ELECTRODEPOSITION OF AMORPHOUS Ni-P ALLOY COATINGS

ＥＬＥＣＴＲＯＤＥＰＯＳＩＴＩＯＮＯＦＡＭＯＲＰＨＯＵＳＮｉＰＡＬＬＯＹＣＯＡＴＩＮＧＳ①ＦａｎｇＺｈａｏｈｅｎｇＩｎｓｔｉｔｕｔｅｏｆＣｈｅｍｉｃａｌＭｅｔａｌｕｒｇｙ，ＣｈｉｎｅｓｅＡｃａｄｅｍｙｏｆＳｃｉｅｎｃｅｓ，Ｂｅｉｊｉｎｇ１０００８０...

Preparation of FeCoNi medium entropy alloy from Fe^(3+)-Co^(2+)-Ni^(2+)solution system

In recent years,medium entropy alloys have become a research hotspot due to their excellent physical and chemical performances.By controlling reasonable elemental composition and processing parameters,the medium entropy alloys can exhibit similar properties to high entropy alloys and have lower costs.In this paper,a FeCoNi medium entropy alloy precursor was prepared via sol-gel and coprecipitation methods,respectively,and FeCoNi medium entropy alloys were prepared by carbothermal and hydrogen reduction.The phases and magnetic properties of FeCoNi medium entropy alloy were investigated.Results showed that FeCoNi medium entropy alloy was produced by carbothermal and hydrogen reduction at 1500℃.Some carbon was detected in the FeCoNi medium entropy alloy prepared by carbothermal reduction.The alloy prepared by hydrogen reduction was uniform and showed a relatively high purity.Moreover,the hydrogen reduction product exhibited better saturation magnetization and lower coercivity.

Influence of introducing Zr,Ti,Nb and Ce elements on externally solidified crystals and mechanical properties of high-pressure die-casting Al–Si alloy

High pressure die casting(HPDC)AlSi10Mn Mg alloy castings are widely used in the automobile industry.Mg can optimize the mechanical properties of castings through heat treatment,while the release of thermal stress arouses the deformation of large integrated die-castings.Herein,the development of non-heat treatment Al alloys is becoming the hot topic.In addition,HPDC contains externally solidified crystals(ESCs),which are detrimental to the mechanical properties of castings.To achieve high strength and toughness of non-heat treatment die-casting Al-Si alloy,we used AlSi9Mn alloy as matrix with the introduction of Zr,Ti,Nb,and Ce.Their influences on ESCs and mechanical properties were systematically investigated through three-dimensional reconstruction and thermodynamic simulation.Our results reveal that the addition of Ti increased ESCs'size and porosity,while the introduction of Nb refined ESCs and decreased porosity.Meanwhile,large-sized Al_3(Zr,Ti)phases formed and degraded the mechanical properties.Subsequent introduction of Ce resulted in the poisoning effect and reduced mechanical properties.

Effects of the extrusion parameters on microstructure,texture and room temperature mechanical properties of extruded Mg-2.49Nd-1.82Gd-0.2Zn-0.2Zr alloy

Microstructure,texture,and mechanical properties of the extruded Mg-2.49Nd-1.82Gd-0.2Zn-0.2Zr alloy were investigated at different extrusion temperatures(260 and 320℃),extrusion ratios(10:1,15:1,and 30:1),and extrusion speeds(3 and 6 mm/s).The experimental results exhibited that the grain sizes after extrusion were much finer than that of the homogenized alloy,and the second phase showed streamline distribution along the extrusion direction(ED).With extrusion temperature increased from 260 to 320℃,the microstructure,texture,and mechanical properties of alloys changed slightly.The dynamic recrystallization(DRX)degree and grain sizes enhanced as the extrusion ratio increased from 10:1 to 30:1,and the strength gradually decreased but elongation(EL)increased.With the extrusion speed increased from 3 to 6 mm/s,the grain sizes and DRX degree increased significantly,and the samples presented the typical<2111>-<1123>rare-earth(RE)textures.The alloy extruded at 260℃ with extrusion ratio of 10:1 and extrusion speed of 3 mm/s showed the tensile yield strength(TYS)of 213 MPa and EL of 30.6%.After quantitatively analyzing the contribution of strengthening mechanisms,it was found that the grain boundary strengthening and dislocation strengthening played major roles among strengthening contributions.These results provide some guidelines for enlarging the industrial application of extruded Mg-RE alloy.

