The deactivation of Ni/SiO2-Al2 O3 catalyst in hydrogenation of crude 1,4-butanediol was investigated.During the operation time of 2140 h,the catalyst showed slow activity decay.Characterization results,for four spent...The deactivation of Ni/SiO2-Al2 O3 catalyst in hydrogenation of crude 1,4-butanediol was investigated.During the operation time of 2140 h,the catalyst showed slow activity decay.Characterization results,for four spent catalysts used at different time,indicated that the main reason of the catalyst deactivation was the deposition of carbonaceous species that covered the active Ni and blocked mesopores of the catalyst.The TPO and SEM measurements revealed that the carbonaceous species included both oligomeric and polymeric species with high C/H ratio and showed sheet.Such carbonaceous species might be eliminated through either direct H2 reduction or the combined oxidation-reduction methodologies.展开更多
Ni/Al_2O_3-SiO_2 catalysts were synthesized via one-step method employing SiO_2 as an additive for the selective hydrogenation of butyne-1,4-diol(B_3D) to butane-1,4-diol(B1D). The prepared catalysts were evaluated by...Ni/Al_2O_3-SiO_2 catalysts were synthesized via one-step method employing SiO_2 as an additive for the selective hydrogenation of butyne-1,4-diol(B_3D) to butane-1,4-diol(B1D). The prepared catalysts were evaluated by a series of characterization techniques including BET, XRD, SEM, EDX-mapping, TEM, H_2-TPR, XPS, NH_3-TPD and Py-FTIR. Compared to Ni/Al_2O_3 catalyst, the SiO_2-doped samples exhibited better B_3D conversion. SiO_2 could help to form a strong interaction between NiO with the support, which inhibited Ni agglomeration at high temperature, improved the Ni dispersion, and enhanced the hydrogenation activity. B_1D selectivity was mainly influenced by the quantity of Lewis acid sites in addition to the Ni dispersion. The catalyst with a silica loading of 6.4% demonstrated an excellent selectivity of 75.18%(by 13% higher than the contrastive Ni/Al_2O_3 catalyst), which was attributed to the larger amount of Lewis acid sites and the moderate interaction between NiO with the support, which could facilitate the nickel dispersion on a preferable surface area of 176.3 m^2/g of support.展开更多
This article reports the production of COx free hydrogen and carbon nanofibers by the catalytic decomposition of methane over Ni-Al2O3-SiO2 catalysts. The influence of reaction temperature, pretreatment temperature, a...This article reports the production of COx free hydrogen and carbon nanofibers by the catalytic decomposition of methane over Ni-Al2O3-SiO2 catalysts. The influence of reaction temperature, pretreatment temperature, and effect of reductive pretreatment on the decomposition of methane activity is investigated. The physico-chemical characteristics of fresh and deactivated samples were characterized using BET-SA, XRD, TPR, SEM/TEM, CHNS analyses and correlated with the methane decomposition results obtained. The Ni-Al-Si (4 : 0.5 : 1.5) catalyst reduced with hydrazine hydrate produced better H2 yields of ca. 1815 mol H2/mol Ni than the catalyst reduced with 5% H2/N2.展开更多
Coral reef-like Ni/Al2O3 catalysts were prepared by co-precipitation of nickel acetate and aluminium nitrate with sodium carbonate aqueous solution in the medium of ethylene glycolye.Methanation of syngas was carried ...Coral reef-like Ni/Al2O3 catalysts were prepared by co-precipitation of nickel acetate and aluminium nitrate with sodium carbonate aqueous solution in the medium of ethylene glycolye.Methanation of syngas was carried out over coral reef-like Ni/Al2O3 catalysts in a continuous flow type fixed-bed reactor.The structure and properties of the fresh and used catalysts were studied by SEM,N2 adsorption-desorption,XRD,H2-TPR,O2-TPO,TG and ICP-AES techniques.The results showed that the coral reef-like Ni/Al2O3 catalysts exhibited better activity than the conventional Ni/Al2O3-H2O catalysts.The activities of coral reef-like catalysts were in the order of Ni/Al2O3-673Ni/Al2O3-573Ni/Al2O3- 473Ni/Al2O3-773.Ni/Al2O3-673-EG catalyst showed not only good activity and improved stability but also superior resistance to carbon deposition,sintering,and Ni loss.Under the reaction conditions of CO/H2(molar ratio)=1:3,593 K,atmospheric pressure and a GHSV of 2500 h-1,CH4 selectivity was 84.7%,and the CO conversion reached 98.2%.展开更多
