The oxidation behavior of sputtered Ni-3Cr-20Al coating at 900℃ in air was investigated. A dense Al2O3 layer was formed on the sputtered Ni-3Cr-20AI coating after 200 h oxidation. However, owing to the segregation of...The oxidation behavior of sputtered Ni-3Cr-20Al coating at 900℃ in air was investigated. A dense Al2O3 layer was formed on the sputtered Ni-3Cr-20AI coating after 200 h oxidation. However, owing to the segregation of Ni3Al during oxidation process at high temperature, the spinel NiAI2O4 was also formed in the Al2O3 layer. It was found that the formation of NiAI204 had no detrimental effect on the oxidation resistance of the sputtered N?3O-20AI coating due to the excellent adhesion shown by the Al2O3 and NiAl2O4complex oxide scale.展开更多
The oxidation kinetics,surface morphology and phase structure of oxide films grown on 25Cr20Ni alloy in air-H2O and H2-H2O atmospheres at 900 ℃ for 20 h were investigated.The anti-coking performance and resistance to...The oxidation kinetics,surface morphology and phase structure of oxide films grown on 25Cr20Ni alloy in air-H2O and H2-H2O atmospheres at 900 ℃ for 20 h were investigated.The anti-coking performance and resistance to carburization of the two oxide films were compared using 25Cr20Ni alloy tubes with an inner diameter of 10 mm and a length of 850 mm in a bench scale naphtha steam pyrolysis unit.The oxidation kinetics followed a parabolic law in an air-H2O atmosphere and a logarithm law in a H2-H2O atmosphere in the steady-state stage.The oxide film grown in the air-H2O atmosphere had cracks where the elements Fe and Ni were enriched and the un-cracked area was covered with octahedral-shaped MnCr2O4 spinels and Cr1.3Fe0.7O3 oxide clusters,while the oxide film grown in the H2-H2O atmosphere was intact and completely covered with dense standing blade MnCr2O4 spinels.In the pyrolysis tests,the anti-coking performance and resistance to carburization of the oxide film grown in the H2-H2O atmosphere were far better than that in the air-H2O atmosphere.The mass of coke formed in the oxide film grown in the H2-H2O atmosphere was less than 10％ of that in the air-H2O atmosphere.The Cr1.3Fe0.7O3 oxide clusters converted into Cr23C6 carbides and the cracks were filled with carbon in the oxide film grown in the air-H2O atmosphere after repeated coking and decoking tests,while the dense standing blade MnCr2O4 spinels remained unchanged in the oxide film grown in the H2-H2O atmosphere.The ethylene,propylene and butadiene yields in the pyrolysis tests were almost the same for the two oxide films.展开更多
Cold closed-die forging is a suitable process to produce spur-bevel gears due to its advantages, such as saving materials and time, reducing costs, increasing die life and improving the quality of the product. The hom...Cold closed-die forging is a suitable process to produce spur-bevel gears due to its advantages, such as saving materials and time, reducing costs, increasing die life and improving the quality of the product. The homogeneity of microstructure of cold closed-die forged gears can highly affect their service performance. The homogeneity of microstructure and Vickers hardness in cold closed-die forged gear of 20 Cr Mn Ti alloy is comprehensively studied by using optical microscopy and Vickers hardness tester. The results show that the distribution homogeneity of the aspect ratio of grain and Vickers hardness is the same. In the circumferential direction of the gear tooth, the distribution of the aspect ratio of grain and Vickers hardness is inhomogeneous and they gradually decrease from the surface to the center of the tooth. In the radial direction, the distribution of the aspect ratio of grain and Vickers hardness is inhomogeneous on the surface of the gear tooth; while it is relatively homogeneous in the center of the gear tooth. In the axial direction of the gear tooth, the distribution of the aspect ratio of grain and Vickers hardness is relatively homogeneous from the small-end to the large-end of the gear tooth.展开更多
The effects of aging temperature on shape memory effect, mechanical properties and microstruc-ture of Fe-14Mn-5Si-8Cr-4Ni-0.2C shape memory alloy have been studied. The results showed that the second phase particles r...The effects of aging temperature on shape memory effect, mechanical properties and microstruc-ture of Fe-14Mn-5Si-8Cr-4Ni-0.2C shape memory alloy have been studied. The results showed that the second phase particles rich in chromium, manganese and silicon precipitate during aging, and thereby increase the hardness and strength of the alloy. The shape recovery ratio can be remarkably improved by aging and a maximum value can be obtained at 1223 K, which is 68% higher than that of the specimen in solid solution state. When the aging temperature is below 1223 K, the amount of second phase particles increases as the aging temperature increases. The size of austenite grain increases with increasing aging temperature. When the temperature is over 1223 K, the second phase particles can not precipitate. The lack of second phase particles and the increase of grain size make the hardness and shape recovery ratio drastically decrease, when the temperature is over 1223 K.展开更多