Study on the hydrogen absorption properties of a YGdTbDyHo rare-earth high-entropy alloy

This study investigated the microstructure and hydrogen absorption properties of a rare-earth high-entropy alloy(HEA),YGdTbDyHo.Results indicated that the YGdTbDyHo alloy had a microstructure of equiaxed grains,with the alloy elements distributed homogeneously.Upon hydrogen absorption,the phase structure of the HEA changed from a solid solution with an hexagonal-close-packed(HCP)structure to a high-entropy hydride with an faced-centered-cubic(FCC)structure without any secondary phase precipitated.The alloy demonstrated a maximum hydrogen storage capacity of 2.33 H/M(hydrogen atom/metal atom)at 723 K,with an enthalpy change(ΔH)of-141.09 kJ·mol^(-1)and an entropy change(ΔS)of-119.14 J·mol^(-1)·K^(-1).The kinetic mechanism of hydrogen absorption was hydride nucleation and growth,with an apparent activation energy(E_(a))of 20.90 kJ·mol^(-1).Without any activation,the YGdTbDyHo alloy could absorb hydrogen quickly(180 s at 923 K)with nearly no incubation period observed.The reason for the obtained value of 2.33 H/M was that the hydrogen atoms occupied both tetrahedral and octahedral interstices.These results demonstrate the potential application of HEAs as a high-capacity hydrogen storage material with a large H/M ratio,which can be used in the deuterium storage field.

Electroless Ni-P plating on Mg-Li alloy by two-step method

Pretreated Mg-Li alloy sheets were pre-plated in a NiCO3？2Ni（OH）2？4H2O solution to form a thin Ni-P alloy film and then plating in a NiSO4？6H2O solution was carried out to obtain a protective coating.The surface morphology,structure and corrosion resistance of the coating were studied.The results showed that a flat,bright and compact plating layer,which was integrated into the matrix metal,was obtained.The P content of the Ni-P coating reached 13.56%（mass fraction）.The hardness value of the Ni-P coating was about HV 549.The polarization curve showed that the corrosion potential of the Ni-P coating reached ？0.249 V（vs SCE）.A long passivation region was found on the polarization curve,and this phenomenon indicated that the coating has an excellent anti-corrosion property.

An in situ measure method to study deposition mechanism of electroless Ni-P plating on AZ31 magnesium alloy

An in situ method was designed to measure a continuous open circuit potential （OCP） curve of AZ31 magnesium alloy and to observe the morphology variation of Ni-P coating during the process of the electroless plating. The deposition mechanism of the electroless Ni-P plating on AZ31 Mg alloy was studied by OCP curve, scanning electron microscopy （SEM）, and energy dispersion spectroscopy （EDS）. The process of electroless Ni-P plating contains the coating formation stage and the coating growth stage. The formation stage includes three procedures, i.e., the nucleation and growth of Ni crystallites, the extension of the coating in two-dimensional （2D） direction and the coalescence of the coating along three-dimensional （3D） direction. SEM investigations demonstrate that the spherical nodules of the Ni-P coating are not only formed during the coating growth stage, but also generated in the initial deposition stage of electroless Ni-P plating. The variation of the coating rates at different deposition stages corresponds to the deposition mechanism of their respective deposition stage.

Effect of novel ternary ligand system on acidic electroless Ni-P plating on AZ91D magnesium alloy

The electroless Ni-P coatings on AZ91 D magnesium alloy substrate were prepared using the acidic hypophosphite-reduced electroless nickel bath containing the novel ternary ligand system. The results indicate that the deposition rate varies with the ternary ligand concentration in plating solution. The structural and morphological characteristics of the coatings were analyzed by XRD and SEM. The anticorrosion properties of the Ni-P coatings were evaluated in 3.5% NaCl solution by electrochemical impedance and potentiodynamic polarization methods. The amount of ternary ligands in electroless plating bath has an significant effect on the surface morphology and structure of Ni-P coatings. The decrease of crystallization temperature and increase of crystallization heat of all the deposits with an increase in ternary ligand concentration are found by DSC measurements. The coating obtained with 0.035 mol/L ternary ligand additive in plating bath can offer a better surface homogeneity and improve corrosion resistance.

