Titanium alloy (Ti-Al-V alloy) substrate was brazed with stainless steel (STS304) using filler metal.At an optimized brazing condition,various filler metals were used.Microstructures were observed at each condition.Fi...Titanium alloy (Ti-Al-V alloy) substrate was brazed with stainless steel (STS304) using filler metal.At an optimized brazing condition,various filler metals were used.Microstructures were observed at each condition.Filler metals were titanium based 40Ti-20Zr-20Cu-20Ni,silver based Ag 5Pd,and nickel based Ni-7Cr-3.1B-4.5Si-3Fe-0.06C (BNi2) and Ni-14Cr-10P-0.06C (BNi7).To select a good filler metal for brazing process,wetting test was performed at 880-1050 °C.It was not brazed using silver based filler metals,but at the conditions using titanium and nickel based filler metals had brazed zone between titanium alloy and stainless steel.However,titanium alloy was eroded during brazing using titanium based filler metals.Nickel based filler metal has a good brazed zone between titanium alloy and stainless steel among the filler metals.展开更多
Laser welding with filler wire of AZ31 magnesium alloys is investigated using a CO2 laser experimental system. The effect of three different filler wires on the joint properties is researched. The results show that th...Laser welding with filler wire of AZ31 magnesium alloys is investigated using a CO2 laser experimental system. The effect of three different filler wires on the joint properties is researched. The results show that the weld appearance can be effectively improved when using laser welding with filler wire. The microhardness and tensile strength of joints are almost the same us those of the base metal when ER AZ31 or ER AZ61 wire is adopted. However, when the filler wire of ER 5356 aluminum alloy is used, the mechanical properties of flints become worse. For ER AZ31 and ER AZ61 filler wires, the microstructure of weld zone slws small dendrite grains. In comparison, for ER 5356 filler wire, the weld shows a structure of snowy dendrites and many intermetallic compounds and eutectic phases distribute in the dendrites. These intermetallic constituents with low melting point increase the tendency of hot crack and result in fiagile joint properties. Therefore, ER AZ31 and ER AZ61 wire are more suitable filler material than ER 5356 for CO2 laser welding of AZ31 magnesium alloys.展开更多
Al-6.5Si-42Zn and Al-6.5Si-42Zn-0.09Sr filler metals were used for brazing 6061 aluminum alloy. Air cooling and water cooling were applied after brazing. Si phase morphologies in the brazing alloy and the brazed joint...Al-6.5Si-42Zn and Al-6.5Si-42Zn-0.09Sr filler metals were used for brazing 6061 aluminum alloy. Air cooling and water cooling were applied after brazing. Si phase morphologies in the brazing alloy and the brazed joints were investigated. It was found that zinc in the Al-Si filler metals could reduce the formation of eutectic Al-Si phase and lower the brazing temperature at about 520℃. Adding 0.09wt% Sr element into the Al-6.5Si-42Zn alloy caused a-Al phase refinement and transformed acicular Si phase into the finely fiber-like. After water cooling, Zn element dissolved into the Al-Si eutectic area, and η-Zn phase disappeared in the brazed joints. Tensile strength testing results showed that the Sr-modified filler metal could enhance the strength of the brazed joints by 13% than Al-12Si, while water-cooling further improved the strength at 144 MPa.展开更多
The density of liquid Ni-Cr alloy was measured by a modified sessile drop method. The density of liquid Ni-Cr alloywas found to decrease with increasing temperature and Cr concentration in the alloy. The molar volume ...The density of liquid Ni-Cr alloy was measured by a modified sessile drop method. The density of liquid Ni-Cr alloywas found to decrease with increasing temperature and Cr concentration in the alloy. The molar volume of liquidNi-Cr alloy increases with increasing the Cr concentration in the alloy. The molar volume of Ni-Cr alloy determinedin the present work shows a positive deviation from the linear molar volume.展开更多