Ni-based catalysts doped with copper additives were studied on their role in ethanol steam reforming reaction. The effects of Cu content, support species involving Al2O3-SIO2, Al2O3-MgO, Al2O3-ZnO, and Al2O3-La2O3, on...Ni-based catalysts doped with copper additives were studied on their role in ethanol steam reforming reaction. The effects of Cu content, support species involving Al2O3-SIO2, Al2O3-MgO, Al2O3-ZnO, and Al2O3-La2O3, on the catalytic performance were studied. Characterizations by TPR, XRD, NH3-TPD, XPS, and TGA indicated that catalysts 30Ni5Cu/Al2O3-MgO and 30Ni5Cu/Al2O3-ZnO have much higher H2 selectivity than 30Ni5Cu/Al2O3-SiO2, as well as good coke resistance. H2 selectivity for 30Ni5Cu/Al2O3-MgO catalyst was 73.3% at 450 ℃ and increased to 94.0% at 600℃, whereas for 30Ni5Cu/Al2O3-ZnO catalyst, the H2 selectivity was 63.6% at 450 ℃ and 95.2% at 600℃. TheseAl2O3-MgO and Al2O3-ZnO supported Ni-Cu bimetallic catalysts may have important applications in the production of hydrogen by ethanol steam reforming reactions.展开更多
Characteristics of carbon deposition of CH 4 and C 2H 4 decomposition over supported Ni and Ni Ce catalysts were studied by using a pulse reaction as well as BET, TPR, XPS and hydrogen chemisorption techniques. It...Characteristics of carbon deposition of CH 4 and C 2H 4 decomposition over supported Ni and Ni Ce catalysts were studied by using a pulse reaction as well as BET, TPR, XPS and hydrogen chemisorption techniques. It is found that there is a metal semiconductor interaction (MScI) in the Ni Ce catalyst, and the effect of MScI on the carbon deposition of CH 4 decomposition is opposite to that of C 2H 4. A novel model of carbon deposition of CH 4 or C 2H 4 decomposition was proposed.展开更多
基金Supported by the National Natural Science Foundation of China(21673132).
文摘The deactivation of Ni/SiO2-Al2 O3 catalyst in hydrogenation of crude 1,4-butanediol was investigated.During the operation time of 2140 h,the catalyst showed slow activity decay.Characterization results,for four spent catalysts used at different time,indicated that the main reason of the catalyst deactivation was the deposition of carbonaceous species that covered the active Ni and blocked mesopores of the catalyst.The TPO and SEM measurements revealed that the carbonaceous species included both oligomeric and polymeric species with high C/H ratio and showed sheet.Such carbonaceous species might be eliminated through either direct H2 reduction or the combined oxidation-reduction methodologies.
基金supported by the National Natural Science Foundation of China(21703194)the Natural Science Foundation of Jiangsu Province(BK20171168,BK20171169)+2 种基金Natural Science Foundation of Jiangsu Higher Education Institutions of China(17KJB530010,17KJB150038 and18KJA430015)Key Research Project of Social Development of Xuzhou(KC17154)Research Project of Xuzhou University of Technology(XKY2017217)
基金Financial support from the National Natural Science Foundation of China (21163019) is gratefully acknowledged
文摘Ni/Al_2O_3-SiO_2 catalysts were synthesized via one-step method employing SiO_2 as an additive for the selective hydrogenation of butyne-1,4-diol(B_3D) to butane-1,4-diol(B1D). The prepared catalysts were evaluated by a series of characterization techniques including BET, XRD, SEM, EDX-mapping, TEM, H_2-TPR, XPS, NH_3-TPD and Py-FTIR. Compared to Ni/Al_2O_3 catalyst, the SiO_2-doped samples exhibited better B_3D conversion. SiO_2 could help to form a strong interaction between NiO with the support, which inhibited Ni agglomeration at high temperature, improved the Ni dispersion, and enhanced the hydrogenation activity. B_1D selectivity was mainly influenced by the quantity of Lewis acid sites in addition to the Ni dispersion. The catalyst with a silica loading of 6.4% demonstrated an excellent selectivity of 75.18%(by 13% higher than the contrastive Ni/Al_2O_3 catalyst), which was attributed to the larger amount of Lewis acid sites and the moderate interaction between NiO with the support, which could facilitate the nickel dispersion on a preferable surface area of 176.3 m^2/g of support.
