A new two dimensional 8 ring network nickle phosphate Ni 3(PO 4) 2·8H 2O was synthesized hydrothermally and its structure was determined by means of single crystal X ray diffraction. The Ni 3(PO 4) 2·8H 2O c...A new two dimensional 8 ring network nickle phosphate Ni 3(PO 4) 2·8H 2O was synthesized hydrothermally and its structure was determined by means of single crystal X ray diffraction. The Ni 3(PO 4) 2·8H 2O crystal crystallizes in the monoclinic system, space group C2/m , with M=128.13, a =0\^994 7(2) nm, b =1.321 7(3) nm; c =0.463 6(1) nm; β=104.80(3)°, V =0.589 3(2) nm 3, Z=2, R=0.027 2 and wR =0.057 5. The network structure consists of vertex sharing which results in the formation of undulating 4 ring chains and 8 ring sheets.展开更多
The novel polyoxometalate, 32[Mo8ⅣMo4ⅤV2ⅣO38(PO4)], was synthesized and characterized by elementary analysis, EPR, IR spectra and X ray diffraction. The compoundcrystallizes in triclinic system, space group with a=...The novel polyoxometalate, 32[Mo8ⅣMo4ⅤV2ⅣO38(PO4)], was synthesized and characterized by elementary analysis, EPR, IR spectra and X ray diffraction. The compoundcrystallizes in triclinic system, space group with a= 1.41999(2)nm, b=1.43467(2)nm, c=1.694610(10)nm, α=95.7250(10)°, β=92.2110(10)°, γ=92.6060(10)°, V=3.42829(7)nm3, Z=2, Dc=2.388g·cm-3, Mr=2465.10g·mol-1, μ=2.489mm-1, F(000)=2388, R1=0.0584, wR2=0.1461, S=1.164. The heteropolyanion is a bi capped pseudo Keggin complex. CCDC: 186645.展开更多
A new compound 2 6[Co(H 2O) 2(VO) 8(OH) 4(PO 4) 8] has been hydrothermally synthesized. Single crystal X-ray analysis indicates that this compound crystallizes in a monoclinic system, space group P2 1/n with a=1.438 5...A new compound 2 6[Co(H 2O) 2(VO) 8(OH) 4(PO 4) 8] has been hydrothermally synthesized. Single crystal X-ray analysis indicates that this compound crystallizes in a monoclinic system, space group P2 1/n with a=1.438 5(3) nm, b=1.012 2(2) nm, c=1.832 5(4) nm, β=90.21°, V=2\^668 2(9) nm 3, Z=2, D c=2.112 g/cm 3, R=0.055, wR=0.149 7, S=1.037. The structure of 2 6[Co(H 2O) 2(VO) 8(OH) 4(PO 4) 8] is characterized by P-V-O layers constructed by [(VO) 4(OH) 2(PO 4) 4] 6- non-symmetric units. The P-V-O layers are pillared by [Co(H 2O) 2] 2+ group, resulting in the channels within which the protonated diaminoethane and H 3O + are located.展开更多
The CoO/CoVO/Ni nanocomposites were rationally designed and prepared by a two-step hydrothermal synthesis and subsequent annealing treatment. The one-dimensional（1D） CoOnanowire arrays directly grew on Ni foam, wher...The CoO/CoVO/Ni nanocomposites were rationally designed and prepared by a two-step hydrothermal synthesis and subsequent annealing treatment. The one-dimensional（1D） CoOnanowire arrays directly grew on Ni foam, whereas the 1D CoVOnanowires adhered to parts of CoOnanowires.Most of the hybrid nanowires were inlayed with each other, forming a 3D hybrid nanowires network.As a result, the discharge capacity of CoO/CoVO/Ni nanocomposites could reach 1201.8 mAh/g after100 cycles at 100 mA/g. After 600 cycles at 1 A/g, the discharge capacity was maintained at 828.1 mAh/g.Moreover, even though the charge/discharge rates were increased to 10 A/g, it rendered reversible capacity of 491.2 mAh/g. The superior electrochemical properties of nanocomposites were probably ascribed to their unique 3D architecture and the synergistic effects of two active materials. Therefore, such CoO/CoVO/Ni nanocomposites could potentially be used as anode materials for high-performance Li-ion batteries.展开更多
