Achieving high fouling resistance and permeability using membrane separation technology in water treatment processes remains a challenge.In this work,a novel mixed-matrix membrane(MMM)(poly(arylene ether ketone)[PAEK]...Achieving high fouling resistance and permeability using membrane separation technology in water treatment processes remains a challenge.In this work,a novel mixed-matrix membrane(MMM)(poly(arylene ether ketone)[PAEK]-containing carboxyl groups[PAEK-COOH]/UiO-66-NH_(2)@graphene oxide[GO])with superb fouling resistance and high permeability was prepared by the nonsolvent-induced phase separation method,by in-situ growth of UiO-66-NH_(2) on the GO layer,and by preparing hydrophilic PAEK-COOH.On the basis of the structure and performance analysis of the MMM,the maximum water flux reached 591.25 L·m^(-2)·h^(-1) for PAEK-COOH/UiO-66-NH_(2)@GO,whereas the retention rate for bovine serum albumin increased from 85.40%to 94.87%.As the loading gradually increased,the hydrophilicity of the MMMs increased,significantly enhancing their fouling resistance.The strongest anti-fouling ability observed was 94.74%,which was 2.02 times greater than that of the pure membrane.At the same time,the MMMs contained internal amide and hydrogen bonds during the preparation process,forming a cross-linked structure,which further enhanced the mechanical strength and chemical stability.In summary,the MMMs with high retention rate,strong permeability,and anti-fouling ability were successfully prepared.展开更多
A novel type of aromatic poly（ ether ether ketone） s with carboxyl groups were prepared by polycondensation of 4,4-bis（4-hydroxyphenyl）pentanoic acid with difluoro-monomers. Their mo- lecular structures were deter...A novel type of aromatic poly（ ether ether ketone） s with carboxyl groups were prepared by polycondensation of 4,4-bis（4-hydroxyphenyl）pentanoic acid with difluoro-monomers. Their mo- lecular structures were determined by ^1H-NMR and IR, respectively. Their molecular weights were measured by gel permeation chromatography （ GPC ）, which showed that all the polymers had high molecule weights （ 〉 42 000）. Due to the long side chains of polymers, all the polymers had good solubility （soluble in NMP, DMAc, THF, etc. ）. The differential scanning calorimeter （DSC） detected their excellent glass transition temperatures （ Tg ） up to 195 ℃. The Tg increased with the content of carboxylic units in the polymer chains, because the interactions of H bonds increased with increasing content of carboxylic. The polymers could form transparent and flexible films, which make them a candidate for membrane materials.展开更多
Free radical co-polymerization was employed to synthesize co-poly carboxylate (PC) su-perplasticizers with different amount of carboxyl and methyl polyethylene glycol (MPEG) side chain. Dispersion ability and retentio...Free radical co-polymerization was employed to synthesize co-poly carboxylate (PC) su-perplasticizers with different amount of carboxyl and methyl polyethylene glycol (MPEG) side chain. Dispersion ability and retention of PC were compared with one another. The results show that increase of side chain is advantageous to dispersion, but it decreases when amount of MPEG is beyond a certain value which is different with the proportion of carboxyl. If the amount of carboxyl increases, the influence of side chain in copolymer on dispersion diminishes. Polyether side chain is advantageous to retention. And the author explained the mechanism of PC using the theory of steric repulsive force.展开更多
In this study, poly（L-lactic acid）/ammonium persulfate doped-polypyrrole composite fibrous scaffolds with moderate conductivity were produced by combining electrospinning with in situ polymerization. PC12 cells were...In this study, poly（L-lactic acid）/ammonium persulfate doped-polypyrrole composite fibrous scaffolds with moderate conductivity were produced by combining electrospinning with in situ polymerization. PC12 cells were cultured on these fibrous scaffolds and their growth following electrical stimulation （0-20.0 μA stimulus intensity, for 1-4 days） was observed using inverted light microscopy, and scanning electron microscopy coupled with the MTT cell viability test. The results demonstrated that the poly（L-lactic acid）/ammonium persulfate doped-polypyrrole fibrous scaffold was a dual multi-porous micro/nano fibrous scaffold. An electrical stimulation with a current intensity 5.0- 10.0 μAfor about 2 days enhanced neuronal growth and neurite outgrowth, while a high current intensity （over 15.0 μA） suppressed them. These results indicate that electrical stimulation with a moderate current intensity for an optimum time frame can promote neuronal growth and neurite outgrowth in an intensity- and time-dependent manner.展开更多