By investigating the thermal expansion properties of three quasicrystalline alloys Al 65 Cu 20 Cr 15 quenched, Al 65 Cu 20 Cr 15 cast and Al 65 Cu 20 Fe 15 cast particles reinforced Al matrix composites from 25 ℃ to ...By investigating the thermal expansion properties of three quasicrystalline alloys Al 65 Cu 20 Cr 15 quenched, Al 65 Cu 20 Cr 15 cast and Al 65 Cu 20 Fe 15 cast particles reinforced Al matrix composites from 25 ℃ to 500 ℃, the thermal expansion coefficients of three quasicrystalline alloys were theoretically estimated. The results show that the thermal expansion coefficients of the composites are much lower than that of pure Al, and the thermal expansion coefficients of the composites reinforced by Al Cu Cr quasicrystalline particles are lower than those of the composites reinforced by Al Cu Fe quasicrystalline particles. According to estimating, quasicrystalline alloys have negative thermal expansion coefficients, and the thermal expansion coefficients of Al Cu Cr quasicrystalline alloys are lower than those of Al Cu Fe quasicrystalline alloys. In the alloys, the more the qusicrystalline content, the lower the thermal expansion coefficient.展开更多
Ti-47Al-2Nb-2Cr-0.15B(mole fraction,%)alloy was vacuum brazed with amorphous and crystalline Ti.25Zr-12.5Cu-12.5Ni-3.0Co-2.0Mo(mass fraction,%)filler alloys,and the melting,spreading and gap filling behaviors of the a...Ti-47Al-2Nb-2Cr-0.15B(mole fraction,%)alloy was vacuum brazed with amorphous and crystalline Ti.25Zr-12.5Cu-12.5Ni-3.0Co-2.0Mo(mass fraction,%)filler alloys,and the melting,spreading and gap filling behaviors of the amorphous and crystalline filler alloys as well as the joints brazed with them were investigated in details.Results showed that the amorphous filler alloy possessed narrower melting temperature interval,lower liquidus temperature and melting active energy compared with the crystalline filler alloy,and it also exhibited better brazeability on the surface of the Ti.47Al.2Nb.2Cr.0.15B alloy.The TiAl joints brazed with crystalline and amorphous filler alloys were composed of two interfacial reaction layers and a central brazed layer.Under the same conditions,the tensile strength of the joint brazed with the amorphous filler alloy was always higher than that with the crystalline filler alloy.The maxmium tensile strength of the joint brazed at 1273 K with the amorphous filler alloy reached 254 MPa.展开更多
Applicability of the following creep constitutive equations was investigated for normal type creep curves of Ni-18.5Cr alloy and tertiary creep dominant curves of Ni-18.5Cr16W alloy under constant load: the θ project...Applicability of the following creep constitutive equations was investigated for normal type creep curves of Ni-18.5Cr alloy and tertiary creep dominant curves of Ni-18.5Cr16W alloy under constant load: the θ projection method describing a creep curse by a sum of two exponential terms, modified θ method describing a primary creep stage by an exponential term and a tertiary creep stage by a logarithmic term, modified Ω method describing a creep curve by a sum of two logarithmic term, 2θ method with only a tertiary creep component and Ω method. The θ, modified θ and modified Ω methods can describe normal type and tertiary creep dominant curves. Tertiary creep dominant curves of Ni-18.5Cr-16W alloy at 900℃ are also described using 2θ and Ω methods. Applicability of the modified θ and modified Ω methods is superior for constant load creep curves because they can predict creep curves up to rupture and rupture life accurately and conservatively.展开更多
基金National Natural Science Foundation of China !under grant 59671060
文摘The oxidation behavior of sputtered Ni-3Cr-20Al coating at 900℃ in air was investigated. A dense Al2O3 layer was formed on the sputtered Ni-3Cr-20AI coating after 200 h oxidation. However, owing to the segregation of Ni3Al during oxidation process at high temperature, the spinel NiAI2O4 was also formed in the Al2O3 layer. It was found that the formation of NiAI204 had no detrimental effect on the oxidation resistance of the sputtered N?3O-20AI coating due to the excellent adhesion shown by the Al2O3 and NiAl2O4complex oxide scale.
