characterized by X-ray diffraction (XRD), thermal gravity-differential thermal analysis (TG-DTA) and scanning electron microscoy (SEM). The results show that using 2% polyvinylpyrrolidone (PVP) (in mass fraction) as additive, a well-dispersed precursor with a uniform morphology can be obtained in a solution with Fe2+ and Ni2+ total concentration (1:1) of 0.8 mol/L, pH value of 6.2 at 60 °C, and a pure and well dispersed fibrous iron-nickel powder can be prepared by direct reduction of this precursor in a mixed atmosphere of nitrogen and hydrogen at the temperature of 420 °C.展开更多
采用CALPHAD(calculation of phase diagram)方法对Fe-V和Ni-V二元系进行了热力学优化,并结合第一性原理计算,利用(A,B)_(10)(A,B)_(4)(A,B)_(16)三亚点阵模型描述σ相,首次成功地描述了σ相的占位分数。使用优化的模型参数不仅可以描述...采用CALPHAD(calculation of phase diagram)方法对Fe-V和Ni-V二元系进行了热力学优化,并结合第一性原理计算,利用(A,B)_(10)(A,B)_(4)(A,B)_(16)三亚点阵模型描述σ相,首次成功地描述了σ相的占位分数。使用优化的模型参数不仅可以描述Fe-V和Ni-V系热化学性质,而且可以很好地重现Fe-V和Ni-V系的相平衡关系,为高熵合金多组元热力学数据库的建立奠定基础。展开更多
Ni80Fe20/Ni48Fe12Cr40 bilayer films and Ni80Fe20 monolayer films were deposited at room temperature on SiO2/Si（100） substrates by electron beam evaporation. The influence of the thickness of the Ni48Fe12Cr40 underla...Ni80Fe20/Ni48Fe12Cr40 bilayer films and Ni80Fe20 monolayer films were deposited at room temperature on SiO2/Si（100） substrates by electron beam evaporation. The influence of the thickness of the Ni48Fe12Cr40 underlayer on the structure, magnetization, and magnetoresistance of the Ni80Fe20/Ni48Fe12Cr40 bilayer film was investigated. The thickness of the Ni48Fe12Cr40 layer varied from about 1 nm to 18 nm while the Ni80Fe20 layer thickness was fixed at 45 nm. For the as-deposited bilayer films the introducing of the Ni48Fe12Cr40 underlayer promotes both the （111） texture and grain growth in the Ni80Fe20 layer. The Ni48Fe12Cr40 underlayer has no significant influence on the magnetic moment of the Ni80Fe20/Ni48Fe12Cr40 bilayer film. However, the coercivity of the bilayer film changes with the thickness of the Ni48Fe12Cr40 undedayer. The optimum thickness of the Ni48Fe12Cr40 underlayer for improving the anisotropic magnetoresistance effect of the Ni80Fe20/Ni48Fe12Cr40 bilayer film is about 5 nm. With a decrease in temperature from 300 K to 81 K, the anisotropic magnetoresistance ratio of the Ni80Fe20 （45 nm）/Ni48Fe12Cr40 （5 nm） bilayer film increases linearly from 2.1% to 4.8% compared with that of the Ni80Fe20 monolayer film from 1.7% to 4.0%.展开更多
The role of Fe/S ratios(ω, g/g) in the uranium bioleaching from a complex uranium ore by Acidithiobacillus ferrooxidans and Acidithiobacillus thiooxidans consortium was investigated. The results showed good uranium e...The role of Fe/S ratios(ω, g/g) in the uranium bioleaching from a complex uranium ore by Acidithiobacillus ferrooxidans and Acidithiobacillus thiooxidans consortium was investigated. The results showed good uranium extraction with over 90% at the Fe/S ratio of 5:0.5, 5:1 and 5:5, while poor extraction(<46%) at the Fe/S ratio of 5:0 and 5:10.Furthermore, the bacterial community analysis based on species-specific gyrB numbers indicated that, absent sulfur or excessive sulfur would be not conducive to the synergistic growth for A. ferrooxidans and A. thiooxidans, and then not conducive to the uranium dissolution. Meanwhile, the sulfur-oxidizers could play an important role in the process of uranium synergistic bioleaching by mixed bacterial consortia. Additionally, the characteristics of mineral residue was detected by SEM-EDS. The results showed appropriate sulfur dosage would change the structure and improve the porosity of passivation substance. Lastly, the uranium dissolution kinetics and biochemical reaction mechanism was analyzed. It indicated that the biochemical reaction coupling iron and sulfur had a pleiotropic effect on the uranium dissolution from the ore particles, appropriate Fe/S ratio is the key factor for uranium bioleaching by chemoautotrophic acidophiles.展开更多
基金Project(51734002)supported by the National Natural Science Foundation of China。
文摘In order to improve the low ductility of the Mo-Ni alloy,Fe is added and the effects of Ni/Fe mass ratio on the densification behavior,microstructure evolution and mechanical properties of alloy were investigated.The experimental results show that when iron is added to 95Mo-5Ni alloy,the formation of brittle intermetallic phaseδ-MoNi at the grain boundary is avoided.Meanwhile,the grain growth of Mo is also effectively inhibited in the sintering process.However,the addition of iron reduces the degree of densification of alloy since the activation effect of Ni is superior to that of Fe.From the experimental results,it could be concluded that the maximum hardness and bending strength are achieved by 95Mo-1.5Ni-3.5Fe alloy,which are HV 614 and 741 MPa,respectively.Combined with the analyses of bending fracture mechanism,the improvement relative to Mo-Ni alloy is likely attributed to the inhibition of the brittle phase.
