Ni/Al2O3、Co/Al2O3和Ni-Co/Al2O3催化剂催化乙醇水蒸气重整制氢的性能

利用浸渍法制备Ni/Al2O3、Co/Al2O3、Ni-Co/Al2O3催化剂,考察催化剂对乙醇水蒸气重整反应的催化性能,对催化剂进行x射线衍射(XRD)表征.实验结果表明,Ni/Al2O3催化剂具有较好的低温活性,Co/Al2O3催化剂具有较高的氢气选择性和较低的甲烷选择性,而Ni-Co/Al2O3催化剂表现出良好的催化性能,有较高的低温活性,较高的氢气、二氧化碳选择性,较低的一氧化碳、甲烷选择性,450℃时乙醇转化率达到100%,氢气选择性为79.8%,二氧化碳选择性为91.9%.

碳钢基体机械搅拌-脉冲电沉积Ni-Co/Al2O3复合镀层的研究

采用机械搅拌-脉冲电沉积法在碳钢基体上制备了Ni-Co/Al2O3复合镀层,并研究了占空比对Ni-Co/Al2O3复合镀层的宏观形貌、成分、显微硬度及耐蚀性的影响。结果表明:随着占空比的提高,Ni-Co/Al2O3复合镀层的宏观形貌先趋好后变差,Ni元素和Co元素的质量分数有所降低,Al元素的质量分数先升高后降低,显微硬度先增大后减小,腐蚀失重先降低后升高;当占空比为40%时,Ni-Co/Al2O3复合镀层的宏观形貌最优,显微硬度达到最大值4 437 MPa,腐蚀失重最低。

Ni-Co/Al_2O_3催化乙醇水蒸气重整制氢性能研究

利用浸渍法制备Ni-Co/Al2O3催化剂,考察催化剂组成、反应温度、水醇比、液体空速对乙醇水蒸气重整反应的影响。结果表明,Ni-Co/Al2O3催化剂中Co含量的增加会提高氢气和一氧化碳的选择性,降低甲烷和二氧化碳的选择性,催化剂Ni7.5Co7.5催化性能最佳,450℃时乙醇转化率达到100%,氢气选择性为79.78%,二氧化碳选择性为91.89%。反应温度会影响乙醇水蒸气重整制氢反应中相关反应的权重和产物的分布。加大水醇比降低一氧化碳选择性,提高二氧化碳选择性;提高液体空速,加大一氧化碳选择性。Ni-Co/Al2O3催化剂反应前后发生明显的物相重构,Co3O4被还原成Co,Co与Ni共同起活性作用,Co3O4作为催化剂前体在乙醇水蒸气重整中显示出良好的活性。

Al_2O_3对电沉积Ni-Co/Al_2O_3复合镀层性能的影响

应用直流复合电沉积技术制备Ni-Co/Al2O3复合镀层,并研究了Al2O3对电沉积Ni-Co/Al2O3复合镀层性能的影响。结果表明:在本试验范围内,镀层的硬度和耐磨性随着Al2O3含量的增加而提高。

占空比对高频脉冲电沉积(Ni-Co)/纳米Al_2O_3复合镀层的影响

采用高频脉冲电沉积法制备(Ni-Co)/纳米Al2O3复合镀层,研究了占空比对复合镀层沉积速率、成分、形貌及表面显微硬度的影响。结果表明:随着占空比由0.3提高至0.5,复合镀层的沉积速率增加,晶粒尺寸变大,表面变粗糙,并且Co含量降低,Ni含量增加,纳米Al2O3颗粒含量变化不明显,Co含量的降低导致硬度降低。

结晶器铜板表面激光熔覆Ni-Co-Al_2O_3复合涂层的微观组织及性能

以Ni-Al2O3纳米复合镀层为中间涂层,在结晶器铜板表面激光熔覆Co42粉末制备Ni-CoAl2O3复合涂层,利用金相显微镜,扫描电镜、显微硬度仪及电化学腐蚀测试系统对涂层的微观组织、硬度及耐蚀性能进行了分析,研究结果表明,Ni-Al2O3纳米复合镀层晶粒细小,微观组织致密、均匀。激光功率为4.5kW,扫描速度为240mm/min时形成的激光熔覆层与基层形成了良好的冶金结合,激光熔覆层晶粒进一步细化,熔覆层的平均显微硬度高达1 000 HV,耐蚀性能优良。

