研究了经热等静压处理后定向凝固 Ni Al/Cr(Mo,Hf)合金中的沉淀相和高温拉伸性能的变化。通过透射电镜和扫描电镜观察发现 :热等静压处理后 ,Ni Al和 Cr(Mo)相的形貌变化不大 ,聚集在 Ni Al/Cr(Mo)相界上的 Heusler减少并在 Ni Al,Cr(Mo...研究了经热等静压处理后定向凝固 Ni Al/Cr(Mo,Hf)合金中的沉淀相和高温拉伸性能的变化。通过透射电镜和扫描电镜观察发现 :热等静压处理后 ,Ni Al和 Cr(Mo)相的形貌变化不大 ,聚集在 Ni Al/Cr(Mo)相界上的 Heusler减少并在 Ni Al,Cr(Mo)相中重新分布。从界面能的角度解释了 Heusler相主要沉淀在Ni Al/Cr(Mo)相界上的原因。热等静压处理后合金中不存在 G相。展开更多
A multiphase NiAl-28Cr-5.85Mo-0.15Hf alloy, which was directionally solidified （DS） in an Al2O3-SiO2 mold by standard Bridgman method and then underwent prolonged solution and aging treatment was prepared. The micro...A multiphase NiAl-28Cr-5.85Mo-0.15Hf alloy, which was directionally solidified （DS） in an Al2O3-SiO2 mold by standard Bridgman method and then underwent prolonged solution and aging treatment was prepared. The microstructure, tensile properties as well as tensile creep of the heat-treated alloy at different temperatures were studied. The alloy was composed of NiAI, Cr（Mo） and Hf-rich phase and small amount of fine Heusler phase （Ni2AlHf）. Although the present alloy exhibited high tensile strength at low temperature, it was weaker than that of system with high content Hf but still stronger than that of many NiAl-based alloys at high temperatures. The fracture toughness is lower than that of DS NiAl-28Cr-6Mo alloy. Nevertheless, advantageous effects on the mechanical properties, i.e. the decrease in brittle-to-ductile transition temperature （BDTT） were obtained for the low content of Hf. The obtained creep curves exhibit conventional shape： a short primary creep and long accelerated creep stages. The rupture properties of the heat-treated alloy follow the Monkman-Grant relationship, which exhibits similar creep behavior to that of NiAl/Cr（Mo） system with high Hf content.展开更多
A suitable combustion synthesis and densification process was designed to fabricate dense NiAl/ TiB2 composites from Ni-Al- Ti-B system. Combustion synthesis processing and microstructure characteristics of products w...A suitable combustion synthesis and densification process was designed to fabricate dense NiAl/ TiB2 composites from Ni-Al- Ti-B system. Combustion synthesis processing and microstructure characteristics of products were studied in detail. The results show that the amount of TiB2 ceramics has a great influence on the combustion synthesis processing and microstructure; with the increase of the amount of TiB2 ceramics, the combustion temperature and combustion velocity increase rapidly. The volume of synthesized products and the grain size of ceramics particle size are also affected by the amount of TiB2 ceramics. TiB2 ceramics fiber can be produced in this synthesis system. The dense NiAl/ TiB2 composites with residual porosity of no more than 1% are fabricated by the combustion synthesis and hot pressing, the mechanical properties of the dense NiAl/ TiB2 composites increase with increase of the amount of TiB2 ceramics.展开更多
A NiAl/TiB2 nanocomposite is synthesized by mechanical alloying elemental powders. Upon milling for a certain time, an abrupt exothermic reaction occurs and a large amount of NiAl and TiB2 compounds form simultaneousl...A NiAl/TiB2 nanocomposite is synthesized by mechanical alloying elemental powders. Upon milling for a certain time, an abrupt exothermic reaction occurs and a large amount of NiAl and TiB2 compounds form simultaneously. It is suggested that two separate chemical reactions,i.e. Ni+Al →NiAl and Ti+2B→TiB2, are involved during the exothermic reaction. Additionof Ti and B to Ni-Al system impedes the structural evolution of Ni and Al powders and delays the abrupt reaction. The final products are equilibrium phases without any metastable phases formed. This type of reaction is suggested to be suitable for alloy systems with two large heatrelease reactions.展开更多