基金Project (20090162120080) supported by the Research Fund for Doctoral Program of Higher Education of ChinaProject (2010FJ3011)supported by the Program of Science and Technology of Hunan Province, ChinaProject supported by the Open-End Fund for the Valuable and Precision Instruments of Central South University, China
文摘The precursor prepared by coordinated co-precipitation was direct reduced by hydrogen to ultra-fine fibrous Fe-Ni alloy powder. The effects of concentrations of reactants, pH value, reaction temperature and additive on the preparation of precursor were systematically investigated. The structures, thermal decomposition processes and morphologies of the precursors were characterized by X-ray diffraction (XRD), thermal gravity-differential thermal analysis (TG-DTA) and scanning electron microscoy (SEM). The results show that using 2% polyvinylpyrrolidone (PVP) (in mass fraction) as additive, a well-dispersed precursor with a uniform morphology can be obtained in a solution with Fe2+ and Ni2+ total concentration (1:1) of 0.8 mol/L, pH value of 6.2 at 60 °C, and a pure and well dispersed fibrous iron-nickel powder can be prepared by direct reduction of this precursor in a mixed atmosphere of nitrogen and hydrogen at the temperature of 420 °C.
文摘采用CALPHAD(calculation of phase diagram)方法对Fe-V和Ni-V二元系进行了热力学优化,并结合第一性原理计算,利用(A,B)_(10)(A,B)_(4)(A,B)_(16)三亚点阵模型描述σ相,首次成功地描述了σ相的占位分数。使用优化的模型参数不仅可以描述Fe-V和Ni-V系热化学性质,而且可以很好地重现Fe-V和Ni-V系的相平衡关系,为高熵合金多组元热力学数据库的建立奠定基础。
文摘Ni80Fe20/Ni48Fe12Cr40 bilayer films and Ni80Fe20 monolayer films were deposited at room temperature on SiO2/Si（100） substrates by electron beam evaporation. The influence of the thickness of the Ni48Fe12Cr40 underlayer on the structure, magnetization, and magnetoresistance of the Ni80Fe20/Ni48Fe12Cr40 bilayer film was investigated. The thickness of the Ni48Fe12Cr40 layer varied from about 1 nm to 18 nm while the Ni80Fe20 layer thickness was fixed at 45 nm. For the as-deposited bilayer films the introducing of the Ni48Fe12Cr40 underlayer promotes both the （111） texture and grain growth in the Ni80Fe20 layer. The Ni48Fe12Cr40 underlayer has no significant influence on the magnetic moment of the Ni80Fe20/Ni48Fe12Cr40 bilayer film. However, the coercivity of the bilayer film changes with the thickness of the Ni48Fe12Cr40 undedayer. The optimum thickness of the Ni48Fe12Cr40 underlayer for improving the anisotropic magnetoresistance effect of the Ni80Fe20/Ni48Fe12Cr40 bilayer film is about 5 nm. With a decrease in temperature from 300 K to 81 K, the anisotropic magnetoresistance ratio of the Ni80Fe20 （45 nm）/Ni48Fe12Cr40 （5 nm） bilayer film increases linearly from 2.1% to 4.8% compared with that of the Ni80Fe20 monolayer film from 1.7% to 4.0%.
基金Project(51804165) supported by the National Natural Science Foundation of ChinaProject(2018JJ3441) supported by the Natural Science Foundation of Hunan Province,China。
文摘The role of Fe/S ratios(ω, g/g) in the uranium bioleaching from a complex uranium ore by Acidithiobacillus ferrooxidans and Acidithiobacillus thiooxidans consortium was investigated. The results showed good uranium extraction with over 90% at the Fe/S ratio of 5:0.5, 5:1 and 5:5, while poor extraction(<46%) at the Fe/S ratio of 5:0 and 5:10.Furthermore, the bacterial community analysis based on species-specific gyrB numbers indicated that, absent sulfur or excessive sulfur would be not conducive to the synergistic growth for A. ferrooxidans and A. thiooxidans, and then not conducive to the uranium dissolution. Meanwhile, the sulfur-oxidizers could play an important role in the process of uranium synergistic bioleaching by mixed bacterial consortia. Additionally, the characteristics of mineral residue was detected by SEM-EDS. The results showed appropriate sulfur dosage would change the structure and improve the porosity of passivation substance. Lastly, the uranium dissolution kinetics and biochemical reaction mechanism was analyzed. It indicated that the biochemical reaction coupling iron and sulfur had a pleiotropic effect on the uranium dissolution from the ore particles, appropriate Fe/S ratio is the key factor for uranium bioleaching by chemoautotrophic acidophiles.