基金financially supported by the scientific research project of China Petroleum and Chemical Corporation(No.409075)
文摘The oxidation kinetics,surface morphology and phase structure of oxide films grown on 25Cr20Ni alloy in air-H2O and H2-H2O atmospheres at 900 ℃ for 20 h were investigated.The anti-coking performance and resistance to carburization of the two oxide films were compared using 25Cr20Ni alloy tubes with an inner diameter of 10 mm and a length of 850 mm in a bench scale naphtha steam pyrolysis unit.The oxidation kinetics followed a parabolic law in an air-H2O atmosphere and a logarithm law in a H2-H2O atmosphere in the steady-state stage.The oxide film grown in the air-H2O atmosphere had cracks where the elements Fe and Ni were enriched and the un-cracked area was covered with octahedral-shaped MnCr2O4 spinels and Cr1.3Fe0.7O3 oxide clusters,while the oxide film grown in the H2-H2O atmosphere was intact and completely covered with dense standing blade MnCr2O4 spinels.In the pyrolysis tests,the anti-coking performance and resistance to carburization of the oxide film grown in the H2-H2O atmosphere were far better than that in the air-H2O atmosphere.The mass of coke formed in the oxide film grown in the H2-H2O atmosphere was less than 10％ of that in the air-H2O atmosphere.The Cr1.3Fe0.7O3 oxide clusters converted into Cr23C6 carbides and the cracks were filled with carbon in the oxide film grown in the air-H2O atmosphere after repeated coking and decoking tests,while the dense standing blade MnCr2O4 spinels remained unchanged in the oxide film grown in the H2-H2O atmosphere.The ethylene,propylene and butadiene yields in the pyrolysis tests were almost the same for the two oxide films.
基金Project(51105287)supported by the National Natural Science Foundation of ChinaProject(2013M531750)supported by China Postdoctoral Science Foundation
文摘Cold closed-die forging is a suitable process to produce spur-bevel gears due to its advantages, such as saving materials and time, reducing costs, increasing die life and improving the quality of the product. The homogeneity of microstructure of cold closed-die forged gears can highly affect their service performance. The homogeneity of microstructure and Vickers hardness in cold closed-die forged gear of 20 Cr Mn Ti alloy is comprehensively studied by using optical microscopy and Vickers hardness tester. The results show that the distribution homogeneity of the aspect ratio of grain and Vickers hardness is the same. In the circumferential direction of the gear tooth, the distribution of the aspect ratio of grain and Vickers hardness is inhomogeneous and they gradually decrease from the surface to the center of the tooth. In the radial direction, the distribution of the aspect ratio of grain and Vickers hardness is inhomogeneous on the surface of the gear tooth; while it is relatively homogeneous in the center of the gear tooth. In the axial direction of the gear tooth, the distribution of the aspect ratio of grain and Vickers hardness is relatively homogeneous from the small-end to the large-end of the gear tooth.
