Preparation of high-purity bismuth by sulphur deleadization in vacuum distillation

The feasibility of separation of impurities in refined bismuth and sulphur deleadization with vacuum distillation was studied theoretically. Experimental studies on sulphur deleadization were carried out under vacuum. The influences of amount of sulphur, distillation temperature, vacuum degree and distillation time on deleadization were investigated and an optimal technical condition was achieved. The content of lead in refined bismuth can be decreased from 30 μg/g to 0.21 μg/g, which has reached the level of “5N” high-purity bismuth. Other impurities in refined bismuth can be also removed effectively under certain conditions.

精铋的真空蒸馏硫化除铅

从理论上分析了用真空蒸馏分离精铋中各杂质和通过加硫除铅的可行性。在真空炉内进行了精铋加硫除铅的实验研究,考察了加硫量、蒸馏温度、残压和蒸馏时间以及加硫次数等因素对除铅效果的影响,得到了最佳工艺条件:每克铋加硫量控制在0.02 g左右、蒸馏温度约1073 K、残压控制在16 Pa左右,蒸馏时间不超过15 min。在此条件下可将金属铋中的杂质铅含量由30μg/g降到了0.21μg/g,达到了“5N”高纯铋的要求。良好的实验结果表明,精铋硫化除铅具有工艺流程简单、改善劳动环境及提高生产率等优点,是一种去除精铋中铅的有效方法。

无氧化阳极铜生产工艺研究与应用

利用冶金热力学和动力学原理,研究开发出“无氧化混合气(N2+LPG)带硫还原”新工艺,应用于金隆生产,创造了显著经济、环保和社会效益。

提高高硫易切削不锈钢热塑性的研究

采用电弧炉 +电渣重熔工艺生产高硫易切削不锈钢 ,在获得高硫 ( 0 2 5%± )的同时 ,硫化物形貌和分布情况得到明显改善 ,使材料热加工塑性提高 ,热脆开裂减少。由此开发的高硫易切削不锈钢丝取得了良好的经济效益。

加工中质高硫原油的新炼油厂设计理念及方案

大连长兴岛石化园区的建设为中国石油天然气集团公司大连石化分公司的进一步发展提供了新的机遇。新建炼油厂设计加工来自中东地区的中质高硫原油,API°为30.6,硫质量分数为2.67%。其重油加工设计以加氢路线为主,以脱碳路线为辅的方案,以增强原油适应能力。规划生产高附加值芳烃产品,高档润滑油基础油产品,汽柴油产品质量定位为欧V标准,充分利用C3,C4轻烃资源发展化工。采用重质原料进行POX制氢,充分回收炼油厂氢气资源,降低氢气成本,分析了与石化园区开展合作的意义及优势,项目具有较好的盈利能力。

石油炼制用阀门使用特性的分析

介绍了在石油炼制过程中不同装置所用阀门。随着石油炼制装置的不断更新及对石油提炼纯度高要求,阐述了高压力抗硫抗氢阀门在生产制造技术上的高要求及石油炼制用阀门的发展趋势。