Si/SiC ceramic composite and lnvar alloy were successfidly joined by vacuum brazing using Ti5OCu-W filler metals into which W was added to release the thermal stress of the brazed joint. Microstructures of the brazed ...Si/SiC ceramic composite and lnvar alloy were successfidly joined by vacuum brazing using Ti5OCu-W filler metals into which W was added to release the thermal stress of the brazed joint. Microstructures of the brazed joints were irwestigated by scanning electron micrascope （SEM） and energy dispersive spectrometer （EDS）. The mechanical properties of the brazed joints were measured by shearing tests. The results showed that the brazed joints were composed of Ti-Cu phase, W phase and Ti-Si phase. W had no effect on the wettability and mobility of the .filler metals. The growth of Ti2 Cu phase was restrained, and the reaction between ceramic composite and filler metals was weakened. The specimen, brazed at 970°C for 5 rain, had the maximum shear strength of 108 MPa at room temperature.展开更多
CO2 laser welding aluminum alloy with filler wire was studied. The results indicate that the problems in CO2 laser welding of Al alloy, such as bad appearance of weld, easily excessive penetration and low strength, ca...CO2 laser welding aluminum alloy with filler wire was studied. The results indicate that the problems in CO2 laser welding of Al alloy, such as bad appearance of weld, easily excessive penetration and low strength, can be improved effectively by using laser welding with filler wire, and the maximum tensile strength of weld can reach 94% for the base metal. It also can be found that, the linear energy have great influence on the microstructure and mechanical properties of the joint. As the heat input increases, the cellular fir-tree crystals in the weld zone become sparse and the form of tensile fracture transforms from gliding fracture to brittle fracture.展开更多
Si3N4 ceramic was jointed to itself using a filler alloy of Cu-Zn-Ti by the reaction between Ti and Si3N4. The microstructure of the interface in the joint is found to be Si3N4 ceramic/TiN reaction layer/Ti5Si3 reacti...Si3N4 ceramic was jointed to itself using a filler alloy of Cu-Zn-Ti by the reaction between Ti and Si3N4. The microstructure of the interface in the joint is found to be Si3N4 ceramic/TiN reaction layer/Ti5Si3 reaction layer. The grain size of the TiN and Ti5Si3 reaction layer is 0.1μm and 1-2μm, respectively. There is no crystal orientation relationship between TiN reaction layer and Si3N4 ceramic or Ti5Si3 reaction layer. The kinetic equation for calculating the thickness of the reaction layer was obtained. When a （CuZn）85Ti15 alloy is used as the filler alloy, the apparent activation energy of the growth of the reaction layer is 201.69kJ/mol.展开更多
Ti-based filler metals made by transient solidification and normal crystallization were selected for the vacuum brazing of the TiAl alloy and 42CrMo under different processing parameters. The results show that the ten...Ti-based filler metals made by transient solidification and normal crystallization were selected for the vacuum brazing of the TiAl alloy and 42CrMo under different processing parameters. The results show that the tensile strength of the joint of transient solidified filler metal is higher than that of normal crystallized filler metal under the same processing parameters. By the analysis of scanning electron microscope（SEM） and X-ray diffracting （XRD） , it is found that the higher strength maybe caused by the generating of TiAl , TiNi and TiCu at the interface of joint made by transient solidified filler metal.展开更多
The effects of the addition of rare earths on the properties of Ti-Zr-Cu-Ni base brazing filler alloys and the mechanical microstructure and properties were studied for the brazed-joints in the vacuum brazing of TC4 b...The effects of the addition of rare earths on the properties of Ti-Zr-Cu-Ni base brazing filler alloys and the mechanical microstructure and properties were studied for the brazed-joints in the vacuum brazing of TC4 by comparing synthetical properties of two kinds of filler metals.The results indicate that the filler metals added with rare earths have lower melting point, better wettability and higher mechanical properties in the brazing joints.展开更多
