Owing to heavy dynamic and thermal loads, PCBN tools are seriously worn during hard cutting, which largely constrains the improvement of their machining performance. Therein, the chamfered structure of a cutting edge ...Owing to heavy dynamic and thermal loads, PCBN tools are seriously worn during hard cutting, which largely constrains the improvement of their machining performance. Therein, the chamfered structure of a cutting edge has a notable influence on the tool wear. Thus, a comparative study was carried out on the wear morphology and wear mechanism of PCBN tools with either a variable chamfered edge or an invariable chamfered edge. The results indicate that, for a PCBN tool with a variable chamfered edge, the rake wear area is far from the cutting edge and slowly extends toward it. A shallow large-area crater wear occurs on the rake face, and the flank wear area has a long triangular shape with a smaller wear area and width, and the cutting edge remains in a good state during the cutting process. In contrast, for a PCBN tool with an invariable chamfered edge, a deep small-area crater appears on the rake face, and the wear area is close to the cutting edge and quickly extends toward it. Thus, it is easy for chips to accumulate in the crater, resulting in large-area and high-speed wear on the flank face. In addition, the tool shows a weak wear resistance. In the initial wear stage, the rake wear mechanism of the two cutting tools is a mixture of abrasive, oxidation, and other types of wear, whereas their flank wear mechanism is dominated by abrasive wear. With an aggravation of the tool wear, the oxidation and diffusion wear mechanism are both increasingly strengthened. The rake wear of the cutter with a variable chamfered edge showed an obvious increase in the oxidation and diffusion wear, as did the flank wear of the cutter with an invariable chamfered edge. This study revealed the wear mechanism of the PCBN tool with a variable chamfered edge and provided theoretical and technological support for its popularization and application in the machining of high-hardness materials.展开更多
The wear forms and reasons of PCBN tools when dry-cutting bearing steel GCr15are studied systematically. The effect law of the workpiece hardness on PCBN tools is gained andtool wearing with the quickest speed at the ...The wear forms and reasons of PCBN tools when dry-cutting bearing steel GCr15are studied systematically. The effect law of the workpiece hardness on PCBN tools is gained andtool wearing with the quickest speed at the workpiece critical hardness is proved. The life equationat two kinds of workpiece hardness demonstrates that the effect of the cutting speed on the PCBNtool life is less than that of carbide tools and ceramic tools.展开更多
A study was undertaken to investigate the performan ce of PCBN tool in the finish turning GCr15 bearing steel with different hardness between 30～64 HRC. The natural thermocouple was used to measure the cutting tem p ...A study was undertaken to investigate the performan ce of PCBN tool in the finish turning GCr15 bearing steel with different hardness between 30～64 HRC. The natural thermocouple was used to measure the cutting tem p erature, tool life and cutting temperature were investigated and compared. The m aterial can be heated by this instrument which using low voltage and high elec trical current, while PCBN can’t be heated by electrifying directly, so the ke ntanium layer coating over the PCBN is heated, so the PCBN is heated and its th ermoelectric property is got by this method. [TPP129,+60mm88mm,Y,PZ#] Fig.1 Effect of cutting depth and workpiec hardness on. the cutting temperatureThe objective was to determine the influence of the workpiece hardness on change s in cutting temperature and tool wear characterize. It can be found from Fig.1 that the cutting temperature show an increasing tendency with the improvement of workpiece hardness within the cutting speed scope when the workpiece hardness i s under HRC50. And on the other hand, it is found that the cutting temperature s how the downtrend with the improvement of workpiece hardness when the workpiece hardness is over HRC50. According to experimental results, the critical hard ness when turning hardened GCr15 bearing steel with PCBN tool is about HRC50. Th e wear causes of PCBN tool have been found out through taking photos on the micr o-shape of PCBN poly-laminate initial surface as well as face and flank of wea r tool and analysis on chemical elements. It is discovered that the PCBN tools a re not suitable for cutting the workpiece at nearly critical hardness, because n ear the critical hardness, PCBN wear at the highest speed. For researching the w ear rule of PCBN tool, the tool wear experiments have been carried on by using b earing steel GCr15 at hardness HRC40 and HRC60 with changing cutting speed. The indexes of tool life equations is gained under two kinds of conditions w hich are bigger than 0.6, so the effects of cutting speed on the PCBN tool are m uch less than that of carbide tool and ceramic tool.展开更多