电刷镀n-Al_2O_3/Ni-Co镀层组织与性能的研究

针对镀硬铬中污染环境和危害人体健康的六价铬,为实现清洁生产,改善生态环境,开展了电刷镀n-Al2O3/Ni-Co纳米复合镀层的研究。测试了纳米微粒的质量浓度对n-Al2O3/Ni-Co纳米复合镀层表面形貌和硬度的影响;并对比了n-Al2O3/Ni-Co纳米复合镀层和硬铬镀层的硬度、耐磨性能和抗高温氧化性能;利用XRD测定了n-Al2O3/Ni-Co纳米复合镀层的结构和晶粒尺寸。研究结果表明:纳米微粒的质量浓度为20 g/L时,镀层具有最优的表面形貌和硬度;室温条件下,n-Al2O3/Ni-Co纳米复合镀层的硬度和耐磨性能都明显优于硬铬镀层的;高温条件下,n-Al2O3/Ni-Co纳米复合镀层的抗高温氧化性能与硬铬镀层的相当。

超声波对Ni-Co-Al_2O_3镀层性能的影响

采用超声电沉积法在纯铜表面成功制备出性能良好的Ni-Co-Al2O3复合镀层,并讨论了超声波对镀层性能的影响机理。结果表明,在适当的超声功率下,超声波主要是通过空化效应、射流效应等影响提高镀层的沉积速率、硬度及耐蚀性;当超声功率过高时,超声波无益于提高镀层性能。

负载型非晶合金催化剂Ni-Co-P/γ-Al_2O_3催化硼氢化钠水解制氢

以三氧化二铝(γ-Al2O3)为载体材料,采用化学镀法在基体表面沉积了Ni-Co-P非晶态合金催化剂。采用能量色散X射线谱仪(EDS)、场发射扫描电子显微镜(SEM)、X射线衍射(XRD)、化学吸附仪(BET)等手段对样品的元素组成、形貌和结构进行了表征,用硼氢化钠水解制氢反应考察了Ni-Co-P/γ-Al2O3非晶态合金催化剂的催化性能。结果表明,化学镀Ni-Co-P/γ-Al2O3非晶态合金催化剂具有非常粗糙的表面和很大的比表面积,对催化碱性硼氢化钠溶液水解具有良好的催化活性和循化使用性能。通过对动力学数据研究得到该催化剂的活化能Ea=36.97kJ·mol-1。

负载型非晶合金催化剂Ni-Co-P/γ-Al_2O_3的制备及其结构和催化性能表征

通过化学镀方法在铁片表面镀覆Ni-Co-P非晶合金,探究了镀液成分以及工艺参数对沉积速率、镀液稳定性及镀层质量的影响。选用化学镀Ni-Co-P的最佳优化配方和工艺参数,在氧化铝基体上制备出负载型Ni-Co-P/γ-Al_2O_3非晶合金催化剂。用场发射扫描电子显微镜(FE-SEM)、X射线能量色散谱仪(EDS)、X射线衍射仪(XRD)、电感耦合等离子体(ICP)和氮气吸附脱附测试方法对该催化剂进行表征。硝基苯催化加氢实验考察了Ni-Co-P/γ-Al_2O_3催化剂的催化加氢性能。结果表明,非晶态Ni-Co-P/γ-Al_2O_3催化剂具有良好的催化活性和循环使用性能。

Al_(2)O_(3)在储能材料中的应用研究进展

Al_(2)O_(3)作为陶瓷材料、催化剂、催化剂载体及研磨磨料等有广泛的应用。因氧化铝具有优良的抗酸碱腐蚀性和力学等性能且热稳定性好、来源丰富,所以近年来逐渐开始应用在储能材料领域,进一步拓展了氧化铝的应用范围。主要针对氧化铝包覆后的二次储能电池正极材料、负极材料,以及改进隔膜的力学性能等方面进行研究。报道了近年来氧化铝在锂离子电池、钠离子电池、锂硫电池、电解液、隔膜方面的应用研究进展。