The aluminide coating process of Ti-6Al-4V alloys with different fillers(100wt.% Al_2O_3,50wt% Y_2O_3+50wt.% Al_2O_3 and 100wt.% Y_2O_3) for improvement of the oxidation resistance were investigated.The results show t...The aluminide coating process of Ti-6Al-4V alloys with different fillers(100wt.% Al_2O_3,50wt% Y_2O_3+50wt.% Al_2O_3 and 100wt.% Y_2O_3) for improvement of the oxidation resistance were investigated.The results show that the filler does not only participate in the aluminizing process,but also has much effect on the coating composition.The XRD analysis reveals that the aluminide coating with filler Al_2O_3 is predominant with TiAl_3 and TiAl phases;while the aluminide coatings with filler Y_2O_3+Al_2O_3 are predominant with Ti_3Al phase.The oxidation kinetics shows that different fillers affect greatly the oxidation resistance of aluminide coating,and the oxidation resistance of aluminized specimens with pack aluminizing filler Al_2O_3 are about 5-8 times than that of the aluminized specimens with other pack aluminizing fillers.展开更多
It＇ s well known welding takes the leading role in development of titanium structures. However, in number of cases technological processes of brazing are more appropriate and, sometimes, being the single possible, in...It＇ s well known welding takes the leading role in development of titanium structures. However, in number of cases technological processes of brazing are more appropriate and, sometimes, being the single possible, in particular, during production of multilayer thin-wall structures. It should be noted that brazing filler metals of Ti-Cu-Ni, Ti-Zr-Cu-Ni, Zr-Ti-Ni and Cu-Zr-Ti systems in a form of plastic foils, as well as in powder form are mainly used in world practice for brazing of titanium alloys. Present work provides the results of complex investigations of brazing filler metals of Ti-Zr-Fe, Ti-Zr-Mn and Ti-Zr-Co systems using differential thermal analysis, light and scanning microscopy, X-ray microspectrum analysis. Data on melting ranges of pilot alloys were obtained, and liquidas su^Caces of given systems using simplex-lattice method were build. Brazing filler metals covering brazing temperature range of current structural titanium materials based on solid solutions as well as intermetallics were proposed. Structure, chemical inhomogeniety and strength characteristics of brazed joints were studied. It is determined that brazing of solid solution based alloys （OT4, VT6 ） using indicated brazing fiUer metals ensures strength characteristics of joints, which are not inferior to that obtained with application of known brazing filler metals even if they are received at lower brazing temperature.展开更多
A high Fe containing aluminum matrix filler metal for hardfacing aluminum silicon alloys has been developed by using iron,nickel,and silicon as the major strengthening elements,and by measuring mechanical properties...A high Fe containing aluminum matrix filler metal for hardfacing aluminum silicon alloys has been developed by using iron,nickel,and silicon as the major strengthening elements,and by measuring mechanical properties,room temperature and high temperature wear tests,and microstructural analysis.The filler metal,which contains 3.0%-5.0% Fe and 11.0%-13.0% Si,exhibits an excellent weldability.The as cast and as welded microstructures for the filler metal are of uniformly distribution and its dispersed network of hard phase is enriched with Al Si Fe Ni.The filler metal shows high mechanical properties and wear resistance at both room temperature and high temperatures.The deposited metal has a better resistance to impact wear at 220℃ than that of substrate Al Si Mg Cu piston alloy;at room temperature,the deposited metal has an equivalent resistance to slide wear with lubrication as that of a hyper eutectic aluminum silicon alloy with 27% Si and 1% Ni.展开更多
Si3N4 ceramic was jointed to itself using a filler alloy of Cu76.5Pd8.5Ti15, and the mechanical properties of the jointwere measured and analyzed. By using a filler alloy of Cu76.5Pd8.5Ti15, the SisN4/SisN4 joints wer...Si3N4 ceramic was jointed to itself using a filler alloy of Cu76.5Pd8.5Ti15, and the mechanical properties of the jointwere measured and analyzed. By using a filler alloy of Cu76.5Pd8.5Ti15, the SisN4/SisN4 joints were obtained bybrazing at 1373～1473 K for 0.9～5.4 ks under a pressure of 2×10-3 MPa. The effect of brazing parameters on theshear strength of the joint was investigated. When the brazing temperature and holding time is 1423 K and 5.4 ksrespectively, the maximum shear strength of the Si3N4/Si3N4 joint is obtained to be 198 MPa.展开更多
