Oxide scale formation on a C-steel surface has been investigated using linear heating rates ranging from 0.1℃/min to 10℃/min at high temperatures. The studies on the oxide scale formation at high temperature (650℃)...Oxide scale formation on a C-steel surface has been investigated using linear heating rates ranging from 0.1℃/min to 10℃/min at high temperatures. The studies on the oxide scale formation at high temperature (650℃) at slower heating rate (0.1℃/min) shows that the kinetic regime is linear. X-ray diffraction measurements revealed that the scale constituents are significantly influenced by the heating rate. The adherence of the scale was improved by using slower heating rate (0.1℃/min-≤650℃), while above such degree the scale was susceptible to cracking and flaking out of the alloy surface. In fact, the development of oxide growth stresses can cause considerable scale cracking. As well, variation of the crystallite sizes under the aforementioned conditions might affect the scale stacking to the alloy surface. The secondary electron detector images of the oxide scale shows that the scale was imperfectly smooth and there were a number of voids and defects in the scale skin, especially at fast heating rate. This observation could be attributed to defects of the as-received alloy. In general, slower heating rate reduced the defects of the scale and improved its adherence.展开更多
The in situ direct-current conductance behaviors of Cu/C_(60) nano-scale granular films have been investigated experimentally.The results show that the incorporation of Cu into Ceo greatly increases the conductance of...The in situ direct-current conductance behaviors of Cu/C_(60) nano-scale granular films have been investigated experimentally.The results show that the incorporation of Cu into Ceo greatly increases the conductance of the film.The orientational phase transition that exists in pure C_(60) single crystals still retains in the Cu/C_(60) co-evaporated Elms,while the transition temperature range is significantly widened.The interactions between the nano-scale Cu clusters and C_(60) grains are discussed.展开更多
The longitude tensile properties of 3-Dimension-4-directional（3D-4d） braided C/Si C composites（CMCs） were investigated with the help of a double scale model. This model involves micro-scale and unit-cell scale. In...The longitude tensile properties of 3-Dimension-4-directional（3D-4d） braided C/Si C composites（CMCs） were investigated with the help of a double scale model. This model involves micro-scale and unit-cell scale. In micro-scale, the tensile properties of fiber tows which involves matrix cracking, interfacial debonding, and fiber failure are studied. The unit-cell scale model can reflect the braided structure and simulate the tensile properties of 3D-4d CMCs by introducing the tensile properties of fiber tows into it. Quasi-static tensile tests of 3D-4d braided CMCs were performed on a PWS-100 test system. The predicted tensile stressstrain curve by the double scale model is in good agreement with that of the experimental results.展开更多
[ Objective] This study aimed to explore the effect of C/N ratio on DHA production by Schizochytrium sp. , and the results were verified by pilot-scale fermentation. [ Method] Effect of C/N ratio on DHA production by ...[ Objective] This study aimed to explore the effect of C/N ratio on DHA production by Schizochytrium sp. , and the results were verified by pilot-scale fermentation. [ Method] Effect of C/N ratio on DHA production by Schizochytrium sp. JN-3 was explored. The industrial fermentation potential of Schizochytrium sp. JN-3 was investigated by pilot-scale fermentation in a 200 L fermentation tank. [ Result] Results of fermentation in a 7 L fermentation tank showed that the maximum biomass and total lipid content were 34.3 and 20.1 g/L, respectively, when C/N ratio was 10 ; the maximum DHA yield was 46.9% when C/N ratio was 20. When pilot-scale fermentation was conducted in a 200 L fermentation tank, the biomass was 30. 2 g/L, total lipid content was 18.4 g/L, accounting for 63.2% of the dry weight of cells; DHA content was 7.4 g/L, accounting for 40. 2% of the total lipid content. [ Condasion ] Schizochytrlum sp. JN-3 has good industrial fermentation notential.展开更多
