Macroreticular bead PAN/PVC IPN resins with cyano and chloro groups were synthesized by interpenetrating polymerization of acrylonitrile, or acrylonitrile and divinylbenzene into a macroporous polyvinyl chloride bead....Macroreticular bead PAN/PVC IPN resins with cyano and chloro groups were synthesized by interpenetrating polymerization of acrylonitrile, or acrylonitrile and divinylbenzene into a macroporous polyvinyl chloride bead. The composition and structure of the bead IPN resins have been investigated by means of FT-IR, NMR, SEM, mercury porosimetry and elemental analysis. During the process of interpenetrating polymerization, the chain propagation obeys Bernoullian statistical law, and no grafting polymerization has been observed. The content of cyano group in the resulting IPN resins can be adjusted by the amount of acrylonitrile added. The morphology of the IPN resins basically resembles that of the polyvinyl chloride bead, whereas the pore structures vary to a certain degree展开更多
An ion-exchange resin of type 201×7 was impregnated with the reagent 1-(2-Pyridylazo)-2-naphthol-6-sulphonic Acid (PAN-S). The adsorption characteristics of PAN-S resin for manganese ion were studied on the stati...An ion-exchange resin of type 201×7 was impregnated with the reagent 1-(2-Pyridylazo)-2-naphthol-6-sulphonic Acid (PAN-S). The adsorption characteristics of PAN-S resin for manganese ion were studied on the static equilibrium adsorption. Within temperature range of 288K^313K and the concentration range investigated, equilibrium data for the adsorption of manganese ions from aqueous solutions by PAN-S resin were obtained and correlated with Freundlich and Langmuir equation. The results showed that the process of the adsorption of manganese ions from aqueous solution by PAN-S was an exothermic process. Estimations of the isothermic enthalpy change of adsorption,free energy change and entropy of adsorption are reported,and the adsorption behaviors are reasonably interpreted.展开更多
基金Supported by the Science Fund of the State Education Commission of China.
文摘Macroreticular bead PAN/PVC IPN resins with cyano and chloro groups were synthesized by interpenetrating polymerization of acrylonitrile, or acrylonitrile and divinylbenzene into a macroporous polyvinyl chloride bead. The composition and structure of the bead IPN resins have been investigated by means of FT-IR, NMR, SEM, mercury porosimetry and elemental analysis. During the process of interpenetrating polymerization, the chain propagation obeys Bernoullian statistical law, and no grafting polymerization has been observed. The content of cyano group in the resulting IPN resins can be adjusted by the amount of acrylonitrile added. The morphology of the IPN resins basically resembles that of the polyvinyl chloride bead, whereas the pore structures vary to a certain degree
基金The Educational Bureau of Jiangsu Province, P. R. China (Grant Code 08KJD150009)Jiangsu Provincial Key Laboratory of Coastal Wetland Bioresources and Environmental Protection (Grant Code JLCBE07016)
文摘An ion-exchange resin of type 201×7 was impregnated with the reagent 1-(2-Pyridylazo)-2-naphthol-6-sulphonic Acid (PAN-S). The adsorption characteristics of PAN-S resin for manganese ion were studied on the static equilibrium adsorption. Within temperature range of 288K^313K and the concentration range investigated, equilibrium data for the adsorption of manganese ions from aqueous solutions by PAN-S resin were obtained and correlated with Freundlich and Langmuir equation. The results showed that the process of the adsorption of manganese ions from aqueous solution by PAN-S was an exothermic process. Estimations of the isothermic enthalpy change of adsorption,free energy change and entropy of adsorption are reported,and the adsorption behaviors are reasonably interpreted.