Electroless plating and growth kinetics of Ni-P alloy film on SiC_p/Al composite with high SiC volume fraction

After Sn/Pd activating, the SiCp/Al composite with 65% SiC (volume fraction) was coated by electroless Ni?P alloy plating. Surface morphology of the composite and its effect on the Ni?P alloy depositing process and bonding action of Ni and P atoms in the Ni?P alloy were studied. The results show that inhomogeneous distribution of the Sn/Pd activating points results in preferential deposition of the Ni?P alloy particles on the Al alloy and rough SiC particle surfaces and in the etched caves. The Ni?P alloy film has an amorphous structure where chemical bonding between Ni and P atoms exists. After a continuous Ni?P alloy film formed, electroless Ni?P alloy plating is not affected by surface morphology and characteristics of the SiCp/Al composite any longer, but by the electroless plating process itself. The Ni?P alloy film follows linear growth kinetics with an activation energy of 68.44 kJ/mol.

TWIP钢表面Ni-P化学镀层组织结构及性能研究

目的在孪生诱发塑性钢(TWIP)表面制备Ni-P镀层,提高TWIP钢的耐腐蚀性能。方法通过化学镀工艺在TWIP钢表面制备了高磷Ni-P镀层,并进行不同温度的热处理,利用扫描电镜及能谱仪、X射线衍射仪及原子力显微镜等探究了热处理温度和时间对Ni-P镀层形貌和组织结构的影响。通过电化学方法研究了TWIP钢表面镀层的耐蚀性能。结果随着热处理温度的升高,镍磷原子发生迁移,胞状组织边界模糊,粗糙度降低,其中600℃热处理镀层表面最为致密平整。随着热处理温度的升高,镀层组织结构演变过程如下:非晶态(普通镀层)→非晶态部分晶化,Ni12P5、Ni5P2等亚稳态镍磷化合物析出(300℃)→非晶态完全晶化、稳态Ni3P相长大(400℃)→晶粒长大(500℃、600℃)。Ni-P镀层能够明显提升TWIP钢的耐腐蚀性能。随着热处理温度的升高,镀层的耐蚀性能先降低后升高。600℃热处理1h镀层的腐蚀电流密度为0.25μA/cm^(2),与普通Ni-P镀层相比降低了80.9%,与TWIP钢基体相比降低了99.6%。600℃热处理镀层光滑致密无缺陷的表面促进了保护性氧化膜的产生,使镀层的耐蚀性能提高。结论合适的热处理工艺提高了Ni-P镀层的致密性和保护能力,光滑致密无缺陷的镀层能够为TWIP钢提供良好的防护。

High corrosion resistance of electroless Ni-P with chromium-free conversion pre-treatments on AZ91D magnesium alloy

Phosphate-manganese, tannic acid and vanadium conversion coatings were proposed as an effective pre-treatment layer between electroless Ni-P coating and AZ91D magnesium alloy substrate to replace the traditional chromate plus HF pre-treatment. The electrochemical results show that the chrome-free coatings plus electroless Ni-P coating on the magnesium alloy has the lowest corrosion current density and most positive corrosion potential compared with chromate plus electroless Ni-P coating on the magnesium alloy. These proposed pre-treatment layers on the substrate reduce the corrosion of magnesium during plating process, and reduce the potential difference between the matrix and the second phase. Thus, an electroless Ni-P coating with fine crystalline and dense structure was obtained, with preferential phosphorus content, low porosity, good corrosion-resistance and strengthened adhesion than the chromate plus electroless Ni-P.