The density of Ni-Cr alloy in the mushy state has been measured using the modified sessile drop method. The density of Ni-Cr alloy in the mushy state was found to decrease with increasing temperature and Cr concentrat...The density of Ni-Cr alloy in the mushy state has been measured using the modified sessile drop method. The density of Ni-Cr alloy in the mushy state was found to decrease with increasing temperature and Cr concentration in alloy. The molar volume of Ni-Cr alloy in the mushy state therefore increases with increasing the Cr concentration in alloy. The ratio of the difference of density divided by the temperature difference between liquidus and solidus temperatures decreases with increasing Cr concentration. The density of the alloy increased with the precipitation of a solid phase in alloy during the solidification process. The temperature dependence of the density of alloy in the mushy state was not linear but biquadratic.展开更多
The purpose of this research was to study the effect of Argon inert gas on the laser welding quality of Co-Cr and Ni-Cr base metal alloys, which are widely used as Fixed Prosthodontics alloys in Dental Laboratories. A...The purpose of this research was to study the effect of Argon inert gas on the laser welding quality of Co-Cr and Ni-Cr base metal alloys, which are widely used as Fixed Prosthodontics alloys in Dental Laboratories. A total of 36 specimens were manufactured (18 of Ni-Cr alloy and 18 of Co-Cr alloy). The specimens were then divided into 3 subgroups (6 specimens each): control;argon-welded;and non-Argon welded. The specimens were cut, laser welded, radiographed and finally tested under tensile strength testing, followed by examination using Scanning Electron Microscopy. The tensile strength of welded specimens was lower than the strength of non-welded specimens, however this difference was not found to be statistically significant. The material factor (Co-Cr alloy or Ni-Cr alloy) has a statistically significant effect on the tensile strength, while the presence or not of the inert gas, as well as the combination of the two factors do not have a statistically significant effect. The laser welding process applied in daily practice (separation of specimen, formation of two cones in contact, aggregation of two cones, filling of the remaining gap by welding) is considered satisfactory in terms of weld strength. The factor of the material, as an independent factor, affects the tensile strength to a statistically significant degree, in contrast to the factor of the presence of inert gas which does not affect to a statistically significant degree.展开更多
Si3N4 ceramic was jointed to Si3N4 ceramic using a filler alloy of Cu-Zn-Ti at 1123-1323K for 0.3-2.7ks. Ti content in the Cu-Zn-Ti filler alloy was 15%（molar fraction）. The effect of bonding parameters on t...Si3N4 ceramic was jointed to Si3N4 ceramic using a filler alloy of Cu-Zn-Ti at 1123-1323K for 0.3-2.7ks. Ti content in the Cu-Zn-Ti filler alloy was 15%（molar fraction）. The effect of bonding parameters on the microstructure and mechanical properties of the Si3N4/Si3N4 joint were investigated. The results indicate that with increasing brazing temperature from 1123K to 1323K and brazing time from 0.3ks to 2.7ks, the thickness of the interfacial reaction layer between the filler alloy and the Si3N4 ceramic and the size and amount of the reactant products in the filler alloy increase, leading to an increase in shear strength of the joint from 163MPa to 276MPa. It is also found that the fracture behavior of the Si3N4/Si3N4 joint greatly depends on the microstructure of the joint.展开更多
文摘Titanium alloy (Ti-Al-V alloy) substrate was brazed with stainless steel (STS304) using filler metal.At an optimized brazing condition,various filler metals were used.Microstructures were observed at each condition.Filler metals were titanium based 40Ti-20Zr-20Cu-20Ni,silver based Ag 5Pd,and nickel based Ni-7Cr-3.1B-4.5Si-3Fe-0.06C (BNi2) and Ni-14Cr-10P-0.06C (BNi7).To select a good filler metal for brazing process,wetting test was performed at 880-1050 °C.It was not brazed using silver based filler metals,but at the conditions using titanium and nickel based filler metals had brazed zone between titanium alloy and stainless steel.However,titanium alloy was eroded during brazing using titanium based filler metals.Nickel based filler metal has a good brazed zone between titanium alloy and stainless steel among the filler metals.
