The coarsening behavior ofγʹprecipitate phase at different temperatures and the compressive performance of novel Co-Ni-Al-W superalloy were investigated.Experiment results show that the evolution of the mean radius a...The coarsening behavior ofγʹprecipitate phase at different temperatures and the compressive performance of novel Co-Ni-Al-W superalloy were investigated.Experiment results show that the evolution of the mean radius and volume fraction of theγʹphase obeys the classical Lifshitz-Slyozov-Wagner model.The coarsening rate of theγʹphase exhibits a significant dependence on the aging temperature,which increases from 1.30×10^(−27)m^(3)/s at 800℃to 9.56×10−27 m^(3)/s at 900℃.The activation energy ofγʹphase is mainly influenced by the W diffusion in theγmatrix,presenting as 210 kJ/mol.The prepared Co-Ni-Al-W alloy possesses superb comprehensive properties,particularly the good combination of highγʹsolvus temperature(1221℃)and low density(8.7 g/cm^(3)).Besides,the compressive yield strength of the Co-Ni-Al-W alloy at ambient and high temperatures are higher than that of otherγʹ-strengthened Co-based superalloys.The compressive yield strength of the Co-Ni-Al-W alloy at 850℃is as high as 774 MPa.展开更多
基金Natural Science Foundation of Liaoning Province(2023-MSLH-337)。
文摘The coarsening behavior ofγʹprecipitate phase at different temperatures and the compressive performance of novel Co-Ni-Al-W superalloy were investigated.Experiment results show that the evolution of the mean radius and volume fraction of theγʹphase obeys the classical Lifshitz-Slyozov-Wagner model.The coarsening rate of theγʹphase exhibits a significant dependence on the aging temperature,which increases from 1.30×10^(−27)m^(3)/s at 800℃to 9.56×10−27 m^(3)/s at 900℃.The activation energy ofγʹphase is mainly influenced by the W diffusion in theγmatrix,presenting as 210 kJ/mol.The prepared Co-Ni-Al-W alloy possesses superb comprehensive properties,particularly the good combination of highγʹsolvus temperature(1221℃)and low density(8.7 g/cm^(3)).Besides,the compressive yield strength of the Co-Ni-Al-W alloy at ambient and high temperatures are higher than that of otherγʹ-strengthened Co-based superalloys.The compressive yield strength of the Co-Ni-Al-W alloy at 850℃is as high as 774 MPa.