Hardness, friction and wear characteristics of electrodeposited RE Ni W P B 4C PTFE composite coatings were studied, and the reason for these fine characteristics was explained in respect of structure. The results sho...Hardness, friction and wear characteristics of electrodeposited RE Ni W P B 4C PTFE composite coatings were studied, and the reason for these fine characteristics was explained in respect of structure. The results show that 1) the structure of RE Ni W P B 4C PTFE composite coatings experiences a transformation process from amorphous to mixture then to crystal as the heat treatment temperature rises; 2) incorporating of B 4C greatly increases the hardness of the coating; 3) the wear resistance of the coating is best with heat treatment for 1?h at 300?℃, which is greatly superior to that of the other traditional coatings.展开更多
Corrosion rate and anode polarization curves of electrodeposited RE-Ni-W-P-SiC-PTFE composite coating in various concentrations of phosphoric and ferric chloride were researched. The results show that corrosion rate o...Corrosion rate and anode polarization curves of electrodeposited RE-Ni-W-P-SiC-PTFE composite coating in various concentrations of phosphoric and ferric chloride were researched. The results show that corrosion rate of the composite coatings increases with the increasing concentrations of phosphoric and ferric chloride, and reaches the maximum value when phosphoric concentration is 40% and ferric chloride concentration is 20% (mass fraction, the same below if not mentioned). Anode polarization curves of the composite coatings show that anode polarization current density of the composite coatings heat-treated at 200 ℃ or 500 ℃ is lower than that of other coatings heat-treated at 300 ℃ or 400 ℃, which displays that the composite coatings heat-treated at 200 ℃ or 500 ℃ have better corrosion resistance. Besides, corrosion resistance of the composite coating heat-treated at 500 ℃ is better than that as deposited and RE-Ni-W-P-SiC composite coating heat-treated at 400 ℃, and is also better than that of 316L stainless steel.展开更多
The components, surface and cross sectional morphologies, and the effects of heat treatment temperature on phase structure, hardness, abrasion resistance and oxidation resistance of pulse electrodeposition RE-Ni-W-B-B...The components, surface and cross sectional morphologies, and the effects of heat treatment temperature on phase structure, hardness, abrasion resistance and oxidation resistance of pulse electrodeposition RE-Ni-W-B-B4C-PTFE composite coatings, were all investigated. The results show that W and B contents increase in the RE-Ni-W-B composite coating by using pulse electrodeposition. RE, PTFE and B4C particles can be co-deposited into the Ni-W-B composite coating, but the amount is very little. X-ray diffraction analysis displays that the RE-Ni-W-B-B4C-PTFE composite coating is mainly amorphous, partially crystallized as-deposited, but it turns into crystalline state and PTFE in the coatings will decompose after the heat treatment temperature is higher than 400℃. The hardness of the composite coating increases with increasing heat treatment temperature, it comes up to the highest value at 400℃. The oxidized film mass of the composite coating increases slowly when the oxidation temperature is lower than 500℃, but it increases linearly and sharply after the oxidation temperature is higher than 600℃.展开更多
A composite hard-anodized coating containing micro PTFE (polytetrafluoroethylene) particles on aluminum alloy 6063 was produced by adding micro PTFE particles into the traditional hardcoat anodizing solution. The size...A composite hard-anodized coating containing micro PTFE (polytetrafluoroethylene) particles on aluminum alloy 6063 was produced by adding micro PTFE particles into the traditional hardcoat anodizing solution. The size of the PTFE particles is around 2 v- m in diameter and the content of the PTFE particles in the composite coating is within 2%-3% by area percentage. Thickness of the composite coating can reach up to 70 v m after one hour’s anodizing. Surface hardness of the composite coating is between 400-480 HVo.i- The average friction coefficient of the composite coating against steel under dry friction test is 0.11, which is 17% lower than that obtained by traditional hardcoat anodizing.展开更多
研究了RE Ni W P SiC PTFE复合镀层的抗氧化性。结果表明 :RE Ni W P SiC PTFE复合镀层随着氧化温度的升高 ,氧化膜的重量增加 ,但在 80 0°C以下氧化温度对镀层的增重不显著 ;80 0°C以上 ,镀层的增重迅速增加。通过对三种镀...研究了RE Ni W P SiC PTFE复合镀层的抗氧化性。结果表明 :RE Ni W P SiC PTFE复合镀层随着氧化温度的升高 ,氧化膜的重量增加 ,但在 80 0°C以下氧化温度对镀层的增重不显著 ;80 0°C以上 ,镀层的增重迅速增加。通过对三种镀层抗氧化性能的比较可知 ,RE Ni W P SiC PTFE镀层的抗氧化性不如Ni W P、Ni W P SiC及RE Ni W P SiC三种镀层好。展开更多
文摘Hardness, friction and wear characteristics of electrodeposited RE Ni W P B 4C PTFE composite coatings were studied, and the reason for these fine characteristics was explained in respect of structure. The results show that 1) the structure of RE Ni W P B 4C PTFE composite coatings experiences a transformation process from amorphous to mixture then to crystal as the heat treatment temperature rises; 2) incorporating of B 4C greatly increases the hardness of the coating; 3) the wear resistance of the coating is best with heat treatment for 1?h at 300?℃, which is greatly superior to that of the other traditional coatings.