基金Supported by National Natural Science Foundation of China(Grant No.51475125)Heilongjiang Provincial Natural Science Foundation of China(Grant No.E2016047)
文摘Owing to heavy dynamic and thermal loads, PCBN tools are seriously worn during hard cutting, which largely constrains the improvement of their machining performance. Therein, the chamfered structure of a cutting edge has a notable influence on the tool wear. Thus, a comparative study was carried out on the wear morphology and wear mechanism of PCBN tools with either a variable chamfered edge or an invariable chamfered edge. The results indicate that, for a PCBN tool with a variable chamfered edge, the rake wear area is far from the cutting edge and slowly extends toward it. A shallow large-area crater wear occurs on the rake face, and the flank wear area has a long triangular shape with a smaller wear area and width, and the cutting edge remains in a good state during the cutting process. In contrast, for a PCBN tool with an invariable chamfered edge, a deep small-area crater appears on the rake face, and the wear area is close to the cutting edge and quickly extends toward it. Thus, it is easy for chips to accumulate in the crater, resulting in large-area and high-speed wear on the flank face. In addition, the tool shows a weak wear resistance. In the initial wear stage, the rake wear mechanism of the two cutting tools is a mixture of abrasive, oxidation, and other types of wear, whereas their flank wear mechanism is dominated by abrasive wear. With an aggravation of the tool wear, the oxidation and diffusion wear mechanism are both increasingly strengthened. The rake wear of the cutter with a variable chamfered edge showed an obvious increase in the oxidation and diffusion wear, as did the flank wear of the cutter with an invariable chamfered edge. This study revealed the wear mechanism of the PCBN tool with a variable chamfered edge and provided theoretical and technological support for its popularization and application in the machining of high-hardness materials.
基金This project is supported by Provincial Natural Science Foundation of China(No.59975026).
文摘The wear forms and reasons of PCBN tools when dry-cutting bearing steel GCr15are studied systematically. The effect law of the workpiece hardness on PCBN tools is gained andtool wearing with the quickest speed at the workpiece critical hardness is proved. The life equationat two kinds of workpiece hardness demonstrates that the effect of the cutting speed on the PCBNtool life is less than that of carbide tools and ceramic tools.
文摘A study was undertaken to investigate the performan ce of PCBN tool in the finish turning GCr15 bearing steel with different hardness between 30～64 HRC. The natural thermocouple was used to measure the cutting tem p erature, tool life and cutting temperature were investigated and compared. The m aterial can be heated by this instrument which using low voltage and high elec trical current, while PCBN can’t be heated by electrifying directly, so the ke ntanium layer coating over the PCBN is heated, so the PCBN is heated and its th ermoelectric property is got by this method. [TPP129,+60mm88mm,Y,PZ#] Fig.1 Effect of cutting depth and workpiec hardness on. the cutting temperatureThe objective was to determine the influence of the workpiece hardness on change s in cutting temperature and tool wear characterize. It can be found from Fig.1 that the cutting temperature show an increasing tendency with the improvement of workpiece hardness within the cutting speed scope when the workpiece hardness i s under HRC50. And on the other hand, it is found that the cutting temperature s how the downtrend with the improvement of workpiece hardness when the workpiece hardness is over HRC50. According to experimental results, the critical hard ness when turning hardened GCr15 bearing steel with PCBN tool is about HRC50. Th e wear causes of PCBN tool have been found out through taking photos on the micr o-shape of PCBN poly-laminate initial surface as well as face and flank of wea r tool and analysis on chemical elements. It is discovered that the PCBN tools a re not suitable for cutting the workpiece at nearly critical hardness, because n ear the critical hardness, PCBN wear at the highest speed. For researching the w ear rule of PCBN tool, the tool wear experiments have been carried on by using b earing steel GCr15 at hardness HRC40 and HRC60 with changing cutting speed. The indexes of tool life equations is gained under two kinds of conditions w hich are bigger than 0.6, so the effects of cutting speed on the PCBN tool are m uch less than that of carbide tool and ceramic tool.