Vapor-phase transformations of furfural over SBA-15 silica supported Ni catalysts under H<sub>2</sub> in a continuous-flow reactor at atmospheric pressure and 170°C and 230°C were investiga...Vapor-phase transformations of furfural over SBA-15 silica supported Ni catalysts under H<sub>2</sub> in a continuous-flow reactor at atmospheric pressure and 170°C and 230°C were investigated. Two different samples having Ni loadings of 5 and 20 wt% (denoted here by SBA-5Ni and SBA-20Ni, respectively) were prepared by impregnation and characterized by atomic absorption spectroscopy, N<sub>2</sub> sorption analysis, X-ray diffraction, X-ray photoelectron spectroscopy, and transmission electron microscopy. Furan and furfuryl alcohol were two primary products resulting, respectively, from decarbonylation and hydrogenation of furfural. Under the conditions of the study, both reactions exhibited structure sensitivity evidenced by changes in product selectivities with variable Ni loadings. Compared with SBA-20Ni, the 5 wt% Ni catalyst showed better catalytic activity, reaching a furfural conversion of 100 mol% and a selectivity to furan of 98 mol%, after 5 h of time-on-stream at 230°C.展开更多
A series of Ni/SBA-15 catalysts with Ni contents ranging from 5wt% to 20wt% as well as 10wt%Ni/10wt%CexZr1-xO2/SBA-15 （x=0, 0.5, 1） were prepared. The structures of the catalysts were characterized using XRD, TPR, T...A series of Ni/SBA-15 catalysts with Ni contents ranging from 5wt% to 20wt% as well as 10wt%Ni/10wt%CexZr1-xO2/SBA-15 （x=0, 0.5, 1） were prepared. The structures of the catalysts were characterized using XRD, TPR, TEM and BET techniques. The catalytic activities of the catalysts for steam reforming of methane were evaluated in a continuous flow microreactor. The results indicated that both the Ni/SBA-15 and the Ni/CexZr1-xO2/SBA-15 catalysts had good catalytic activities at at- mospheric pressure. The 10wt%Ni/SBA-15 catalyst exhibited excellent stability at 800 ℃ for time on stream of 740 h. After the reaction, carbon deposits were not formed on the surface of the catalyst. There existed a regular hexagonal mesoporous structure in the Ni/SBA-15 and the Ni/CexZr1-xO2/SBA-15 catalysts. The nickel species and the CexZr1-xO2 component were all confined in the SBA-15 mesopores. The CexZr1-xO2 could promote dispersion of the nickel species in the Ni/CexZr1-xO2/SBA-15 catalysts.展开更多
A series of Ni/SBA-15 catalysts with 5wt% to 15wt% Ni content as well as a series of 12.5%Ni/Cu/SBA-15 catalysts with 1% to 10% copper content were prepared by the impregnation method. The catalytic performance for pa...A series of Ni/SBA-15 catalysts with 5wt% to 15wt% Ni content as well as a series of 12.5%Ni/Cu/SBA-15 catalysts with 1% to 10% copper content were prepared by the impregnation method. The catalytic performance for partial oxidation of methane was investigated in a continuous flow microreactor under atmospheric pressure. The textural and chemical properties of the catalysts were characterized by XRD, TEM, BET and Hz-TPR techniques. The results indicated that the catalysts modified with Cu promoter showed better performance than those without modification. For the 12.5%Ni/2.5%/Cu/SBA-15 catalyst, at 850 ℃ the conversion of CH4 reached 97.9% and the selectivity of CO and H2 reached 98.0% and 96.0%, respectively. In XRD patterns of the Ni/Cu/SBA-15 catalyst with 7.5 to 10% Cu contents there were CuO characteristic peaks beside NiO characteristic peaks. The mesoporous structure of SBA-15 was retained in all of the catalysts. TPR analysis of the catalysts revealed that a strong interaction between Ni, Cu promoter and SBA-15 support may be existed. This interaction enhanced significantly the redox properties of the catalysts resulting in the higher catalytic activity.展开更多
A series of Ni/SBA-15 catalysts with Ni contents from 7.5 wt% to 15 wt% were prepared by impregnation method.The effect of O2 and H2O on the combined reforming of the simulated biogas to syngas was investigated in a c...A series of Ni/SBA-15 catalysts with Ni contents from 7.5 wt% to 15 wt% were prepared by impregnation method.The effect of O2 and H2O on the combined reforming of the simulated biogas to syngas was investigated in a continuous flow fixed-bed micro-reactor.The stability of the catalyst was tested at 800 ？C.The results indicated that 10wt%Ni/SBA-15 catalyst exhibited the highest catalytic activities for the combined reforming of the simulated biogas to syngas.Under the reaction conditions of the feed gas molar ratios CH4/CO2/O2/H2O = 2/1/0.6/0.6,GHSV = 24000 ml·gcat^-1·h^-1 and the reaction temperature T = 800 ℃,the conversions of CH4 and CO2 were 92.8% and 76.3%,respectively,and the yields of CO and H2 were 99.0% and 82.0%,respectively.The catalytic activities of the catalyst did not decrease obviously after 100 h reaction time on stream.展开更多
基金Supported by the National Natural Science Foundation of China(U1361125,U1261208,21176001,51174254)the Provincial Innovative Group for Processing&Clean Utilization of Coal Resourcethe Innovative Research Team of Anhui University of Technology
文摘Vapor-phase transformations of furfural over SBA-15 silica supported Ni catalysts under H<sub>2</sub> in a continuous-flow reactor at atmospheric pressure and 170°C and 230°C were investigated. Two different samples having Ni loadings of 5 and 20 wt% (denoted here by SBA-5Ni and SBA-20Ni, respectively) were prepared by impregnation and characterized by atomic absorption spectroscopy, N<sub>2</sub> sorption analysis, X-ray diffraction, X-ray photoelectron spectroscopy, and transmission electron microscopy. Furan and furfuryl alcohol were two primary products resulting, respectively, from decarbonylation and hydrogenation of furfural. Under the conditions of the study, both reactions exhibited structure sensitivity evidenced by changes in product selectivities with variable Ni loadings. Compared with SBA-20Ni, the 5 wt% Ni catalyst showed better catalytic activity, reaching a furfural conversion of 100 mol% and a selectivity to furan of 98 mol%, after 5 h of time-on-stream at 230°C.