文摘The effects of aging temperature on shape memory effect, mechanical properties and microstruc-ture of Fe-14Mn-5Si-8Cr-4Ni-0.2C shape memory alloy have been studied. The results showed that the second phase particles rich in chromium, manganese and silicon precipitate during aging, and thereby increase the hardness and strength of the alloy. The shape recovery ratio can be remarkably improved by aging and a maximum value can be obtained at 1223 K, which is 68% higher than that of the specimen in solid solution state. When the aging temperature is below 1223 K, the amount of second phase particles increases as the aging temperature increases. The size of austenite grain increases with increasing aging temperature. When the temperature is over 1223 K, the second phase particles can not precipitate. The lack of second phase particles and the increase of grain size make the hardness and shape recovery ratio drastically decrease, when the temperature is over 1223 K.
文摘By investigating the thermal expansion properties of three quasicrystalline alloys Al 65 Cu 20 Cr 15 quenched, Al 65 Cu 20 Cr 15 cast and Al 65 Cu 20 Fe 15 cast particles reinforced Al matrix composites from 25 ℃ to 500 ℃, the thermal expansion coefficients of three quasicrystalline alloys were theoretically estimated. The results show that the thermal expansion coefficients of the composites are much lower than that of pure Al, and the thermal expansion coefficients of the composites reinforced by Al Cu Cr quasicrystalline particles are lower than those of the composites reinforced by Al Cu Fe quasicrystalline particles. According to estimating, quasicrystalline alloys have negative thermal expansion coefficients, and the thermal expansion coefficients of Al Cu Cr quasicrystalline alloys are lower than those of Al Cu Fe quasicrystalline alloys. In the alloys, the more the qusicrystalline content, the lower the thermal expansion coefficient.
基金Foundation item:Project(51865012)supported by the National Natural Science Foundation of ChinaProject(2016005)supported by the Open Foundation of National Engineering Research Center of Near-net-shape Forming for Metallic Materials,China+2 种基金Project(GJJ170372)supported by the Science Foundation of Educational Department of Jiangxi Province,ChinaProject(JCKY2016603C003)supported by the GF Basic Research Project,ChinaProject(JPPT125GH038)supported by the Research Project of Special Furnishment and Part,China
文摘Ti-47Al-2Nb-2Cr-0.15B(mole fraction,%)alloy was vacuum brazed with amorphous and crystalline Ti.25Zr-12.5Cu-12.5Ni-3.0Co-2.0Mo(mass fraction,%)filler alloys,and the melting,spreading and gap filling behaviors of the amorphous and crystalline filler alloys as well as the joints brazed with them were investigated in details.Results showed that the amorphous filler alloy possessed narrower melting temperature interval,lower liquidus temperature and melting active energy compared with the crystalline filler alloy,and it also exhibited better brazeability on the surface of the Ti.47Al.2Nb.2Cr.0.15B alloy.The TiAl joints brazed with crystalline and amorphous filler alloys were composed of two interfacial reaction layers and a central brazed layer.Under the same conditions,the tensile strength of the joint brazed with the amorphous filler alloy was always higher than that with the crystalline filler alloy.The maxmium tensile strength of the joint brazed at 1273 K with the amorphous filler alloy reached 254 MPa.
文摘Applicability of the following creep constitutive equations was investigated for normal type creep curves of Ni-18.5Cr alloy and tertiary creep dominant curves of Ni-18.5Cr16W alloy under constant load: the θ projection method describing a creep curse by a sum of two exponential terms, modified θ method describing a primary creep stage by an exponential term and a tertiary creep stage by a logarithmic term, modified Ω method describing a creep curve by a sum of two logarithmic term, 2θ method with only a tertiary creep component and Ω method. The θ, modified θ and modified Ω methods can describe normal type and tertiary creep dominant curves. Tertiary creep dominant curves of Ni-18.5Cr-16W alloy at 900℃ are also described using 2θ and Ω methods. Applicability of the modified θ and modified Ω methods is superior for constant load creep curves because they can predict creep curves up to rupture and rupture life accurately and conservatively.