Microstructure,phase transformation and mechanical properties of NiMnGa particles/Cu composites prepared by spark plasma sintering method were investigated by SEM,EDS,XRD,susceptibility measurements and mechanical tes...Microstructure,phase transformation and mechanical properties of NiMnGa particles/Cu composites prepared by spark plasma sintering method were investigated by SEM,EDS,XRD,susceptibility measurements and mechanical tests.The NiMnGa particles were found to react with Cu matrix and the composites exhibited a similar crystal structure to the Cu matrix.The martensitic transformation and Curie transition of the composites were weakened due to the composition change of NiMnGa particles caused by reactions.With increasing NiMnGa particles content,the martensitic transformation and Curie transition of the composites were enhanced to some extent.However,the martensitic transformation temperature and Curie transition temperature were decreased by~50 K as compared to those of the original NiMnGa particles.The compressive strength of the composites increased with the increase of NiMnGa particles content,whereas the compressive strain was decreased gradually.展开更多
基金supported by the National Natural Science Foundation of China(No.51201044)High-level Scientific Research Guidance Project of Harbin Engineering University,China(No.3072022TS1006)+1 种基金Postdoctoral Scientific Research Developmental Fund of Heilongjiang Province,China(No.LBH-Q16046)Key Laboratory of Superlight Materials&Surface Technology(Harbin Engineering University),Ministry of Education,China.
文摘Microstructure,phase transformation and mechanical properties of NiMnGa particles/Cu composites prepared by spark plasma sintering method were investigated by SEM,EDS,XRD,susceptibility measurements and mechanical tests.The NiMnGa particles were found to react with Cu matrix and the composites exhibited a similar crystal structure to the Cu matrix.The martensitic transformation and Curie transition of the composites were weakened due to the composition change of NiMnGa particles caused by reactions.With increasing NiMnGa particles content,the martensitic transformation and Curie transition of the composites were enhanced to some extent.However,the martensitic transformation temperature and Curie transition temperature were decreased by~50 K as compared to those of the original NiMnGa particles.The compressive strength of the composites increased with the increase of NiMnGa particles content,whereas the compressive strain was decreased gradually.