A novel three dimensional fluorinated gallium phosphate has been hydrothermally synthesized by using diethylenetriamine as an organic structure directing agent. X ray single crystal structure analysis indicates this c...A novel three dimensional fluorinated gallium phosphate has been hydrothermally synthesized by using diethylenetriamine as an organic structure directing agent. X ray single crystal structure analysis indicates this compound crystallizes in the orthorhombic space group Pbca, a =1.605 6(7) nm, b = 1 011 4 (4) nm, c =1.854 6(5) nm, V =3.011 6(19) nm 3, Z =4. The three dimensional framework based on linkage of corner sharing polyhedron PO 4, GaO 4F and GaO 4F 2 delimit ten ring channels along b axis in which the triply protonated amines are located serving as charge compensating guests and supporters.展开更多
A new compound, \[Ni(en)\-3\]\-2\[Ni(en)\-2(H\-2O)\-2\]\[As\-6V\-\{15\}O\-\{42\}\]·4H\-2O, was first prepared by hydrothermal synthesis and characterized by elemental analysis, IR, TGA\|DSC, ESR and single crysta...A new compound, \[Ni(en)\-3\]\-2\[Ni(en)\-2(H\-2O)\-2\]\[As\-6V\-\{15\}O\-\{42\}\]·4H\-2O, was first prepared by hydrothermal synthesis and characterized by elemental analysis, IR, TGA\|DSC, ESR and single crystal X\|ray diffraction. Crystal data: monoclinic, space group \%C\-c, a\%=1\^523 6(3) nm, \%b\%=2\^051 8(4) nm, \%c\%=2\^395 9(5) nm, \%β=97\^41(3)°, V\%=7\^427(3) nm\+3, \%Z=4, R=0\^057 0, wR\-2=0\^135 7\%. The polyanion consists of six AsO\-3 pyramids and fifteen VO\-5 pyramids. Counterions are complex ions with octahedral structure, which consist of NH\-2CH\-2CH\-2NH\-2 and Ni\+\{2+\}.展开更多
A\} novel two-dimensional coordination polymer Zn 3(PTC) 2(H 2O) 8·4H 2O was formed by \{Zn(CH 3COO) 2·\}2H 2O and 2-pyridine-1,3,5-tricarboxylate(H 3PTC) under the hydrothermal condition at 417 K and charac...A\} novel two-dimensional coordination polymer Zn 3(PTC) 2(H 2O) 8·4H 2O was formed by \{Zn(CH 3COO) 2·\}2H 2O and 2-pyridine-1,3,5-tricarboxylate(H 3PTC) under the hydrothermal condition at 417 K and characterized by fluorescence. The crystal structure of the compound was determined by single-crystal X-ray diffraction analyses. The six-coordinated Zinc(Ⅱ) center displays an octahedral geometry . The crystal is monoclinic and space group is P2(1)/c with a=0.722 70(14) nm, b= 1.866 7(4) nm , \{c=\}1.072 6(3) nm, α=90°, β=103.198(19)°, γ=90°, V=1.408 7(6) nm 3, Z=4, D c= 2.474 Mg/m 3, M r=828.536, μ=3.099 mm -1 , F(000)=1 060, GOF=0.892, R=0.061 3, wR= 0.133 9 .展开更多
文摘A new two dimensional 8 ring network nickle phosphate Ni 3(PO 4) 2·8H 2O was synthesized hydrothermally and its structure was determined by means of single crystal X ray diffraction. The Ni 3(PO 4) 2·8H 2O crystal crystallizes in the monoclinic system, space group C2/m , with M=128.13, a =0\^994 7(2) nm, b =1.321 7(3) nm; c =0.463 6(1) nm; β=104.80(3)°, V =0.589 3(2) nm 3, Z=2, R=0.027 2 and wR =0.057 5. The network structure consists of vertex sharing which results in the formation of undulating 4 ring chains and 8 ring sheets.
文摘The novel polyoxometalate, 32[Mo8ⅣMo4ⅤV2ⅣO38(PO4)], was synthesized and characterized by elementary analysis, EPR, IR spectra and X ray diffraction. The compoundcrystallizes in triclinic system, space group with a= 1.41999(2)nm, b=1.43467(2)nm, c=1.694610(10)nm, α=95.7250(10)°, β=92.2110(10)°, γ=92.6060(10)°, V=3.42829(7)nm3, Z=2, Dc=2.388g·cm-3, Mr=2465.10g·mol-1, μ=2.489mm-1, F(000)=2388, R1=0.0584, wR2=0.1461, S=1.164. The heteropolyanion is a bi capped pseudo Keggin complex. CCDC: 186645.