Poly （3, 4-ethylenedioxythiophene） （PEDOT）, together with its dopes, such as poly （styrene sulfonate） （PSS）, has been acknowledged to have a wide range of biomedical applications as an important conducting pol...Poly （3, 4-ethylenedioxythiophene） （PEDOT）, together with its dopes, such as poly （styrene sulfonate） （PSS）, has been acknowledged to have a wide range of biomedical applications as an important conducting polymer. In this study, gelatin can be polymerized into PEDOT/PSS polymers on indium tin oxide （ITO）-coated glass. PEDOT/PSS/gelatin layer on ITO-coated glass significantly decreases electrochemical impedance spectroscopy （EIS） and increases charge delivery capacity relative to the gelatin layer and bare ITO- coated glass, comparable to the PEDOT/PSS layer on ITO-coated glass. PEDOT/PSS/gelatin layer on ITO- coated glass enhances pheochromocytoma （PC 12） cell affinity, possesses a high biocompatibility and promotes PC 12 cell growth by delivery of electrical stimulation. These results suggest that gelatin can be incorporated into the PEDOT/PSS polymers through electrochemical polymerization and the PEDOT/PSS/gelatin layer on ITO-coated glass possesses high electrochemical and biological activities.展开更多
The characterization of complexes is particularly critical for quality control and development of gene delivery systems. Here, the method of capillary zone electrophoresis （CZE） for the characterization of DNA and p...The characterization of complexes is particularly critical for quality control and development of gene delivery systems. Here, the method of capillary zone electrophoresis （CZE） for the characterization of DNA and polyoL-lysine （MW 28 500） or DNA and poly-L-lysine modified with polyethylene glycol （MW10 000） complexes at various charge ratios in phosphate buffer is described firstly. During the characterization, DNA complexes can be separated into various components with different charge-to-mass ratio, i.e, components with single physicochemical property. And also the size and zeta potential of complexes were characterized by using photon correlation spectroscopy. This method is useful to characterize various complexes formed by DNA and polycations, and has the potential to separate complexes into homogeneous component for better transfection efficiency in vitro and in vivo in future.展开更多
基金support of this work by National Natural Science Foundation of China(22075031,51673030,51603017 and 51803011)Jilin Provincial Science&Technology Department(20220201105GX)Chang Bai Mountain Scholars Program of Jilin Province.
文摘Achieving high fouling resistance and permeability using membrane separation technology in water treatment processes remains a challenge.In this work,a novel mixed-matrix membrane(MMM)(poly(arylene ether ketone)[PAEK]-containing carboxyl groups[PAEK-COOH]/UiO-66-NH_(2)@graphene oxide[GO])with superb fouling resistance and high permeability was prepared by the nonsolvent-induced phase separation method,by in-situ growth of UiO-66-NH_(2) on the GO layer,and by preparing hydrophilic PAEK-COOH.On the basis of the structure and performance analysis of the MMM,the maximum water flux reached 591.25 L·m^(-2)·h^(-1) for PAEK-COOH/UiO-66-NH_(2)@GO,whereas the retention rate for bovine serum albumin increased from 85.40%to 94.87%.As the loading gradually increased,the hydrophilicity of the MMMs increased,significantly enhancing their fouling resistance.The strongest anti-fouling ability observed was 94.74%,which was 2.02 times greater than that of the pure membrane.At the same time,the MMMs contained internal amide and hydrogen bonds during the preparation process,forming a cross-linked structure,which further enhanced the mechanical strength and chemical stability.In summary,the MMMs with high retention rate,strong permeability,and anti-fouling ability were successfully prepared.
基金Supported by Open Project of State Key Laboratory of Supramolecular Structure and Materials(SKLSSM201114)the National Natural Science Foundation of China(51103010)
文摘A novel type of aromatic poly（ ether ether ketone） s with carboxyl groups were prepared by polycondensation of 4,4-bis（4-hydroxyphenyl）pentanoic acid with difluoro-monomers. Their mo- lecular structures were determined by ^1H-NMR and IR, respectively. Their molecular weights were measured by gel permeation chromatography （ GPC ）, which showed that all the polymers had high molecule weights （ 〉 42 000）. Due to the long side chains of polymers, all the polymers had good solubility （soluble in NMP, DMAc, THF, etc. ）. The differential scanning calorimeter （DSC） detected their excellent glass transition temperatures （ Tg ） up to 195 ℃. The Tg increased with the content of carboxylic units in the polymer chains, because the interactions of H bonds increased with increasing content of carboxylic. The polymers could form transparent and flexible films, which make them a candidate for membrane materials.
