The present work aims to investigate the recovery of light rare earth elements(LREEs) oxides from end-oflife NiMH batteries using a hydro metallurgical process followed by effective precipitation.The operational leach...The present work aims to investigate the recovery of light rare earth elements(LREEs) oxides from end-oflife NiMH batteries using a hydro metallurgical process followed by effective precipitation.The operational leaching parameters such as phosphoric acid concentration,temperature,and the solid-liquid ratio were first optimized by Box-Behnken design.The results reveal that under optimum conditions([H_(3)PO_(4)]=2 mol/L,T=80℃,and S/L=1:10 g/mL) the leaching efficiencies of Ni,Co reach 98.1% and99.3%.While La,Ce,and Nd elements remain in the leaching residue as(La,Ce,Nd)PO_(4) with yields of 98.2%,98.6%,and 99.6% for La,Ce,and Nd,respectively.Afterward,the(La,Ce,Nd)PO_(4) is leached with HCl acid,then the rare earth oxalate was precipitated using oxalic acid at a pH of 1.8 and then the product was calcined at 800℃ for 2 h in order to synthesize the(Nd,La,Ce)_(2)O_(3).The analysis using scanning electron microscopy(SEM) coupled with energy dispersive X-ray spectroscopy(EDX) confirms the homogeneity of(Nd,La,Ce)_(2)O_(3) particles that have two morphologies,i.e.,flower and sticks with a particle size between 3and 6 μm.The unit cell parameters of(Nd,La,Ce)_(2)O_(3) were calculated after Rietveld refinement of the XRD patterns,in the space group of Fm-3m are a=b=c=0.57921 nm and the volume equal to 0.194322 nm^(3).展开更多
Fundamental physical and (electro) chemical principles of rechargeable battery operation form the basis of the electronic network models developed for Nickel-based aqueous battery systems, including Nickel Metal Hydri...Fundamental physical and (electro) chemical principles of rechargeable battery operation form the basis of the electronic network models developed for Nickel-based aqueous battery systems, including Nickel Metal Hydride (NiMH), and non-aqueous battery systems, such as the well-known Li-ion. Refined equivalent network circuits for both systems represent the main contribution of this paper. These electronic network models describe the behavior of batteries during normal operation and during over (dis) charging in the case of the aqueous battery systems. This makes it possible to visualize the various reaction pathways, including convention and pulse (dis) charge behavior and for example, the self-discharge performance.展开更多
文摘The present work aims to investigate the recovery of light rare earth elements(LREEs) oxides from end-oflife NiMH batteries using a hydro metallurgical process followed by effective precipitation.The operational leaching parameters such as phosphoric acid concentration,temperature,and the solid-liquid ratio were first optimized by Box-Behnken design.The results reveal that under optimum conditions([H_(3)PO_(4)]=2 mol/L,T=80℃,and S/L=1:10 g/mL) the leaching efficiencies of Ni,Co reach 98.1% and99.3%.While La,Ce,and Nd elements remain in the leaching residue as(La,Ce,Nd)PO_(4) with yields of 98.2%,98.6%,and 99.6% for La,Ce,and Nd,respectively.Afterward,the(La,Ce,Nd)PO_(4) is leached with HCl acid,then the rare earth oxalate was precipitated using oxalic acid at a pH of 1.8 and then the product was calcined at 800℃ for 2 h in order to synthesize the(Nd,La,Ce)_(2)O_(3).The analysis using scanning electron microscopy(SEM) coupled with energy dispersive X-ray spectroscopy(EDX) confirms the homogeneity of(Nd,La,Ce)_(2)O_(3) particles that have two morphologies,i.e.,flower and sticks with a particle size between 3and 6 μm.The unit cell parameters of(Nd,La,Ce)_(2)O_(3) were calculated after Rietveld refinement of the XRD patterns,in the space group of Fm-3m are a=b=c=0.57921 nm and the volume equal to 0.194322 nm^(3).
文摘Fundamental physical and (electro) chemical principles of rechargeable battery operation form the basis of the electronic network models developed for Nickel-based aqueous battery systems, including Nickel Metal Hydride (NiMH), and non-aqueous battery systems, such as the well-known Li-ion. Refined equivalent network circuits for both systems represent the main contribution of this paper. These electronic network models describe the behavior of batteries during normal operation and during over (dis) charging in the case of the aqueous battery systems. This makes it possible to visualize the various reaction pathways, including convention and pulse (dis) charge behavior and for example, the self-discharge performance.