文摘Laser welding with filler wire of AZ31 magnesium alloys is investigated using a CO2 laser experimental system. The effect of three different filler wires on the joint properties is researched. The results show that the weld appearance can be effectively improved when using laser welding with filler wire. The microhardness and tensile strength of joints are almost the same us those of the base metal when ER AZ31 or ER AZ61 wire is adopted. However, when the filler wire of ER 5356 aluminum alloy is used, the mechanical properties of flints become worse. For ER AZ31 and ER AZ61 filler wires, the microstructure of weld zone slws small dendrite grains. In comparison, for ER 5356 filler wire, the weld shows a structure of snowy dendrites and many intermetallic compounds and eutectic phases distribute in the dendrites. These intermetallic constituents with low melting point increase the tendency of hot crack and result in fiagile joint properties. Therefore, ER AZ31 and ER AZ61 wire are more suitable filler material than ER 5356 for CO2 laser welding of AZ31 magnesium alloys.
基金financially supported by the Foundation of Scientist and Technician Serving the Enterprise,the Ministry of Science and Technology of China (No.2009GJC20040)
文摘Al-6.5Si-42Zn and Al-6.5Si-42Zn-0.09Sr filler metals were used for brazing 6061 aluminum alloy. Air cooling and water cooling were applied after brazing. Si phase morphologies in the brazing alloy and the brazed joints were investigated. It was found that zinc in the Al-Si filler metals could reduce the formation of eutectic Al-Si phase and lower the brazing temperature at about 520℃. Adding 0.09wt% Sr element into the Al-6.5Si-42Zn alloy caused a-Al phase refinement and transformed acicular Si phase into the finely fiber-like. After water cooling, Zn element dissolved into the Al-Si eutectic area, and η-Zn phase disappeared in the brazed joints. Tensile strength testing results showed that the Sr-modified filler metal could enhance the strength of the brazed joints by 13% than Al-12Si, while water-cooling further improved the strength at 144 MPa.
文摘The density of liquid Ni-Cr alloy was measured by a modified sessile drop method. The density of liquid Ni-Cr alloywas found to decrease with increasing temperature and Cr concentration in the alloy. The molar volume of liquidNi-Cr alloy increases with increasing the Cr concentration in the alloy. The molar volume of Ni-Cr alloy determinedin the present work shows a positive deviation from the linear molar volume.
文摘Si/SiC ceramic composite and lnvar alloy were successfidly joined by vacuum brazing using Ti5OCu-W filler metals into which W was added to release the thermal stress of the brazed joint. Microstructures of the brazed joints were irwestigated by scanning electron micrascope （SEM） and energy dispersive spectrometer （EDS）. The mechanical properties of the brazed joints were measured by shearing tests. The results showed that the brazed joints were composed of Ti-Cu phase, W phase and Ti-Si phase. W had no effect on the wettability and mobility of the .filler metals. The growth of Ti2 Cu phase was restrained, and the reaction between ceramic composite and filler metals was weakened. The specimen, brazed at 970°C for 5 rain, had the maximum shear strength of 108 MPa at room temperature.
文摘CO2 laser welding aluminum alloy with filler wire was studied. The results indicate that the problems in CO2 laser welding of Al alloy, such as bad appearance of weld, easily excessive penetration and low strength, can be improved effectively by using laser welding with filler wire, and the maximum tensile strength of weld can reach 94% for the base metal. It also can be found that, the linear energy have great influence on the microstructure and mechanical properties of the joint. As the heat input increases, the cellular fir-tree crystals in the weld zone become sparse and the form of tensile fracture transforms from gliding fracture to brittle fracture.
