The microstructure,microhardness,and corrosion resistance of laser cladding Ni−WC coating on the surface of AlSi5Cu1Mg alloy were investigated by scanning electron microscopy,X-ray diffraction,microhardness testing,im...The microstructure,microhardness,and corrosion resistance of laser cladding Ni−WC coating on the surface of AlSi5Cu1Mg alloy were investigated by scanning electron microscopy,X-ray diffraction,microhardness testing,immersion corrosion testing,and electrochemical measurement.The results show that a smooth coating containing NiAl,Ni_(3)Al,M_(7)C_(3),M_(23)C_(6)phases(M=Ni,Al,Cr,W,Fe)and WC particles is prepared by laser cladding.Under a laser scanning speed of 120 mm/min,the microhardness of the cladding coating is 9−11 times that of AlSi5Cu1Mg,due to the synergistic effect of excellent metallurgical bond and newly formed carbides.The Ni−WC coating shows higher corrosion potential(−318.09 mV)and lower corrosion current density(12.33μA/cm^(2))compared with the matrix.The crack-free,dense cladding coating obviously inhibits the penetration of Cl^(−)and H^(+),leading to the remarkedly improved corrosion resistance of cladding coating.展开更多
Ni-Ag/TiC composite coating was prepared on the 45 steel substrates by means of laser cladding. Microstructure and wear properties of composite coatings were analyzed using optical microscopy, field emission scanning ...Ni-Ag/TiC composite coating was prepared on the 45 steel substrates by means of laser cladding. Microstructure and wear properties of composite coatings were analyzed using optical microscopy, field emission scanning electron microscopy and wear machine. The experimental results show that defects, such as cracks and pores, do not occur in the laser-cladded Ni-Ag/TiC composite coating and 45 steel substrate, and they present good metallurgical bonding between them. Compared with Ni/TiC composite coating, micro- hardness values of the two coatings do not present evident differences. The wear experiment result shows that Ni-Ag/TiC composite coated with Ag possesses low friction coefficient and good wear resistance compared with Ni/TiC composite coating.展开更多
WC7Co/Ti6Al4V composite coatings are deposited on the pure Ti substrate by pulse laser cladding(LC).During the laser melting process,the decomposition of WC7Co particles will lead to the evolution of microstructure an...WC7Co/Ti6Al4V composite coatings are deposited on the pure Ti substrate by pulse laser cladding(LC).During the laser melting process,the decomposition of WC7Co particles will lead to the evolution of microstructure and phases,which is directly related to the wear resistance and mechanism of composite coating.The microstructural evolution,phase compositions and interface reaction of WC7Co/Ti6Al4V composite coating were examined by scanning electron microscopy,energydispersive spectrum and X-ray diffraction(XRD).The hardness of different structures and abrasive resistance of composite coating were measured.The results show that the typical microstructure of LC WC7Co/Ti6Al4V composite coating can be classified into dissolved WC7Co composite structure and un-dissolved WC7Co structure.According to XRD results,there are Ti solid solution,W,TiC,VC,Co3W3C and secondary W2C in composite coating.The eutectic structure formed by the dissolved WC7Co particles consisted of W,W2C,TiC and P-Ti solid solution.The mean hardness of different structures exhibits a significant gradient distribution in composite coating.A reaction layer composed of TiC,W and W2C is also generated onto the interface between un-dissolved WC7Co particles and Ti6Al4V alloy matrix.The abrasive mechanisms of WC7Co/Ti6Al4V composite coating are mainly adhesive wear and oxidation wear during the dry sliding process.展开更多
文摘The microstructure,microhardness,and corrosion resistance of laser cladding Ni−WC coating on the surface of AlSi5Cu1Mg alloy were investigated by scanning electron microscopy,X-ray diffraction,microhardness testing,immersion corrosion testing,and electrochemical measurement.The results show that a smooth coating containing NiAl,Ni_(3)Al,M_(7)C_(3),M_(23)C_(6)phases(M=Ni,Al,Cr,W,Fe)and WC particles is prepared by laser cladding.Under a laser scanning speed of 120 mm/min,the microhardness of the cladding coating is 9−11 times that of AlSi5Cu1Mg,due to the synergistic effect of excellent metallurgical bond and newly formed carbides.The Ni−WC coating shows higher corrosion potential(−318.09 mV)and lower corrosion current density(12.33μA/cm^(2))compared with the matrix.The crack-free,dense cladding coating obviously inhibits the penetration of Cl^(−)and H^(+),leading to the remarkedly improved corrosion resistance of cladding coating.
基金Funded by the Natural Science Foundation of Zhejiang Province(LY12E02003)the National Natural Science Foundation of China(No.51204064)the Training Program of the Major Research Plan of the National Natural Science Foundation of China(No.91023030)
文摘Ni-Ag/TiC composite coating was prepared on the 45 steel substrates by means of laser cladding. Microstructure and wear properties of composite coatings were analyzed using optical microscopy, field emission scanning electron microscopy and wear machine. The experimental results show that defects, such as cracks and pores, do not occur in the laser-cladded Ni-Ag/TiC composite coating and 45 steel substrate, and they present good metallurgical bonding between them. Compared with Ni/TiC composite coating, micro- hardness values of the two coatings do not present evident differences. The wear experiment result shows that Ni-Ag/TiC composite coated with Ag possesses low friction coefficient and good wear resistance compared with Ni/TiC composite coating.
基金National Natural Science Foundation of China(51701165)the Natural Science Foundation of Shaanxi Province(2018JM5005)+1 种基金Postdoctoral Science Foundation of China(2017M623334XB)Shaanxi Province Postdoctoral Science Foundation(2018BSHQYXMZZ36).
文摘WC7Co/Ti6Al4V composite coatings are deposited on the pure Ti substrate by pulse laser cladding(LC).During the laser melting process,the decomposition of WC7Co particles will lead to the evolution of microstructure and phases,which is directly related to the wear resistance and mechanism of composite coating.The microstructural evolution,phase compositions and interface reaction of WC7Co/Ti6Al4V composite coating were examined by scanning electron microscopy,energydispersive spectrum and X-ray diffraction(XRD).The hardness of different structures and abrasive resistance of composite coating were measured.The results show that the typical microstructure of LC WC7Co/Ti6Al4V composite coating can be classified into dissolved WC7Co composite structure and un-dissolved WC7Co structure.According to XRD results,there are Ti solid solution,W,TiC,VC,Co3W3C and secondary W2C in composite coating.The eutectic structure formed by the dissolved WC7Co particles consisted of W,W2C,TiC and P-Ti solid solution.The mean hardness of different structures exhibits a significant gradient distribution in composite coating.A reaction layer composed of TiC,W and W2C is also generated onto the interface between un-dissolved WC7Co particles and Ti6Al4V alloy matrix.The abrasive mechanisms of WC7Co/Ti6Al4V composite coating are mainly adhesive wear and oxidation wear during the dry sliding process.