NiAl/Al2O3 composite were synthesized by thermite reaction of nickel oxide and aluminum powder mixtures.The phase,the microstructure of the composite,as well as the thermite reaction mechanism,were investigated by X-r...NiAl/Al2O3 composite were synthesized by thermite reaction of nickel oxide and aluminum powder mixtures.The phase,the microstructure of the composite,as well as the thermite reaction mechanism,were investigated by X-ray diffractomety（XRD0,scanning electron microscopy（SEM） combined with differential scanning calorimetry（DSC）.The experimental results show that the thermite reaction leads to the interpenetrating network structure of NiAl/Al2O3 at 1223K for 60min and the chemical reaction apparent activation energy is Eap=166.960±13.496kJ·mol^-1 in the NiO/Al system.展开更多
文摘A multiphase NiAl-28Cr-5.85Mo-0.15Hf alloy, which was directionally solidified （DS） in an Al2O3-SiO2 mold by standard Bridgman method and then underwent prolonged solution and aging treatment was prepared. The microstructure, tensile properties as well as tensile creep of the heat-treated alloy at different temperatures were studied. The alloy was composed of NiAI, Cr（Mo） and Hf-rich phase and small amount of fine Heusler phase （Ni2AlHf）. Although the present alloy exhibited high tensile strength at low temperature, it was weaker than that of system with high content Hf but still stronger than that of many NiAl-based alloys at high temperatures. The fracture toughness is lower than that of DS NiAl-28Cr-6Mo alloy. Nevertheless, advantageous effects on the mechanical properties, i.e. the decrease in brittle-to-ductile transition temperature （BDTT） were obtained for the low content of Hf. The obtained creep curves exhibit conventional shape： a short primary creep and long accelerated creep stages. The rupture properties of the heat-treated alloy follow the Monkman-Grant relationship, which exhibits similar creep behavior to that of NiAl/Cr（Mo） system with high Hf content.
文摘A suitable combustion synthesis and densification process was designed to fabricate dense NiAl/ TiB2 composites from Ni-Al- Ti-B system. Combustion synthesis processing and microstructure characteristics of products were studied in detail. The results show that the amount of TiB2 ceramics has a great influence on the combustion synthesis processing and microstructure; with the increase of the amount of TiB2 ceramics, the combustion temperature and combustion velocity increase rapidly. The volume of synthesized products and the grain size of ceramics particle size are also affected by the amount of TiB2 ceramics. TiB2 ceramics fiber can be produced in this synthesis system. The dense NiAl/ TiB2 composites with residual porosity of no more than 1% are fabricated by the combustion synthesis and hot pressing, the mechanical properties of the dense NiAl/ TiB2 composites increase with increase of the amount of TiB2 ceramics.
文摘A NiAl/TiB2 nanocomposite is synthesized by mechanical alloying elemental powders. Upon milling for a certain time, an abrupt exothermic reaction occurs and a large amount of NiAl and TiB2 compounds form simultaneously. It is suggested that two separate chemical reactions,i.e. Ni+Al →NiAl and Ti+2B→TiB2, are involved during the exothermic reaction. Additionof Ti and B to Ni-Al system impedes the structural evolution of Ni and Al powders and delays the abrupt reaction. The final products are equilibrium phases without any metastable phases formed. This type of reaction is suggested to be suitable for alloy systems with two large heatrelease reactions.
文摘NiAl/Al2O3 composite were synthesized by thermite reaction of nickel oxide and aluminum powder mixtures.The phase,the microstructure of the composite,as well as the thermite reaction mechanism,were investigated by X-ray diffractomety（XRD0,scanning electron microscopy（SEM） combined with differential scanning calorimetry（DSC）.The experimental results show that the thermite reaction leads to the interpenetrating network structure of NiAl/Al2O3 at 1223K for 60min and the chemical reaction apparent activation energy is Eap=166.960±13.496kJ·mol^-1 in the NiO/Al system.