文摘Si3N4 ceramic was jointed to itself using a filler alloy of Cu-Zn-Ti by the reaction between Ti and Si3N4. The microstructure of the interface in the joint is found to be Si3N4 ceramic/TiN reaction layer/Ti5Si3 reaction layer. The grain size of the TiN and Ti5Si3 reaction layer is 0.1μm and 1-2μm, respectively. There is no crystal orientation relationship between TiN reaction layer and Si3N4 ceramic or Ti5Si3 reaction layer. The kinetic equation for calculating the thickness of the reaction layer was obtained. When a （CuZn）85Ti15 alloy is used as the filler alloy, the apparent activation energy of the growth of the reaction layer is 201.69kJ/mol.
文摘Ti-based filler metals made by transient solidification and normal crystallization were selected for the vacuum brazing of the TiAl alloy and 42CrMo under different processing parameters. The results show that the tensile strength of the joint of transient solidified filler metal is higher than that of normal crystallized filler metal under the same processing parameters. By the analysis of scanning electron microscope（SEM） and X-ray diffracting （XRD） , it is found that the higher strength maybe caused by the generating of TiAl , TiNi and TiCu at the interface of joint made by transient solidified filler metal.
文摘The effects of the addition of rare earths on the properties of Ti-Zr-Cu-Ni base brazing filler alloys and the mechanical microstructure and properties were studied for the brazed-joints in the vacuum brazing of TC4 by comparing synthetical properties of two kinds of filler metals.The results indicate that the filler metals added with rare earths have lower melting point, better wettability and higher mechanical properties in the brazing joints.
基金This work is financially supported by Project 985-Automotive Engineering of Jilin University
文摘The aluminide coating process of Ti-6Al-4V alloys with different fillers(100wt.% Al_2O_3,50wt% Y_2O_3+50wt.% Al_2O_3 and 100wt.% Y_2O_3) for improvement of the oxidation resistance were investigated.The results show that the filler does not only participate in the aluminizing process,but also has much effect on the coating composition.The XRD analysis reveals that the aluminide coating with filler Al_2O_3 is predominant with TiAl_3 and TiAl phases;while the aluminide coatings with filler Y_2O_3+Al_2O_3 are predominant with Ti_3Al phase.The oxidation kinetics shows that different fillers affect greatly the oxidation resistance of aluminide coating,and the oxidation resistance of aluminized specimens with pack aluminizing filler Al_2O_3 are about 5-8 times than that of the aluminized specimens with other pack aluminizing fillers.
文摘It＇ s well known welding takes the leading role in development of titanium structures. However, in number of cases technological processes of brazing are more appropriate and, sometimes, being the single possible, in particular, during production of multilayer thin-wall structures. It should be noted that brazing filler metals of Ti-Cu-Ni, Ti-Zr-Cu-Ni, Zr-Ti-Ni and Cu-Zr-Ti systems in a form of plastic foils, as well as in powder form are mainly used in world practice for brazing of titanium alloys. Present work provides the results of complex investigations of brazing filler metals of Ti-Zr-Fe, Ti-Zr-Mn and Ti-Zr-Co systems using differential thermal analysis, light and scanning microscopy, X-ray microspectrum analysis. Data on melting ranges of pilot alloys were obtained, and liquidas su^Caces of given systems using simplex-lattice method were build. Brazing filler metals covering brazing temperature range of current structural titanium materials based on solid solutions as well as intermetallics were proposed. Structure, chemical inhomogeniety and strength characteristics of brazed joints were studied. It is determined that brazing of solid solution based alloys （OT4, VT6 ） using indicated brazing fiUer metals ensures strength characteristics of joints, which are not inferior to that obtained with application of known brazing filler metals even if they are received at lower brazing temperature.