文摘This article reports the production of COx free hydrogen and carbon nanofibers by the catalytic decomposition of methane over Ni-Al2O3-SiO2 catalysts. The influence of reaction temperature, pretreatment temperature, and effect of reductive pretreatment on the decomposition of methane activity is investigated. The physico-chemical characteristics of fresh and deactivated samples were characterized using BET-SA, XRD, TPR, SEM/TEM, CHNS analyses and correlated with the methane decomposition results obtained. The Ni-Al-Si (4 : 0.5 : 1.5) catalyst reduced with hydrazine hydrate produced better H2 yields of ca. 1815 mol H2/mol Ni than the catalyst reduced with 5% H2/N2.
基金financially supported by Independent Research Subject from Ministry of Science and Technology of China(No.2008BWZ005)
文摘Coral reef-like Ni/Al2O3 catalysts were prepared by co-precipitation of nickel acetate and aluminium nitrate with sodium carbonate aqueous solution in the medium of ethylene glycolye.Methanation of syngas was carried out over coral reef-like Ni/Al2O3 catalysts in a continuous flow type fixed-bed reactor.The structure and properties of the fresh and used catalysts were studied by SEM,N2 adsorption-desorption,XRD,H2-TPR,O2-TPO,TG and ICP-AES techniques.The results showed that the coral reef-like Ni/Al2O3 catalysts exhibited better activity than the conventional Ni/Al2O3-H2O catalysts.The activities of coral reef-like catalysts were in the order of Ni/Al2O3-673Ni/Al2O3-573Ni/Al2O3- 473Ni/Al2O3-773.Ni/Al2O3-673-EG catalyst showed not only good activity and improved stability but also superior resistance to carbon deposition,sintering,and Ni loss.Under the reaction conditions of CO/H2(molar ratio)=1:3,593 K,atmospheric pressure and a GHSV of 2500 h-1,CH4 selectivity was 84.7%,and the CO conversion reached 98.2%.
基金973 Program (2006CB202500)the National Natural Science Foundation of China (20676096)New Century Excellent Talents in University.9gram (2006CB202500)
文摘Ni-based catalysts doped with copper additives were studied on their role in ethanol steam reforming reaction. The effects of Cu content, support species involving Al2O3-SIO2, Al2O3-MgO, Al2O3-ZnO, and Al2O3-La2O3, on the catalytic performance were studied. Characterizations by TPR, XRD, NH3-TPD, XPS, and TGA indicated that catalysts 30Ni5Cu/Al2O3-MgO and 30Ni5Cu/Al2O3-ZnO have much higher H2 selectivity than 30Ni5Cu/Al2O3-SiO2, as well as good coke resistance. H2 selectivity for 30Ni5Cu/Al2O3-MgO catalyst was 73.3% at 450 ℃ and increased to 94.0% at 600℃, whereas for 30Ni5Cu/Al2O3-ZnO catalyst, the H2 selectivity was 63.6% at 450 ℃ and 95.2% at 600℃. TheseAl2O3-MgO and Al2O3-ZnO supported Ni-Cu bimetallic catalysts may have important applications in the production of hydrogen by ethanol steam reforming reactions.
文摘Characteristics of carbon deposition of CH 4 and C 2H 4 decomposition over supported Ni and Ni Ce catalysts were studied by using a pulse reaction as well as BET, TPR, XPS and hydrogen chemisorption techniques. It is found that there is a metal semiconductor interaction (MScI) in the Ni Ce catalyst, and the effect of MScI on the carbon deposition of CH 4 decomposition is opposite to that of C 2H 4. A novel model of carbon deposition of CH 4 or C 2H 4 decomposition was proposed.