Double-scale model for three-dimension-4 directional（3D-4d） braided C/SiC composites has been proposed to investigate its elastic properties. The double-scale model involves micro-scale that takes fiber/ matrix/poro...Double-scale model for three-dimension-4 directional（3D-4d） braided C/SiC composites has been proposed to investigate its elastic properties. The double-scale model involves micro-scale that takes fiber/ matrix/porosity in fibers tows into consideration with unit cell which considers the 3D-4d braiding structure. Micro-optical photographs of composites have been taken to study the braided structure. Then a parameterized finite element model that reflects the structure of 3D-4d braided composites is proposed. Double-scale elastic modulus prediction model is developed to predict the elastic properties of 3D-4d braided C/SiC composites. Stiffness and eompliance-averaging method and energy method are adopted to predict the elastic properties of composites. Static-tension experiments have been conducted to investigate the elastic modulus of 3D-4d braided C/SiC composites. Finally, the effect of micro-porosity in fibers tows on the elastic modulus of 3D-4d braided C/SiC composites has been studied. According to the conclusion of this thesis, elastic modulus predicted by energy method and stiffness-averaging method both find good agreement with the experimental values, when taking the micro-porosity in fibers tows into consideration. Differences between the theoretical and experimental values become smaller.展开更多
针对液晶显示器(LCD)面板的“Chip/FPC on Glass”(C/FOG)工艺生产制造过程中存在的计量延迟大、生产异常无法提前预测的问题,本文提出一种基于神经网络的C/FOG工艺生产制造虚拟计量方法。该方法利用生产机台上的传感器采集生产过程中...针对液晶显示器(LCD)面板的“Chip/FPC on Glass”(C/FOG)工艺生产制造过程中存在的计量延迟大、生产异常无法提前预测的问题,本文提出一种基于神经网络的C/FOG工艺生产制造虚拟计量方法。该方法利用生产机台上的传感器采集生产过程中的过程状态数据,构建基于多尺度一维卷积及通道注意力模型(MS1DC-CA)的虚拟计量模型。通过多个尺度的卷积核提取不同尺度范围内的状态数据特征。在对含有缺失值的原始数据预处理中,提出了基于粒子群算法改进的K近邻填补方法(PSO-KNN Imputation)进行缺失值填充,保留特征的同时,减少因填充值引入的干扰。最后在实际生产采集的数据上进行实验对比分析,实际不良率主要集中在0.1%~0.5%,该虚拟计量模型的拟合均方误差为0.397 7‱,低于其他现有拟合模型,在平均绝对误差、对称平均绝对百分比误差和拟合优度3种评价指标下也均优于其他现有的拟合模型,具有良好的预测性能。展开更多
文摘Oxide scale formation on a C-steel surface has been investigated using linear heating rates ranging from 0.1℃/min to 10℃/min at high temperatures. The studies on the oxide scale formation at high temperature (650℃) at slower heating rate (0.1℃/min) shows that the kinetic regime is linear. X-ray diffraction measurements revealed that the scale constituents are significantly influenced by the heating rate. The adherence of the scale was improved by using slower heating rate (0.1℃/min-≤650℃), while above such degree the scale was susceptible to cracking and flaking out of the alloy surface. In fact, the development of oxide growth stresses can cause considerable scale cracking. As well, variation of the crystallite sizes under the aforementioned conditions might affect the scale stacking to the alloy surface. The secondary electron detector images of the oxide scale shows that the scale was imperfectly smooth and there were a number of voids and defects in the scale skin, especially at fast heating rate. This observation could be attributed to defects of the as-received alloy. In general, slower heating rate reduced the defects of the scale and improved its adherence.
基金Supported by the National Natural Science Foundation of China under Grant Nos.59529204 and 19734002.
文摘The in situ direct-current conductance behaviors of Cu/C_(60) nano-scale granular films have been investigated experimentally.The results show that the incorporation of Cu into Ceo greatly increases the conductance of the film.The orientational phase transition that exists in pure C_(60) single crystals still retains in the Cu/C_(60) co-evaporated Elms,while the transition temperature range is significantly widened.The interactions between the nano-scale Cu clusters and C_(60) grains are discussed.
基金Funded by the National Basic Research Program of Chinathe National Natural Science Foundation of China(51675266)+3 种基金the Aeronautical Science Foundation of China(2014ZB52024)the Fundamental Research Funds for the Central Universities(NJ20160038)the Jiangsu Innovation Program for Graduate Education(CXLX13_165)the Fundamental Research Funds for the Central Universities
文摘The longitude tensile properties of 3-Dimension-4-directional（3D-4d） braided C/Si C composites（CMCs） were investigated with the help of a double scale model. This model involves micro-scale and unit-cell scale. In micro-scale, the tensile properties of fiber tows which involves matrix cracking, interfacial debonding, and fiber failure are studied. The unit-cell scale model can reflect the braided structure and simulate the tensile properties of 3D-4d CMCs by introducing the tensile properties of fiber tows into it. Quasi-static tensile tests of 3D-4d braided CMCs were performed on a PWS-100 test system. The predicted tensile stressstrain curve by the double scale model is in good agreement with that of the experimental results.