High-temperature tribological properties of Ni-P alloy coatings deposited by electro-brush plating

High-temperature tribological properties of Ni-P alloy coatings processed by electro-brush plating on 20CrMo steel have been investigated. A baU-on-disc configuration was employed and 4 mm diameter Si3N4 balls were used as static counterpart. All the wear tests were carried out at 450℃ for 180 rain without lubricants. The electro-brush plating Ni-P coating is amorphous in as-deposited condition, and it becomes polycrystalline with the formation of Ni and Ni3P after heat treatment at 450℃for 1 h. The friction coefficient of the Ni-P coating is just 50% of that of the 20CrMo steel at the friction temperature of 450℃. A mild adhesive wear mechanism was found for the electro-brush plating Ni-P coating tested at 450℃, whereas for the 20CrMo steel at the same temperature a mixed adhesive and abrasive wear mechanism was observed.

化学镀Ni-P/Sn2.5Ag0.7Cu0.1RE微连接焊点热时效过程组织与性能

为探究化学镀Ni-P无铅焊点在热时效作用下的组织与性能,采用化学镀方法在T2紫铜表面制备Ni-P层,使用Sn_(2.5)Ag_(0.7)Cu_(0.1)RE钎料通过回流焊方法制备化学镀Ni-P无铅焊点。结果表明:微焊点Ni-P/钎缝过渡区域金属间化合物(IMC)初始组织为呈块状的(Ni,Cu)_(3)Sn_(4),平均厚度为1.5μm。在180℃条件下时效100 h过程中,微焊点Ni-P/钎缝过渡区(Ni,Cu)_(3)Sn_(4)IMC形貌逐渐转变为层状并增厚至3.3μm,微焊点剪切断裂位置由钎缝处向Ni-Sn-P/IMC交界处转移,断裂方式由韧性断裂转变为脆性断裂,相应微焊点的推剪力由初始的16 N下降11.9%。

低浓度硫酸铜对化学镀Ni-P镀层微观结构及性能的影响

为改善镍磷(Ni-P)镀层的表面质量、提高Ni-P镀层的性能,在化学镀Ni-P镀液中加入少量的硫酸铜(CuSO_(4)·5H_(2)O)制备Ni-P镀层。利用扫描电镜、能谱仪、X射线衍射仪分析了镀层的表面形貌、成分和结构,研究了CuSO_(4)·5H_(2)O浓度对镀层的微观结构、表面粗糙度、光泽度、硬度、耐磨性和耐蚀性的影响。研究表明:当CuSO_(4)·5H_(2)O浓度为0.1 g/L时,镀层为致密的非晶态节瘤状组织,具有最佳的耐蚀性;当CuSO_(4)·5H_(2)O浓度为0.2 g/L时,镀层表面质量最好,硬度高、耐磨性优异,但镀层中出现少量微晶态Ni-Cu固溶体,耐蚀性下降;当CuSO_(4)·5H_(2)O浓度超过0.2 g/L后,镀层为混晶态菜花状组织,镀层表面的质量和耐蚀性随CuSO_(4)·5H_(2)O浓度的增加不断恶化。

Homogenization pretreatment and electroless Ni-P plating on AZ91D magnesium alloy

Electroless nickel plating on AZ91D substrate with a new and eco-friendly pretreatment process based on tuning an electrochemical homogeneous surface was investigated. The morphology, deposition process, chemical composition and microstructure of Ni-P coating were studied. It is indicated that β phases are selectively removed, producing a microstructural homogeneous surface and the subsequent uniform and compact Zn immersion layer. A defect-free and well adhesive Ni-P coating can be successfully obtained due to its uniform nucleation and growth based on such pretreatment. Potentiodynamic polarization and electrochemical impedance spectroscopy （EIS） tests reveal that Ni-P coating could significantly improve the corrosion resistance of AZ91D substrate.

