PCD和CVD金刚石刀具切削性能对比及失效机理初探

通过切削实验,观察切削前后刀具的表面和刃口形貌、金刚石刀片组成成分、以及被加工工件表面粗糙度,比较两种刀具的切削性能,探讨其失效机理。结果表明:在同等条件下,CVD金刚石刀具的切削性能要明显优于PCD刀具。在车削过程中,PCD刀具的失效机理主要是结合剂与被加工材料中化学成分发生化学反应使结合剂流失,导致刀具结构疏松,从而导致磨粒团脱落。CVD刀具的失效机理为产生变质层磨损。切削过程中随着加工时间的进一步延长,切削区温度不断升高,当达到热化学反应温度时,就会在刀具表面形成变质层,从而带来切削过程中刀具的磨损;同时高温状态下CVD金刚石的晶界疲劳破坏,也可能会造成CVD金刚石刀具的磨损失效。

PCD面铣刀切削刃对低刚性的缸盖面的毛刺影响

在夹具系统刚性不足的情况下,铝合金缸盖燃烧室和覆盖面很容易出现毛刺。文中介绍了PCD铣刀出现毛刺的原因。研究PCD面铣刀切削刃的几何参数对于毛刺影响的研究。提出了一种在刚性不足的切削系统下,达到既没有振纹又没有毛刺的方法。

Influence of Machining Parameter on Tool Life While Machining Hybrid Metal Matrix Composites

A metal matrix composite constitutes a continuous metallic matrix and a discontinuous phase known as reinforcement. The hybrid metal matrix composites (Hmmcs) have been used to manufacture drive shafts, disc brake rotors, brake drums, connecting rods pistons, engine block cylinder liners for automotive and rail vehicle applications. The Hmmcs castings of diameter 120 mm and length 300 mm were prepared through sand mould technique following stir casting methodology. The cast components further subjected to evaluation of physical properties and machining tests using two grades of coated inserts and PCD inserts. The experiments were carried out following ISO 3685 standards. The coating thickness of the TiN coated and TiAlN coated inserts were measured using Kalo testing method; the results of the test show that the interface of the substrate and coating was free from the porosity, and the coating thickness of TiN coating was 4.84 microns and TiAlN coating was measured 4.6 microns. The results of the experiments show that performance of the PCD insert was better than coated inserts at 0.1 mm/rev feed; however at 0.2 mm/revolution feed PCD insert failed by micro chipping of cutting edge while machining Hmmcs. When TiAlN coated inserts were used to machine Hmmcs the coated inserts failed by gradual wear and BUE formation.

新型金刚石刀片及刀盘铣削铝合金时对毛刺的控制

毛刺通常由于塑性变形产生于被加工材料切削终端边缘,并且特别容易产生于诸如铝合金一类延展性较好或是如不锈钢一样韧性较好的材质。因而,为了控制毛刺,就要设法减小被加工材料切削终端边缘部分的塑性变形,也就是必须降低切削力。本研究主要探讨了刀盘的几何构造及其所使用的金刚石刀片的刀尖几何形状与面铣刀盘加工时毛刺发生机理的相关性。