文摘Free radical co-polymerization was employed to synthesize co-poly carboxylate (PC) su-perplasticizers with different amount of carboxyl and methyl polyethylene glycol (MPEG) side chain. Dispersion ability and retention of PC were compared with one another. The results show that increase of side chain is advantageous to dispersion, but it decreases when amount of MPEG is beyond a certain value which is different with the proportion of carboxyl. If the amount of carboxyl increases, the influence of side chain in copolymer on dispersion diminishes. Polyether side chain is advantageous to retention. And the author explained the mechanism of PC using the theory of steric repulsive force.
基金supported by the National Natural Science Foundation of China,No.51073072the Natural Science Foundation of Zhejiang Province in China,No.Y4100745+1 种基金the Key Laboratory Open Foundation of Advanced Textile Materials&Manufacturing Technology of Zhejiang Sci-Tech University from Ministry of Education of China,No.2009007the Science and Technology Commission of Jiaxing Municipality Program,No.2010AY1089
文摘In this study, poly（L-lactic acid）/ammonium persulfate doped-polypyrrole composite fibrous scaffolds with moderate conductivity were produced by combining electrospinning with in situ polymerization. PC12 cells were cultured on these fibrous scaffolds and their growth following electrical stimulation （0-20.0 μA stimulus intensity, for 1-4 days） was observed using inverted light microscopy, and scanning electron microscopy coupled with the MTT cell viability test. The results demonstrated that the poly（L-lactic acid）/ammonium persulfate doped-polypyrrole fibrous scaffold was a dual multi-porous micro/nano fibrous scaffold. An electrical stimulation with a current intensity 5.0- 10.0 μAfor about 2 days enhanced neuronal growth and neurite outgrowth, while a high current intensity （over 15.0 μA） suppressed them. These results indicate that electrical stimulation with a moderate current intensity for an optimum time frame can promote neuronal growth and neurite outgrowth in an intensity- and time-dependent manner.
基金Funded by National Natural Science Foundation of China(Nos.11179015,51173108)Innovation Program of Shanghai Municipal Education Commission(No.12ZZ143)
文摘Poly （3, 4-ethylenedioxythiophene） （PEDOT）, together with its dopes, such as poly （styrene sulfonate） （PSS）, has been acknowledged to have a wide range of biomedical applications as an important conducting polymer. In this study, gelatin can be polymerized into PEDOT/PSS polymers on indium tin oxide （ITO）-coated glass. PEDOT/PSS/gelatin layer on ITO-coated glass significantly decreases electrochemical impedance spectroscopy （EIS） and increases charge delivery capacity relative to the gelatin layer and bare ITO- coated glass, comparable to the PEDOT/PSS layer on ITO-coated glass. PEDOT/PSS/gelatin layer on ITO- coated glass enhances pheochromocytoma （PC 12） cell affinity, possesses a high biocompatibility and promotes PC 12 cell growth by delivery of electrical stimulation. These results suggest that gelatin can be incorporated into the PEDOT/PSS polymers through electrochemical polymerization and the PEDOT/PSS/gelatin layer on ITO-coated glass possesses high electrochemical and biological activities.
文摘The characterization of complexes is particularly critical for quality control and development of gene delivery systems. Here, the method of capillary zone electrophoresis （CZE） for the characterization of DNA and polyoL-lysine （MW 28 500） or DNA and poly-L-lysine modified with polyethylene glycol （MW10 000） complexes at various charge ratios in phosphate buffer is described firstly. During the characterization, DNA complexes can be separated into various components with different charge-to-mass ratio, i.e, components with single physicochemical property. And also the size and zeta potential of complexes were characterized by using photon correlation spectroscopy. This method is useful to characterize various complexes formed by DNA and polycations, and has the potential to separate complexes into homogeneous component for better transfection efficiency in vitro and in vivo in future.