基金Financial funds from the Chinese Natural Science Foundation(Project No.20473009)the Beijing Natural Science Foundation(Project No.8062023)+1 种基金the National Basic Research Program of China(Project No.2005CB221405)the National"863"Project of China(No.2006 AA10Z425)are gratefully acknowledged.
文摘A series of Ni/SBA-15 catalysts with Ni contents ranging from 5wt% to 20wt% as well as 10wt%Ni/10wt%CexZr1-xO2/SBA-15 （x=0, 0.5, 1） were prepared. The structures of the catalysts were characterized using XRD, TPR, TEM and BET techniques. The catalytic activities of the catalysts for steam reforming of methane were evaluated in a continuous flow microreactor. The results indicated that both the Ni/SBA-15 and the Ni/CexZr1-xO2/SBA-15 catalysts had good catalytic activities at at- mospheric pressure. The 10wt%Ni/SBA-15 catalyst exhibited excellent stability at 800 ℃ for time on stream of 740 h. After the reaction, carbon deposits were not formed on the surface of the catalyst. There existed a regular hexagonal mesoporous structure in the Ni/SBA-15 and the Ni/CexZr1-xO2/SBA-15 catalysts. The nickel species and the CexZr1-xO2 component were all confined in the SBA-15 mesopores. The CexZr1-xO2 could promote dispersion of the nickel species in the Ni/CexZr1-xO2/SBA-15 catalysts.
基金supported by the National Basic Research Program of China (Project No. 2005CB221405)the National "863" Project of China (No.2006AA10Z425)
文摘A series of Ni/SBA-15 catalysts with 5wt% to 15wt% Ni content as well as a series of 12.5%Ni/Cu/SBA-15 catalysts with 1% to 10% copper content were prepared by the impregnation method. The catalytic performance for partial oxidation of methane was investigated in a continuous flow microreactor under atmospheric pressure. The textural and chemical properties of the catalysts were characterized by XRD, TEM, BET and Hz-TPR techniques. The results indicated that the catalysts modified with Cu promoter showed better performance than those without modification. For the 12.5%Ni/2.5%/Cu/SBA-15 catalyst, at 850 ℃ the conversion of CH4 reached 97.9% and the selectivity of CO and H2 reached 98.0% and 96.0%, respectively. In XRD patterns of the Ni/Cu/SBA-15 catalyst with 7.5 to 10% Cu contents there were CuO characteristic peaks beside NiO characteristic peaks. The mesoporous structure of SBA-15 was retained in all of the catalysts. TPR analysis of the catalysts revealed that a strong interaction between Ni, Cu promoter and SBA-15 support may be existed. This interaction enhanced significantly the redox properties of the catalysts resulting in the higher catalytic activity.
基金supported by the National Basic Research Program of China(Project No.2005CB221405)the National "863" Project of China (No.2006AA10Z425)the Beijing Natural Science Foundation (Project No: 8062023)
文摘A series of Ni/SBA-15 catalysts with Ni contents from 7.5 wt% to 15 wt% were prepared by impregnation method.The effect of O2 and H2O on the combined reforming of the simulated biogas to syngas was investigated in a continuous flow fixed-bed micro-reactor.The stability of the catalyst was tested at 800 ？C.The results indicated that 10wt%Ni/SBA-15 catalyst exhibited the highest catalytic activities for the combined reforming of the simulated biogas to syngas.Under the reaction conditions of the feed gas molar ratios CH4/CO2/O2/H2O = 2/1/0.6/0.6,GHSV = 24000 ml·gcat^-1·h^-1 and the reaction temperature T = 800 ℃,the conversions of CH4 and CO2 were 92.8% and 76.3%,respectively,and the yields of CO and H2 were 99.0% and 82.0%,respectively.The catalytic activities of the catalyst did not decrease obviously after 100 h reaction time on stream.