The surface properties of PAN-based carbon fibers electrochemically treated in aqueous ammonium bicarbonate before and after treatment were characterized by X-ray photoelectron spectroscopy (XPS), atomic force microsc...The surface properties of PAN-based carbon fibers electrochemically treated in aqueous ammonium bicarbonate before and after treatment were characterized by X-ray photoelectron spectroscopy (XPS), atomic force microscopy (AFM) and Dynamic Contact Angle Analysis (DCAA). The results of characterization indicated that the oxygen and nitrogen contents in carbon fiber surface were significantly increased by electrochemical treatment, and amide groups was introduced onto it, which was related with the electrolyte. The AFM photographs illustrated that the roughness of the fiber surface was also increased. The wettibality of the fibers was improved after treatment because the surface energy especially the polar part of it was increased.展开更多
When the PAN-based stabilized fiber(PAN-SF) was converted to the carbon fiber, the effect of some of the carbonizing parameters on the structure and properties of the resulting carbon fibers, such as the molecular str...When the PAN-based stabilized fiber(PAN-SF) was converted to the carbon fiber, the effect of some of the carbonizing parameters on the structure and properties of the resulting carbon fibers, such as the molecular structure development, element contents, morphology and mechanical properties, was discussed. The results show that the carbonizing temperature, the purity of the inert gas and the de-oil pretreatment of the tiber have a great influence on them.展开更多
The deformation resistance effect of polyacrylonitrile （PAN）-based carbon fibers was investigated, and the variatipn law of electrical resistivity under tensile stress was analyzed. The results show that the gauge f...The deformation resistance effect of polyacrylonitrile （PAN）-based carbon fibers was investigated, and the variatipn law of electrical resistivity under tensile stress was analyzed. The results show that the gauge factor （fractional change in resistance per unit strain） of PAN-based carbon fibers is 1.38, which is lower than that of the commonly-used resistance strain gauge. These may due to that the electrical resistivity of carbon fibers decreases under tensile stress. In addition when the carbon fibers are stretched, the change of its resistance is caused by fiber physical dimension and the change of electric resistivity, and mainly caused by the change of physical dimension. The mechanical properties of carbon fiber monofilament were also measured.展开更多
Structural changes in carbon fibers at each stage of, especially, preoxidation process are well known to play a great role in achieving the ultimate product quality. Differential scanning calorimetry (DSC), scanning e...Structural changes in carbon fibers at each stage of, especially, preoxidation process are well known to play a great role in achieving the ultimate product quality. Differential scanning calorimetry (DSC), scanning electron microscope (SEM), density method and optical microscope were used to characterize the preoxidation extent. A conventional approach, e.g., density aim, to evaluate the extent of preoxidation is not very exact. A DSC curve of a PAN precursor only can provide general information, major in the temperature regime of preoxidation reaction. However, the evaluation of a preoxidation extent, especially from conventional preoxidation temperature with a great span regime of 200~400癈, is put forward in this paper, in which the evolution of core/shell morphological structure is a kind of straightforward evidence.展开更多
Polyacrylonitrile preoxided fibre PANOF is an intermediate in carbon fibre preparation. Thequality of PANOF is closely related to the property and structure of carbon fibre. In this paper, thermal mechanical analysis(...Polyacrylonitrile preoxided fibre PANOF is an intermediate in carbon fibre preparation. Thequality of PANOF is closely related to the property and structure of carbon fibre. In this paper, thermal mechanical analysis(TMA), thermogravimetric analysis(TGA), swell-ing differential scanning calorimetry(SDSC)and X-ray photoelectron spectroscopy(XPS)wereused to study the increase in tenacity of PANOF from the precursor treated with cuprous salt It has been discovered that the cuprous salt reacts strongly with the uncyclized CN of PANOF,resulting in an increase in the tenacity of PANOF by 30%. The results shwo that the cause of thistenacity improvement is the formation of coordinated complex. Cu^+is the central ion, and PANOFthe ligand. It is due to the coordinate bond that the network structure is formed from uncyclizedCN of PANOF. Therefore the tenacity of PANOF is remarkably increased.展开更多
The nanopore structures in precursors Four carbon-fiber precursors are prepared. They are crucial to the performance of PAN-based carbon fibers are bath-fed filaments （A）, water-washing filaments （B） hot-stretchin...The nanopore structures in precursors Four carbon-fiber precursors are prepared. They are crucial to the performance of PAN-based carbon fibers are bath-fed filaments （A）, water-washing filaments （B） hot-stretching filaments （C） and drying-densification filaments （D）. Synchrotron radiation small angle X-ray scattering is used to probe and compare the nanopore structures of the four fibers. The nanopore size, discrete volume distribution, nanopore orientation degree along the fiber axis and the porosity are obtained. The results demonstrate that the nanopores are mainly formed in the water-washing stage. During the processes of the subsequent production technologies, the slenderness ratio of nanopores and their orientation degree along the fiber axis increase further and simultaneously, the porosity decreases. These results are helpful for improving the performance of the final carbon fibers.展开更多
基金Sponsored by the Scientific Research Foundation of Harbin Institute of Technology(Grant No. HIT. 2003.57)
文摘The surface properties of PAN-based carbon fibers electrochemically treated in aqueous ammonium bicarbonate before and after treatment were characterized by X-ray photoelectron spectroscopy (XPS), atomic force microscopy (AFM) and Dynamic Contact Angle Analysis (DCAA). The results of characterization indicated that the oxygen and nitrogen contents in carbon fiber surface were significantly increased by electrochemical treatment, and amide groups was introduced onto it, which was related with the electrolyte. The AFM photographs illustrated that the roughness of the fiber surface was also increased. The wettibality of the fibers was improved after treatment because the surface energy especially the polar part of it was increased.