Investigation on a Non-cyanide Plating Process of Ni-P Coating on Magnesium Alloy AZ91D

In this research we presented a non-cyanide plating process of Ni-P alloy coating on Mg alloy AZ91D. By applying a new process flow of electroless nickel plating in which zinc coating is used as transition of Ni-P coating on Mg alloy AZ91D, the process of copper transition coating plated in the cyanides bath can be replaced. A new bath composed of NiSO4 was established by orthogonal test. The results show that zinc transition coating can increase the adhesion and protect the Mg alloy substrate from the bath corrosion. The optimal plating bath composition is NiSO4·6H2O 20 g/L, NaH2PO2·H2O20g/L and C6H8O7·H2O 2.5 g/L, and optimal bath acidity and optimal plating temperature are pH 4.0 and 95℃, respectively. The present process flow is composed of ultrasonic cleaning→alkaline cleaning→acid pickling→activation→double immersing zinc→electroplating zinc→electroless nickel plating→passivation treatment. The present non-cyanide process of electroless nickel plating is harmless to our surroundings and Ni-P coating on Mg alloy AZ91D produced by present process possesses good adhesion and corrosion resistance.

Pretreatment-free Ni-P plating on magnesium alloy at low temperatures

Electrochemically promoted electroless plating(EPEP)was used for the application of pretreatment-free Ni-P coating on AM60B magnesium alloy at low temperatures and the obtained coating was characterized by SEM,AFM,EDS and XRD techniques.Compact,uniform,and medium-phosphorus Ni-P coating with mixed crystalline-amorphous microstructure was obtained by applying a cathodic current density of4mA/cm^2at50℃.Also,island-like nickel clusters were deposited on the alloy surface under the same plating condition but without applying the cathodic current.In addition,the durability of the magnesium alloy against corrosion was strongly improved after plating via EPEP technique which was revealed by electrochemical examinations in3.5%NaCl(mass fraction)corrosive electrolyte.The results of the electrochemical examinations were confirmed by microscopic observations.Thickness,microhardness,porosity and adhesive strength of the deposits were also qualified.

High-temperature Compressive Performance of Mg Alloy Foams Coated with Ni-P Layer

Mg/Ni hybrid foams were fabricated by the electroless method.The Ni-P(Nickel-Phosphorous)coatings were deposited on the surface of closed-cell Mg alloy foams.The composition,microstructure and phases of the Ni-P coatings were characterized by scanning electron microscopy(SEM),energy-dispersive X-ray spectroscopy(EDS)and X-ray diffraction(XRD),respectively.The compressive tests were performed on the Mg/Ni hybrid foams at 400℃using the Mg alloy foams as a reference.The experimental results show that the yield strength,plateau stress and energy absorption capacity of the closed-cell Mg alloy foams at high temperature were improved by the Ni-P coating.And there are four main modes for the Mg/Ni hybrid foam failure at 400℃,i e,shearing in cell wall,bending in cell edge,shedding and cracking in Ni-P coating.

Study on Electromagnetic Shielding Effectiveness of Ni-P-La Alloy Coatings

Ni-P and Ni-P-La alloy coatings were prepared by electroplating. Electromagnetic shielding effectiveness under the different components of rare earth or the different operating conditions was tested by the network analyzer. The results show that electromagnetic shielding effectiveness of Ni-P-La alloy coating varies from 45 dB to 70 dB with the variety of the frequency from 10 MHz to 350 MHz. Corrosion of the salt fog impacts on the electromagnetic shielding effectiveness a little. A small amount of rare earth added to plating bath can not only enhance corrosion resistance of coating, but make electromagnetic shielding effectiveness increase by 1 ~ 5 dB.

Electrochemical behavior of Cu-Zn-Al shape memory alloy after surface modification by electroless plated Ni-P

The electrochemical behavior of Cu-Zn-Al shape memory alloy (SMA) with andwithout electroless plated Ni-P was investigated by electrochemical methods, in artificial Tyrode'ssolution. The results showed that Cu-Zn-Al SMA engendered dezincification corrosion in Tyrode'ssolution. The anodic active current densities as well as electrochemical dissolution sensitivity ofthe electroless plated Ni-P Cu-Zn-Al SMA increased with NaCl concentration rising, pH of solutiondecreasing and environmental temperature uprising. X-ray diffraction analysis indicated that aftersurface modification by electroless plated Ni-P, an amorphous plated film formed on the surface ofCu-Zn-Al SMA. This film can effectively isolate matrix metal from corrosion media and significantlyimprove the electrochemical property of Cu-Zn-Al SMA in artificial Tyrode's solution.