文摘A high Fe containing aluminum matrix filler metal for hardfacing aluminum silicon alloys has been developed by using iron,nickel,and silicon as the major strengthening elements,and by measuring mechanical properties,room temperature and high temperature wear tests,and microstructural analysis.The filler metal,which contains 3.0%-5.0% Fe and 11.0%-13.0% Si,exhibits an excellent weldability.The as cast and as welded microstructures for the filler metal are of uniformly distribution and its dispersed network of hard phase is enriched with Al Si Fe Ni.The filler metal shows high mechanical properties and wear resistance at both room temperature and high temperatures.The deposited metal has a better resistance to impact wear at 220℃ than that of substrate Al Si Mg Cu piston alloy;at room temperature,the deposited metal has an equivalent resistance to slide wear with lubrication as that of a hyper eutectic aluminum silicon alloy with 27% Si and 1% Ni.
文摘Si3N4 ceramic was jointed to itself using a filler alloy of Cu76.5Pd8.5Ti15, and the mechanical properties of the jointwere measured and analyzed. By using a filler alloy of Cu76.5Pd8.5Ti15, the SisN4/SisN4 joints were obtained bybrazing at 1373～1473 K for 0.9～5.4 ks under a pressure of 2×10-3 MPa. The effect of brazing parameters on theshear strength of the joint was investigated. When the brazing temperature and holding time is 1423 K and 5.4 ksrespectively, the maximum shear strength of the Si3N4/Si3N4 joint is obtained to be 198 MPa.
文摘The density of Ni-Cr alloy in the mushy state has been measured using the modified sessile drop method. The density of Ni-Cr alloy in the mushy state was found to decrease with increasing temperature and Cr concentration in alloy. The molar volume of Ni-Cr alloy in the mushy state therefore increases with increasing the Cr concentration in alloy. The ratio of the difference of density divided by the temperature difference between liquidus and solidus temperatures decreases with increasing Cr concentration. The density of the alloy increased with the precipitation of a solid phase in alloy during the solidification process. The temperature dependence of the density of alloy in the mushy state was not linear but biquadratic.
文摘The purpose of this research was to study the effect of Argon inert gas on the laser welding quality of Co-Cr and Ni-Cr base metal alloys, which are widely used as Fixed Prosthodontics alloys in Dental Laboratories. A total of 36 specimens were manufactured (18 of Ni-Cr alloy and 18 of Co-Cr alloy). The specimens were then divided into 3 subgroups (6 specimens each): control;argon-welded;and non-Argon welded. The specimens were cut, laser welded, radiographed and finally tested under tensile strength testing, followed by examination using Scanning Electron Microscopy. The tensile strength of welded specimens was lower than the strength of non-welded specimens, however this difference was not found to be statistically significant. The material factor (Co-Cr alloy or Ni-Cr alloy) has a statistically significant effect on the tensile strength, while the presence or not of the inert gas, as well as the combination of the two factors do not have a statistically significant effect. The laser welding process applied in daily practice (separation of specimen, formation of two cones in contact, aggregation of two cones, filling of the remaining gap by welding) is considered satisfactory in terms of weld strength. The factor of the material, as an independent factor, affects the tensile strength to a statistically significant degree, in contrast to the factor of the presence of inert gas which does not affect to a statistically significant degree.
文摘Si3N4 ceramic was jointed to Si3N4 ceramic using a filler alloy of Cu-Zn-Ti at 1123-1323K for 0.3-2.7ks. Ti content in the Cu-Zn-Ti filler alloy was 15%（molar fraction）. The effect of bonding parameters on the microstructure and mechanical properties of the Si3N4/Si3N4 joint were investigated. The results indicate that with increasing brazing temperature from 1123K to 1323K and brazing time from 0.3ks to 2.7ks, the thickness of the interfacial reaction layer between the filler alloy and the Si3N4 ceramic and the size and amount of the reactant products in the filler alloy increase, leading to an increase in shear strength of the joint from 163MPa to 276MPa. It is also found that the fracture behavior of the Si3N4/Si3N4 joint greatly depends on the microstructure of the joint.