文摘When the PAN-based stabilized fiber(PAN-SF) was converted to the carbon fiber, the effect of some of the carbonizing parameters on the structure and properties of the resulting carbon fibers, such as the molecular structure development, element contents, morphology and mechanical properties, was discussed. The results show that the carbonizing temperature, the purity of the inert gas and the de-oil pretreatment of the tiber have a great influence on them.
基金Funded by the National Natural Science Foundation of China (No.10672128 and 50878170)
文摘The deformation resistance effect of polyacrylonitrile （PAN）-based carbon fibers was investigated, and the variatipn law of electrical resistivity under tensile stress was analyzed. The results show that the gauge factor （fractional change in resistance per unit strain） of PAN-based carbon fibers is 1.38, which is lower than that of the commonly-used resistance strain gauge. These may due to that the electrical resistivity of carbon fibers decreases under tensile stress. In addition when the carbon fibers are stretched, the change of its resistance is caused by fiber physical dimension and the change of electric resistivity, and mainly caused by the change of physical dimension. The mechanical properties of carbon fiber monofilament were also measured.
基金the National Natural Science Foundatlon of China under grant No.50172004,50273002 ,50333070.
文摘Structural changes in carbon fibers at each stage of, especially, preoxidation process are well known to play a great role in achieving the ultimate product quality. Differential scanning calorimetry (DSC), scanning electron microscope (SEM), density method and optical microscope were used to characterize the preoxidation extent. A conventional approach, e.g., density aim, to evaluate the extent of preoxidation is not very exact. A DSC curve of a PAN precursor only can provide general information, major in the temperature regime of preoxidation reaction. However, the evaluation of a preoxidation extent, especially from conventional preoxidation temperature with a great span regime of 200~400癈, is put forward in this paper, in which the evolution of core/shell morphological structure is a kind of straightforward evidence.
文摘Polyacrylonitrile preoxided fibre PANOF is an intermediate in carbon fibre preparation. Thequality of PANOF is closely related to the property and structure of carbon fibre. In this paper, thermal mechanical analysis(TMA), thermogravimetric analysis(TGA), swell-ing differential scanning calorimetry(SDSC)and X-ray photoelectron spectroscopy(XPS)wereused to study the increase in tenacity of PANOF from the precursor treated with cuprous salt It has been discovered that the cuprous salt reacts strongly with the uncyclized CN of PANOF,resulting in an increase in the tenacity of PANOF by 30%. The results shwo that the cause of thistenacity improvement is the formation of coordinated complex. Cu^+is the central ion, and PANOFthe ligand. It is due to the coordinate bond that the network structure is formed from uncyclizedCN of PANOF. Therefore the tenacity of PANOF is remarkably increased.
基金Supported by National Natural Science Foundation of China (10835008)Knowledge Innovation Program of Chinese Academy of Sciences (KJCX3-SYW-N8)Momentous Equipment Program of Chinese Academy of Sciences (YZ200829)
文摘The nanopore structures in precursors Four carbon-fiber precursors are prepared. They are crucial to the performance of PAN-based carbon fibers are bath-fed filaments （A）, water-washing filaments （B） hot-stretching filaments （C） and drying-densification filaments （D）. Synchrotron radiation small angle X-ray scattering is used to probe and compare the nanopore structures of the four fibers. The nanopore size, discrete volume distribution, nanopore orientation degree along the fiber axis and the porosity are obtained. The results demonstrate that the nanopores are mainly formed in the water-washing stage. During the processes of the subsequent production technologies, the slenderness ratio of nanopores and their orientation degree along the fiber axis increase further and simultaneously, the porosity decreases. These results are helpful for improving the performance of the final carbon fibers.