基金Supported by Research Fund for the Doctoral Program of Ministry of Education(20100093120002)Open Project of the Key Laboratory of Industrial Biotechnology under Ministry of Education(KLIB-KF200906,KLIB-KF201005)
文摘[ Objective] This study aimed to explore the effect of C/N ratio on DHA production by Schizochytrium sp. , and the results were verified by pilot-scale fermentation. [ Method] Effect of C/N ratio on DHA production by Schizochytrium sp. JN-3 was explored. The industrial fermentation potential of Schizochytrium sp. JN-3 was investigated by pilot-scale fermentation in a 200 L fermentation tank. [ Result] Results of fermentation in a 7 L fermentation tank showed that the maximum biomass and total lipid content were 34.3 and 20.1 g/L, respectively, when C/N ratio was 10 ; the maximum DHA yield was 46.9% when C/N ratio was 20. When pilot-scale fermentation was conducted in a 200 L fermentation tank, the biomass was 30. 2 g/L, total lipid content was 18.4 g/L, accounting for 63.2% of the dry weight of cells; DHA content was 7.4 g/L, accounting for 40. 2% of the total lipid content. [ Condasion ] Schizochytrlum sp. JN-3 has good industrial fermentation notential.
基金Funded by the National Basic Research Program of China,National Natural Science Foundation of China(No.51075204)Funding of Jiangsu Innovation Program for Graduate Education(No.CXLX13_165)+2 种基金the Fundamental Research Funds for the Central Universities,Aeronautical Science Foundation of China(No.2012ZB52026)Research Fund for the Doctoral Program of Higher Education of China(No.20070287039)NUAA Research Funding(No.NZ2012106)
文摘Double-scale model for three-dimension-4 directional（3D-4d） braided C/SiC composites has been proposed to investigate its elastic properties. The double-scale model involves micro-scale that takes fiber/ matrix/porosity in fibers tows into consideration with unit cell which considers the 3D-4d braiding structure. Micro-optical photographs of composites have been taken to study the braided structure. Then a parameterized finite element model that reflects the structure of 3D-4d braided composites is proposed. Double-scale elastic modulus prediction model is developed to predict the elastic properties of 3D-4d braided C/SiC composites. Stiffness and eompliance-averaging method and energy method are adopted to predict the elastic properties of composites. Static-tension experiments have been conducted to investigate the elastic modulus of 3D-4d braided C/SiC composites. Finally, the effect of micro-porosity in fibers tows on the elastic modulus of 3D-4d braided C/SiC composites has been studied. According to the conclusion of this thesis, elastic modulus predicted by energy method and stiffness-averaging method both find good agreement with the experimental values, when taking the micro-porosity in fibers tows into consideration. Differences between the theoretical and experimental values become smaller.
文摘针对液晶显示器(LCD)面板的“Chip/FPC on Glass”(C/FOG)工艺生产制造过程中存在的计量延迟大、生产异常无法提前预测的问题,本文提出一种基于神经网络的C/FOG工艺生产制造虚拟计量方法。该方法利用生产机台上的传感器采集生产过程中的过程状态数据,构建基于多尺度一维卷积及通道注意力模型(MS1DC-CA)的虚拟计量模型。通过多个尺度的卷积核提取不同尺度范围内的状态数据特征。在对含有缺失值的原始数据预处理中,提出了基于粒子群算法改进的K近邻填补方法(PSO-KNN Imputation)进行缺失值填充,保留特征的同时,减少因填充值引入的干扰。最后在实际生产采集的数据上进行实验对比分析,实际不良率主要集中在0.1%~0.5%,该虚拟计量模型的拟合均方误差为0.397 7‱,低于其他现有拟合模型,在平均绝对误差、对称平均绝对百分比误差和拟合优度3种评价指标下也均优于其他现有的拟合模型,具有良好的预测性能。