Ni-Co-P-BN（h）-Al2O3二元纳米复合镀层表面组织结构及耐磨性研究

为改善材料表面耐磨性能,采用电沉积法在不同纳米颗粒质量浓度及其混杂配比下制备了Ni-Co-P-BN(h)、Ni-Co-P-Al2O3和Ni-Co-P-BN(h)-Al2O3的3种纳米复合镀层,通过扫描电镜、能谱仪、X射线衍射仪、显微硬度仪、摩擦磨损仪及激光共聚焦显微镜,对镀层的表面组织结构与耐磨性能进行了研究.结果表明:不同纳米颗粒质量浓度及其混杂配比对纳米复合镀层表面组织结构有重要影响,纳米复合镀层表面呈现出典型的包状结构,混杂配比后出现明显纳米Al2O3的衍射峰;与Ni-Co-P-BN(h)和Ni-Co-P-Al2O3镀层相比,Ni-Co-P-BN(h)-Al2O3二元纳米复合镀层的平均显微硬度更大,达到753.6 HV 0.2;摩擦磨损试验中对摩件是直径4 mm的GCr15合金球,在施加载荷3.2N、转速500 r/min、摩擦时间30 min的磨损条件下,二元纳米复合镀层磨损量最小为9.2 mg/h.纳米BN(h)和Al 2O 3在电沉积加工过程中充分发挥了二元纳米粒子协同生长的优势,使得Ni-Co-P-BN(h)-Al2O3二元纳米复合镀层具有更好的耐磨性能.

Modification of Nano-α-Al2O3 and Its Influence on the Surface Properties of Waterborne Polyurethane Resin Composite Passivation Films

Silane coupling agent KH560 was used to modify the surface of nano-α-Al2O3 in ethanol-aqueous solution with different proportions. The particle size of nano-α-Al2O3 was determined by nano-particle size analyzer, and the effects of nano-α-Al2O3 content, ethanol-aqueous solution ratio and KH560 dosage on the dispersion and particle size of nano-α-Al2O3 were investigated. The material structure before and after modification was determined by Fourier transform infrared spectroscopy (FTIR). Aqueous polyurethane resin and inorganic components are combined with modified nano-α-Al2O3 dispersion to form chromium-free passivation solution. The solution is coated on the galvanized sheet, the adhesion and surface hardness are tested, the bonding strength of the coating and the surface hardness of the substrate are discussed. The corrosion resistance and surface morphology of the matrix were investigated by electrochemical test, neutral salt spray test and scanning electron microscope test. The chromium-free passivation film formed after the modification of nano-α-Al2O3 increases the surface hardness of galvanized sheet by about 85%. The corrosion resistance of the film is better than that of a single polyurethane film. The results show that the surface hardness and corrosion resistance of polyurethane resin composite passivation film are significantly improved by the introduction of nano-α-Al2O3.

Ni-Co-P-BN（h）-Al2O3二元纳米复合镀层润湿性及耐蚀性

采用电沉积法在45钢表面制得Ni-Co-P-BN(h)、Ni-Co-P-Al2O3及Ni-Co-P-BN(h)-Al2O3纳米复合镀层。利用SEM、EDS、XRD对镀层的组织、成分及相结构进行了表征和分析,并利用激光共聚焦显微镜、光学接触角测量仪和电化学工作站分别对镀层的表面粗糙度、润湿性及防腐性能进行研究。结果表明:二元纳米颗粒掺杂配比对Ni-Co-P-BN(h)-Al2O3镀层的表面形貌、表面粗糙度及厚度均有影响。与Ni-Co-P-BN(h)和Ni-Co-P-Al2O3镀层相比,在水滴体积为3μL、速度为1μL/s条件下,Ni-Co-P-BN(h)-Al2O3镀层表面静态接触角为133°,镀层表面具有更高的疏水角。电化学试验表明:在5%的NaCl溶液中,Ni-Co-P-BN(h)-Al2O3镀层的最小腐蚀电流密度和腐蚀速率分别为1.0806×10^-6A/cm^2和0.01308mm/a,镀层具有更优的耐蚀性。镀层中共沉积的纳米BN(h)、Al2O3颗粒充分发挥二元纳米粒子的优势,进一步提高了二元纳米复合镀层表面的疏水性和耐蚀性。

磷对Ni(Co)Mo(W)/Al_2O_3加氢处理催化剂的影响研究进展

Ni(Co)Mo(W)/Al2O3催化剂是工业中最常用的加氢处理催化剂。磷作为Ni(Co)Mo(W)/Al2O3加氢处理催化剂中较为常用的添加剂,用于改善催化剂的物理化学性质。本文从磷对Ni(Co)Mo(W)/Al2O3加氢催化剂孔结构、酸性、活性组分分散度等理化性能以及磷对加氢脱硫(HDS)和加氢脱氮(HDN)催化性能两个方面的影响对文献研究结果进行了综述,对磷添加剂的研究结果、存在的分歧以及研究机会进行了分析讨论。

