Ni-plated glass beads（GB） was obtained by electroless plating, based on PVC adhesive, Niplated GB/PVC composite was prepared. Temperature insulation, fi re retardation and microwave absorption properties were tested...Ni-plated glass beads（GB） was obtained by electroless plating, based on PVC adhesive, Niplated GB/PVC composite was prepared. Temperature insulation, fi re retardation and microwave absorption properties were tested, the results showed that the nickel coating was compact and continuous, Ni-plated GB/ PVC composite is a kind of excellent temperature insulated, fi re retardate and light-weight material, and especially for microwave absorption well; Refl ectivity was lower than-2 dB in the frequency range of 11-17 GHz.展开更多
Hydrogen is a promising fuel for it is clean,highly abundant and non-toxic,but on-board storage of hydrogen is still a challenge.So it is imperative to have an efficient method of hydrogen storage.The mesoporous MCM-4...Hydrogen is a promising fuel for it is clean,highly abundant and non-toxic,but on-board storage of hydrogen is still a challenge.So it is imperative to have an efficient method of hydrogen storage.The mesoporous MCM-48 especially the nickel-containing MCM-48 has great potential in hydrogen storage.MCM-48 was prepared by hydrothermal synthesis.Then electroless plating technology was used to deposit Ni on the surface of MCM-48 under ultrasonic environment.Powder X-ray diffraction（XRD）,transmission electron microscopy（TEM）,and N2 adsorption-desorption were employed to investigate the pore structure properties.The results showed that all the samples had Ia3 d cubic structure and pore channels were highly ordered.Hydrogen adsorption studies showed that the MCM-48 after nickel plating adsorbed nearly twice the amount of hydrogen than pure MCM-48 at 2.0 MPa,263 K.So we believe that a small amount of Ni can improve the capacity of hydrogen adsorption of MCM-48 efficiently.展开更多
基金Funded in Part by the National Key Technology Research and Development Program of the Ministry of Science and Technology of China(No.2011BAC10B05)
文摘Ni-plated glass beads（GB） was obtained by electroless plating, based on PVC adhesive, Niplated GB/PVC composite was prepared. Temperature insulation, fi re retardation and microwave absorption properties were tested, the results showed that the nickel coating was compact and continuous, Ni-plated GB/ PVC composite is a kind of excellent temperature insulated, fi re retardate and light-weight material, and especially for microwave absorption well; Refl ectivity was lower than-2 dB in the frequency range of 11-17 GHz.
文摘Hydrogen is a promising fuel for it is clean,highly abundant and non-toxic,but on-board storage of hydrogen is still a challenge.So it is imperative to have an efficient method of hydrogen storage.The mesoporous MCM-48 especially the nickel-containing MCM-48 has great potential in hydrogen storage.MCM-48 was prepared by hydrothermal synthesis.Then electroless plating technology was used to deposit Ni on the surface of MCM-48 under ultrasonic environment.Powder X-ray diffraction（XRD）,transmission electron microscopy（TEM）,and N2 adsorption-desorption were employed to investigate the pore structure properties.The results showed that all the samples had Ia3 d cubic structure and pore channels were highly ordered.Hydrogen adsorption studies showed that the MCM-48 after nickel plating adsorbed nearly twice the amount of hydrogen than pure MCM-48 at 2.0 MPa,263 K.So we believe that a small amount of Ni can improve the capacity of hydrogen adsorption of MCM-48 efficiently.