Simulation research on heat-affected zone of the NiTi alloy plasma arc welded joints

In order to study the compositions and properties of NiTi alloy plasma arc welded joints, different temperatures of the heat-affected zone（HAZ） are simulated. Temperatures are set at 20 ℃, 400 ℃, 500 ℃, 600 ℃, 700 ℃, 800 ℃, 900 ℃ and 1 000 ℃. X-ray diffraction results of the thermal simulated specimens show that NiTi2 phase emerges in the alloy when the temperature is between 500 ℃ and 800 ℃, while NiTi2 and Ni3 Ti phases emerge when the temperature is between 800 ℃ and 1 000 ℃. Tensile strengths of specimens at 600 ℃ and 900 ℃ are only 68. 0% and 61.3% of the strength at the room temperature respectively due to the emergence of NiTi2 and Ni3 Ti phases.

等离子弧堆焊TiC增强NiTi合金的组织和耐磨性

利用等离子弧堆焊方法在Q235钢板表面制备了添加TiC颗粒的NiTi合金耐磨堆焊层,并对堆焊层的微观组织和耐磨性进行研究。结果表明,在湿砂橡胶轮磨粒磨损试验条件下,当TiC加入量为55%时堆焊层的相对耐磨性最好,为Q235钢的11倍。TiC含量为55%的堆焊层由TiC、Ni3Ti及NiTi组成,堆焊层组织致密、与基材之间结合良好。堆焊层具有优异耐磨性的主要原因是TiC和Ni3Ti具有高硬度高耐磨性,起到抗磨骨架作用,而NiTi对TiC和Ni3Ti起到了支撑作用。堆焊层的磨损机制主要为塑性切削和硬质相的脆性剥落。

高纯难熔金属及其合金单晶的发展

介绍了难熔金属及其合金单晶的制备技术,对电子束悬浮区域熔炼技术和等离子弧熔炼技术进行了比较。电子束悬浮区域熔炼法温度梯度易于控制、材料不受坩埚材料污染,但熔体表面张力对活性杂质和温度梯度敏感性高,所能制备的高纯难熔金属及其单晶材料尺寸规格受到很大限制,且材料内部位错密度较高。等离子弧熔炼法加热源能量密度高,原料规格形式多样,可制备单晶棒材、板材、管材及其他特定形状的单晶铸件,可最大程度地去除杂质元素(尤其是C元素),但设备系统复杂,单晶材料位错密度大。讨论了单晶材料发展现状,通过固溶强化可进一步提高材料的高温性能及其稳定性。单晶管材的制备也是一个发展方向。此外还对单晶材料制备技术和发展前景提出了一些建议。