文摘A new compound 2 6[Co(H 2O) 2(VO) 8(OH) 4(PO 4) 8] has been hydrothermally synthesized. Single crystal X-ray analysis indicates that this compound crystallizes in a monoclinic system, space group P2 1/n with a=1.438 5(3) nm, b=1.012 2(2) nm, c=1.832 5(4) nm, β=90.21°, V=2\^668 2(9) nm 3, Z=2, D c=2.112 g/cm 3, R=0.055, wR=0.149 7, S=1.037. The structure of 2 6[Co(H 2O) 2(VO) 8(OH) 4(PO 4) 8] is characterized by P-V-O layers constructed by [(VO) 4(OH) 2(PO 4) 4] 6- non-symmetric units. The P-V-O layers are pillared by [Co(H 2O) 2] 2+ group, resulting in the channels within which the protonated diaminoethane and H 3O + are located.
基金supported by the National Natural Science Foundation of China(no.51362018)the Foundation for Innovation Groups of Basic Research in Gansu Province(no.1606RJIA322)
文摘The CoO/CoVO/Ni nanocomposites were rationally designed and prepared by a two-step hydrothermal synthesis and subsequent annealing treatment. The one-dimensional（1D） CoOnanowire arrays directly grew on Ni foam, whereas the 1D CoVOnanowires adhered to parts of CoOnanowires.Most of the hybrid nanowires were inlayed with each other, forming a 3D hybrid nanowires network.As a result, the discharge capacity of CoO/CoVO/Ni nanocomposites could reach 1201.8 mAh/g after100 cycles at 100 mA/g. After 600 cycles at 1 A/g, the discharge capacity was maintained at 828.1 mAh/g.Moreover, even though the charge/discharge rates were increased to 10 A/g, it rendered reversible capacity of 491.2 mAh/g. The superior electrochemical properties of nanocomposites were probably ascribed to their unique 3D architecture and the synergistic effects of two active materials. Therefore, such CoO/CoVO/Ni nanocomposites could potentially be used as anode materials for high-performance Li-ion batteries.
基金supported by the Fund for Young Scientists of Sichuan University, China (2011SCU11081)Research Fund for the Doctoral Program of Higher Education, Ministry of Education of China (20120181120103)~~
文摘A novel three dimensional fluorinated gallium phosphate has been hydrothermally synthesized by using diethylenetriamine as an organic structure directing agent. X ray single crystal structure analysis indicates this compound crystallizes in the orthorhombic space group Pbca, a =1.605 6(7) nm, b = 1 011 4 (4) nm, c =1.854 6(5) nm, V =3.011 6(19) nm 3, Z =4. The three dimensional framework based on linkage of corner sharing polyhedron PO 4, GaO 4F and GaO 4F 2 delimit ten ring channels along b axis in which the triply protonated amines are located serving as charge compensating guests and supporters.
文摘A new compound, \[Ni(en)\-3\]\-2\[Ni(en)\-2(H\-2O)\-2\]\[As\-6V\-\{15\}O\-\{42\}\]·4H\-2O, was first prepared by hydrothermal synthesis and characterized by elemental analysis, IR, TGA\|DSC, ESR and single crystal X\|ray diffraction. Crystal data: monoclinic, space group \%C\-c, a\%=1\^523 6(3) nm, \%b\%=2\^051 8(4) nm, \%c\%=2\^395 9(5) nm, \%β=97\^41(3)°, V\%=7\^427(3) nm\+3, \%Z=4, R=0\^057 0, wR\-2=0\^135 7\%. The polyanion consists of six AsO\-3 pyramids and fifteen VO\-5 pyramids. Counterions are complex ions with octahedral structure, which consist of NH\-2CH\-2CH\-2NH\-2 and Ni\+\{2+\}.
文摘A\} novel two-dimensional coordination polymer Zn 3(PTC) 2(H 2O) 8·4H 2O was formed by \{Zn(CH 3COO) 2·\}2H 2O and 2-pyridine-1,3,5-tricarboxylate(H 3PTC) under the hydrothermal condition at 417 K and characterized by fluorescence. The crystal structure of the compound was determined by single-crystal X-ray diffraction analyses. The six-coordinated Zinc(Ⅱ) center displays an octahedral geometry . The crystal is monoclinic and space group is P2(1)/c with a=0.722 70(14) nm, b= 1.866 7(4) nm , \{c=\}1.072 6(3) nm, α=90°, β=103.198(19)°, γ=90°, V=1.408 7(6) nm 3, Z=4, D c= 2.474 Mg/m 3, M r=828.536, μ=3.099 mm -1 , F(000)=1 060, GOF=0.892, R=0.061 3, wR= 0.133 9 .