Ce含量对Ni-Ce/Al_2O_3催化剂结构及浆态床CO甲烷化性能的影响

以γ-Al2O3为载体,采用等体积浸渍法制备了不同Ce含量的Ni-Ce/Al2O3催化剂,并考察了其浆态床CO甲烷化反应性能。借助XRD、BET、H2-TPR及CO-TPD等对催化剂进行了表征分析,研究了催化剂的微观结构与甲烷化性能之间的关系。结果表明,助剂Ce的引入能够加强Ni物种与载体之间的相互作用、增强活性组分Ni对CO的吸附能力。随着Ce含量的升高,Ni物种在载体表面的分散度提高、Ni晶粒粒径减小,催化剂的比表面积及与载体相互作用较强的β-NiO相对含量先升后降。催化剂的浆态床甲烷化活性随Ce含量的升高呈现规律性的变化,CO转化率和CH4时空收率先增加后略有下降,当Ce含量为4%(质量分数)时,催化剂甲烷化活性最佳。

激光清洗硅片表面Al_2O_3颗粒的试验和理论分析

以KrF准分子激光器为激光源,对目前工业上常用的硅片研磨抛光液的主要成分Al2O3颗粒进行激光清洗的试验和理论分析。建立一维热传导模型,利用有限元分析软件MSC.MarC模拟硅片表面的温度随激光作用时间和能量密度的分布。通过理论计算,量化了颗粒所受到的清洗力以及其与硅片表面之间的粘附力,理论预测出1μm Al2O3颗粒的激光清洗阈值为60 mJ/cm2。在理论分析的指导下,利用248 nm3、0 ns的KrF准分子激光进行单因素试验,研究激光能量密度、脉冲个数、激光束入射角度对激光干法清洗效率的影响,并且实验验证了清洗模型以及场增强效应对激光清洗结果的影响。

纳米Al_2O_3改性变压器绝缘纸性能的研究

为了研究纳米Al2O3改性绝缘纸的绝缘性能,实验室制备了含不同质量分数的纳米Al2O3绝缘纸手抄片,并对真空浸油后的绝缘纸性能进行了测试。结果表明在一定的质量分数内纳米Al2O3改性后的绝缘纸的工频击穿场强得到较大的提高,在质量分数为1%时,工频击穿场强提高了12.75%,绝缘纸的抗张强度增加了14.13%;在1%的添加量内绝缘纸的介电常数、介电损耗都随纳米Al2O3含量的增加而减小。

TiO_2对Ni/Al_2O_3催化剂CO甲烷化性能的影响

采用溶胶凝胶法制备了一系列不同TiO2含量的TiO2-Al2O3复合载体,并通过浸渍法制备了NiO/TiO2-Al2O3催化剂。分别考察了不同TiO2含量的NiO/TiO2-Al2O3催化剂及反应温度对CO甲烷化催化性能的影响。实验结果表明,当复合载体中TiO2质量分数为30%,反应温度为350～450℃时,催化剂催化活性较高。利用N2吸附-脱附(BET)、X射线衍射(XRD)及H2程序升温还原(H2-TPR)等手段对催化剂物化性能进行了表征。结果表明,加入适量的TiO2能抑制镍铝尖晶石NiAl2O4物种的生成,改善NiO的表面分散性能,避免大晶粒NiO的形成,也改善了催化剂的还原性能,从而提高催化剂的CO甲烷化活性。

Al2O3纳米颗粒对氨水鼓泡吸收过程的强化影响

在试制出了性能稳定的Al2O3纳米流体的基础上,通过定氨气流量和定入口压力两种实验方案,验证了Al2O3纳米颗粒对氨水吸收过程的强化影响,同时找出了引起强化吸收的两个主要影响因素:纳米流体性能的稳定性和吸收器入口与吸收器内气相界面的压力差。在添加十二烷基苯磺酸钠(SDBS)的情况下,可以获得性能稳定而具有强化吸收效果的Al2O3纳米流体,尽管SDBS本身对Al2O3纳米流体强化吸收具有抑制作用。较大的压力差下Al2O3纳米流体在吸收开始阶段就表现出强化吸收效果。随着氨水浓度的增加,氨水对氨气的吸收潜力减小,而Al2O3纳米流体对氨水溶液强化吸收的效果更加明显。对强化现象的可能机理给出了合理解释,为纳米流体对传热传质强化研究提供参考。