The oxidation rate,the growth,morphology and structure of oxide scale and whiskers for Fe-Ni-Cr sealing alloys in H_2-H_2O atmosphere at high temperatures have been studied. The growth rate of scale is controlled by d...The oxidation rate,the growth,morphology and structure of oxide scale and whiskers for Fe-Ni-Cr sealing alloys in H_2-H_2O atmosphere at high temperatures have been studied. The growth rate of scale is controlled by diffusion.The scale is composed of Cr_2O_3 and spinel(Fe,Mn)O·Cr_2O_3 and the oxide whisker,are spinel(Fe,Mn)O·Cr_2O_3.展开更多
The growth.of oxide films on 476 alloy,with a small amount of additive elements such as Si etc.,oxidized in wet hydrogen atmosphere is some times accompanied by the formation of a great many whiskers.Typical form of w...The growth.of oxide films on 476 alloy,with a small amount of additive elements such as Si etc.,oxidized in wet hydrogen atmosphere is some times accompanied by the formation of a great many whiskers.Typical form of whiskers grown on the oxide film is of flag pole type with a globe on its top.The pole is a spinel single crysul oxide(Fe,Mn)Cr_(2)O_(4) and the globe is a metallic compound(Ni,Fe)_(x)Al_(y) covered with protective Al,Si oxide layer.Nucleation of the metallic globe named while particle is formed at the early stage of heating be tween 700℃ and 900℃.It seems to be extracted from the alloy matrix as a result of arummrum obrusion .Asial growth of pole begins at about 115℃.It is supposed that the whisker grows at the root of a white particle and the interaction effect between the stress of oxide around the particle and the climbing motion of dislocation beneath the particle.If the alloy surface is covered uniformly with Cr_(2)O_(3) as the ini tai oxide film,its final surface oxide film has no whiskers even after long time oxidation at higher temperature in hydrogen atmosphere.Proper surface treatment of base alloy,such mechanical brushing,is very effective for the formation of Cr_(2)O_(3) at initial stage.it is supposed that the brushed surface may be activated to produce surface reactions by an enrichment of lattice defects.展开更多
文摘The oxidation rate,the growth,morphology and structure of oxide scale and whiskers for Fe-Ni-Cr sealing alloys in H_2-H_2O atmosphere at high temperatures have been studied. The growth rate of scale is controlled by diffusion.The scale is composed of Cr_2O_3 and spinel(Fe,Mn)O·Cr_2O_3 and the oxide whisker,are spinel(Fe,Mn)O·Cr_2O_3.
文摘The growth.of oxide films on 476 alloy,with a small amount of additive elements such as Si etc.,oxidized in wet hydrogen atmosphere is some times accompanied by the formation of a great many whiskers.Typical form of whiskers grown on the oxide film is of flag pole type with a globe on its top.The pole is a spinel single crysul oxide(Fe,Mn)Cr_(2)O_(4) and the globe is a metallic compound(Ni,Fe)_(x)Al_(y) covered with protective Al,Si oxide layer.Nucleation of the metallic globe named while particle is formed at the early stage of heating be tween 700℃ and 900℃.It seems to be extracted from the alloy matrix as a result of arummrum obrusion .Asial growth of pole begins at about 115℃.It is supposed that the whisker grows at the root of a white particle and the interaction effect between the stress of oxide around the particle and the climbing motion of dislocation beneath the particle.If the alloy surface is covered uniformly with Cr_(2)O_(3) as the ini tai oxide film,its final surface oxide film has no whiskers even after long time oxidation at higher temperature in hydrogen atmosphere.Proper surface treatment of base alloy,such mechanical brushing,is very effective for the formation of Cr_(2)O_(3) at initial stage.it is supposed that the brushed surface may be activated to produce surface reactions by an enrichment of lattice defects.