基金Project([2002]24) supported by the National Development and Reform Commission of China
文摘Corrosion rate and anode polarization curves of electrodeposited RE-Ni-W-P-SiC-PTFE composite coating in various concentrations of phosphoric and ferric chloride were researched. The results show that corrosion rate of the composite coatings increases with the increasing concentrations of phosphoric and ferric chloride, and reaches the maximum value when phosphoric concentration is 40% and ferric chloride concentration is 20% (mass fraction, the same below if not mentioned). Anode polarization curves of the composite coatings show that anode polarization current density of the composite coatings heat-treated at 200 ℃ or 500 ℃ is lower than that of other coatings heat-treated at 300 ℃ or 400 ℃, which displays that the composite coatings heat-treated at 200 ℃ or 500 ℃ have better corrosion resistance. Besides, corrosion resistance of the composite coating heat-treated at 500 ℃ is better than that as deposited and RE-Ni-W-P-SiC composite coating heat-treated at 400 ℃, and is also better than that of 316L stainless steel.
文摘The components, surface and cross sectional morphologies, and the effects of heat treatment temperature on phase structure, hardness, abrasion resistance and oxidation resistance of pulse electrodeposition RE-Ni-W-B-B4C-PTFE composite coatings, were all investigated. The results show that W and B contents increase in the RE-Ni-W-B composite coating by using pulse electrodeposition. RE, PTFE and B4C particles can be co-deposited into the Ni-W-B composite coating, but the amount is very little. X-ray diffraction analysis displays that the RE-Ni-W-B-B4C-PTFE composite coating is mainly amorphous, partially crystallized as-deposited, but it turns into crystalline state and PTFE in the coatings will decompose after the heat treatment temperature is higher than 400℃. The hardness of the composite coating increases with increasing heat treatment temperature, it comes up to the highest value at 400℃. The oxidized film mass of the composite coating increases slowly when the oxidation temperature is lower than 500℃, but it increases linearly and sharply after the oxidation temperature is higher than 600℃.
文摘A composite hard-anodized coating containing micro PTFE (polytetrafluoroethylene) particles on aluminum alloy 6063 was produced by adding micro PTFE particles into the traditional hardcoat anodizing solution. The size of the PTFE particles is around 2 v- m in diameter and the content of the PTFE particles in the composite coating is within 2%-3% by area percentage. Thickness of the composite coating can reach up to 70 v m after one hour’s anodizing. Surface hardness of the composite coating is between 400-480 HVo.i- The average friction coefficient of the composite coating against steel under dry friction test is 0.11, which is 17% lower than that obtained by traditional hardcoat anodizing.
文摘研究了RE Ni W P SiC PTFE复合镀层的抗氧化性。结果表明 :RE Ni W P SiC PTFE复合镀层随着氧化温度的升高 ,氧化膜的重量增加 ,但在 80 0°C以下氧化温度对镀层的增重不显著 ;80 0°C以上 ,镀层的增重迅速增加。通过对三种镀层抗氧化性能的比较可知 ,RE Ni W P SiC PTFE镀层的抗氧化性不如Ni W P、Ni W P SiC及RE Ni W P SiC三种镀层好。