To improve the surface properties of AZ91 magnesium alloy, Ni-SiC nanocomposite coatings with various SiC contents were pulse electrodeposited in modified Watts baths containing SiC nano-particles with the concentrati...To improve the surface properties of AZ91 magnesium alloy, Ni-SiC nanocomposite coatings with various SiC contents were pulse electrodeposited in modified Watts baths containing SiC nano-particles with the concentration of 0-15 g/L. The morphology of the coatings was studied by scanning electron microscope （SEM）. The SiC content of the coatings was measured by energy dispersive spectroscopy （EDS） analyzer. Microhardness measurement of the coatings showed up to 600% enhancement for the sample produced from the bath with 15 g/L SiC. The corrosion behavior of the coated AZ91 alloy was investigated by potentiodynamic polarization method. The results reveal a significant improvement in the corrosion resistance, that is, the corrosion current density decreases from 0.13 mA/cm2 for uncoated specimen to 1.74x10-6 mA/cm2 for the sample coated from the bath containing 15 g/L SiC and the corrosion potential increases from -1.6 V for uncoated specimen to -0.31 V for the sample coated from the bath. The wear resistance of both coated and uncoated samples was evaluated by pin-on-disc tribotester. The results show that the wear volume loss of coated sample is 8 times less than the bare alloy.展开更多
The influences of surfactant type and concentration on the content and uniformity of SiC particles in Ni-SiC deposit were studied in this paper. The electrochemical behavior of preparing Ni-SiC composite coating was i...The influences of surfactant type and concentration on the content and uniformity of SiC particles in Ni-SiC deposit were studied in this paper. The electrochemical behavior of preparing Ni-SiC composite coating was investigated using the cyclic voltammetry method. Then the impact of surfactants on the deposition potential of Ni-SiC coating was analyzed. Electrochemical studies showed that the cathode overvoltage increases gradually with increasing SDS（Sodium dodecyl sulfate） concentration. The CV curve showed the shift towards a lower current at a given potential with increasing SDS concentration. Ni-SiC composite coatings were prepared by electrodeposition. The experimental results show that the dispersion of 40 nm SiC in Ni-SiC coating obtained in the electrolyte containing SDS is superior that containing CTAB（cetyltrimethyl ammonium bromide）. CTAB increases the content of 40 nm SiC particles in the Ni-SiC coating, but the uniformity of 40 nm SiC particles in Ni-SiC composite coating is poor. SiC particles are still agglomerated. Compared with the anionic surfactant SDS and the cationic surfactant CTAB, surfactant SDS makes the particles better dispersed. But the contribution of surfactant SDS for co-deposition amount of SiC particles is negligible. The cationic surfactant CTAB can effectively improve the suspension performance of SiC particles and promote the co-deposition of SiC particles and metallic nickel. But there is still some reunion of SiC.展开更多
文摘To improve the surface properties of AZ91 magnesium alloy, Ni-SiC nanocomposite coatings with various SiC contents were pulse electrodeposited in modified Watts baths containing SiC nano-particles with the concentration of 0-15 g/L. The morphology of the coatings was studied by scanning electron microscope （SEM）. The SiC content of the coatings was measured by energy dispersive spectroscopy （EDS） analyzer. Microhardness measurement of the coatings showed up to 600% enhancement for the sample produced from the bath with 15 g/L SiC. The corrosion behavior of the coated AZ91 alloy was investigated by potentiodynamic polarization method. The results reveal a significant improvement in the corrosion resistance, that is, the corrosion current density decreases from 0.13 mA/cm2 for uncoated specimen to 1.74x10-6 mA/cm2 for the sample coated from the bath containing 15 g/L SiC and the corrosion potential increases from -1.6 V for uncoated specimen to -0.31 V for the sample coated from the bath. The wear resistance of both coated and uncoated samples was evaluated by pin-on-disc tribotester. The results show that the wear volume loss of coated sample is 8 times less than the bare alloy.
基金the Program for Liaoning Excellent Talents in University(LJQ2015074)the Shenyang Science and Technology Plan(17-231-1-15)
文摘The influences of surfactant type and concentration on the content and uniformity of SiC particles in Ni-SiC deposit were studied in this paper. The electrochemical behavior of preparing Ni-SiC composite coating was investigated using the cyclic voltammetry method. Then the impact of surfactants on the deposition potential of Ni-SiC coating was analyzed. Electrochemical studies showed that the cathode overvoltage increases gradually with increasing SDS（Sodium dodecyl sulfate） concentration. The CV curve showed the shift towards a lower current at a given potential with increasing SDS concentration. Ni-SiC composite coatings were prepared by electrodeposition. The experimental results show that the dispersion of 40 nm SiC in Ni-SiC coating obtained in the electrolyte containing SDS is superior that containing CTAB（cetyltrimethyl ammonium bromide）. CTAB increases the content of 40 nm SiC particles in the Ni-SiC coating, but the uniformity of 40 nm SiC particles in Ni-SiC composite coating is poor. SiC particles are still agglomerated. Compared with the anionic surfactant SDS and the cationic surfactant CTAB, surfactant SDS makes the particles better dispersed. But the contribution of surfactant SDS for co-deposition amount of SiC particles is negligible. The cationic surfactant CTAB can effectively improve the suspension performance of SiC particles and promote the co-deposition of SiC particles and metallic nickel. But there is still some reunion of SiC.