In traditional electroforming process for revolving parts with complex profiles, the drawbacks on surface of deposits, such as pinholes and nodules, will lead to varying physical and mechanical properties on different...In traditional electroforming process for revolving parts with complex profiles, the drawbacks on surface of deposits, such as pinholes and nodules, will lead to varying physical and mechanical properties on different parts of electroformed components. To solve the problem, compositely moving cathode is employed in abrasive-assisted electroforming of revolving parts with complicated profiles. The cathode translates and rotates simultaneously to achieve uniform friction effect on deposits without drawbacks. The influences of current density and transla- tion speed on the microstructure and properties of the electroformed nickel layers are investigated. It is found that abrasive-assisted electroforming with compound cathode motion can effectively remove the pinholes and nodules, positively affect the crystal nucleation, and refine the grains of layer. The increase of current density will lead to coarse microstructure and lower micro hardness, from 325 HV down to 189 HV. While, faster translational linear speed produces better surface quality and higher micro hardness, from 236 HV up to 283 HV. The weld-ability of the electroformed layers are also studied through the metallurgical analysis of welded joints between nickel layer and 304 stainless steel. The electrodeposited nickel layer shows fine performance in welding. The novel compound motion of cathode promotes the mechanical properties and refines the microstructure of deposited layer.展开更多
A cathode mandrel with translational and rotational motion, which was supposed to obtain uniform friction effect on surface, was employed in abrasive-assisted electroforming for revolving parts with complex profile. T...A cathode mandrel with translational and rotational motion, which was supposed to obtain uniform friction effect on surface, was employed in abrasive-assisted electroforming for revolving parts with complex profile. The effects of current density, translational speed and rotational speed on the deposit properties were studied by orthogonal test. The tensile strength,elongation and micro hardness value were measured to find out how the factors affected the properties. The optimized results show that changes of current density affect the tensile strength of nickel layer most, while translational speed has the most remarkable influences on both elongation and micro hardness. The low rotational speed affects the properties least. In this experiment, a smooth nickel layer with tensile strength 581 MPa, elongation 17% and micro hardness 248 HV is obtained by the orthogonal test.展开更多
基金Supported by National Natural Science Foundation of China(Grant No.51475239)Program for New Century Excellent Talents in University of China(Grand No.NCET-10-0074)
文摘In traditional electroforming process for revolving parts with complex profiles, the drawbacks on surface of deposits, such as pinholes and nodules, will lead to varying physical and mechanical properties on different parts of electroformed components. To solve the problem, compositely moving cathode is employed in abrasive-assisted electroforming of revolving parts with complicated profiles. The cathode translates and rotates simultaneously to achieve uniform friction effect on deposits without drawbacks. The influences of current density and transla- tion speed on the microstructure and properties of the electroformed nickel layers are investigated. It is found that abrasive-assisted electroforming with compound cathode motion can effectively remove the pinholes and nodules, positively affect the crystal nucleation, and refine the grains of layer. The increase of current density will lead to coarse microstructure and lower micro hardness, from 325 HV down to 189 HV. While, faster translational linear speed produces better surface quality and higher micro hardness, from 236 HV up to 283 HV. The weld-ability of the electroformed layers are also studied through the metallurgical analysis of welded joints between nickel layer and 304 stainless steel. The electrodeposited nickel layer shows fine performance in welding. The novel compound motion of cathode promotes the mechanical properties and refines the microstructure of deposited layer.
基金financial support from the Program for New Century Excellent Talents in University of China (No. NCET-10-0074)
文摘A cathode mandrel with translational and rotational motion, which was supposed to obtain uniform friction effect on surface, was employed in abrasive-assisted electroforming for revolving parts with complex profile. The effects of current density, translational speed and rotational speed on the deposit properties were studied by orthogonal test. The tensile strength,elongation and micro hardness value were measured to find out how the factors affected the properties. The optimized results show that changes of current density affect the tensile strength of nickel layer most, while translational speed has the most remarkable influences on both elongation and micro hardness. The low rotational speed affects the properties least. In this experiment, a smooth nickel layer with tensile strength 581 MPa, elongation 17% and micro hardness 248 HV is obtained by the orthogonal test.