The spherulitic structure and morphology development of poly(ethylene succinate)/poly(ethylene oxide) (PES/PEO) blends with one-step crystallization behavior were observed by means of polarizing optical microscope.It ...The spherulitic structure and morphology development of poly(ethylene succinate)/poly(ethylene oxide) (PES/PEO) blends with one-step crystallization behavior were observed by means of polarizing optical microscope.It was found that the pure PES spherulite in which the adequate quantity of PEO melt existed in the interlamellar regions,and the blending spherulite formed by both PES and PEO lamellae could form simultaneously.When the two types of spherulites contacted with each other the front of the blending ...展开更多
For evaluation of the rheological and mechanical properties of highly filled wood plastic composites （WPCs）, polypropylene/polyethylene （PP/PE） blends were grafted with maleic anhydride （MAH） to enhance the inte...For evaluation of the rheological and mechanical properties of highly filled wood plastic composites （WPCs）, polypropylene/polyethylene （PP/PE） blends were grafted with maleic anhydride （MAH） to enhance the interfacial adhesion between wood fiber and matrix. WPCs were prepared from wood fiber up to 60 wt.% and modified PP/PE was blended by extrusion. The rheological properties were studied by using dynamic measurement. According to the strain sweep test, the linear viscoelastic region of composites in the melt was determined. The result showed that the storage modulus was independent of the strain at low strain region （〈0.1%）. The frequency sweep resuits indicated that all composites exhibited shear thinning behavior, and both the storage modulus and complex viscosity of MAH modified composites were decreased comparing to those unmodified. Flexural properties and impact strength of the prepared WPCs were measured according to the relevant standard specifications. The flexural and impact strength of the manufactured composites significantly increased and reached a maximum when MAH dosage was 1.0 wt%, whereas the flexural modulus after an initial decreased, also increased with MAH dosage. The increase in mechanical properties indicated that the presence of anhydride groups enhanced the interracial adhesion between wood fiber and PP/PE blends.展开更多
应用广角 X 光散射(WAXS)和示差扫描量热分析(DSC)技术研究了聚苯硫醚/聚醚砜共混物及其碳纤维增强聚苯硫醚/聚醚砜混杂基体复合材料的结构特征和熔融、结晶行为。实验结果表明,(1)聚醚砜和碳纤维的混入未使聚苯硫醚的晶型发生改变,但...应用广角 X 光散射(WAXS)和示差扫描量热分析(DSC)技术研究了聚苯硫醚/聚醚砜共混物及其碳纤维增强聚苯硫醚/聚醚砜混杂基体复合材料的结构特征和熔融、结晶行为。实验结果表明,(1)聚醚砜和碳纤维的混入未使聚苯硫醚的晶型发生改变,但使聚苯硫醚的结晶规整度降低;(2)碳纤维的混入可引起聚苯硫醚熔点降低,而混入聚醚砜并不引起聚苯硫醚的熔点降低;(3)聚醚砜和碳纤维均对聚苯硫醚存在诱导结晶效应,当碳纤维和聚醚砜共存时,聚本硫醚倾向于在碳纤维表面择优成核结晶。展开更多
基金supported by Key Science Foundation of Education Ministry of China (No.207051)Key Lab Foundation of Anhui (No.2005383).
文摘The spherulitic structure and morphology development of poly(ethylene succinate)/poly(ethylene oxide) (PES/PEO) blends with one-step crystallization behavior were observed by means of polarizing optical microscope.It was found that the pure PES spherulite in which the adequate quantity of PEO melt existed in the interlamellar regions,and the blending spherulite formed by both PES and PEO lamellae could form simultaneously.When the two types of spherulites contacted with each other the front of the blending ...
文摘For evaluation of the rheological and mechanical properties of highly filled wood plastic composites （WPCs）, polypropylene/polyethylene （PP/PE） blends were grafted with maleic anhydride （MAH） to enhance the interfacial adhesion between wood fiber and matrix. WPCs were prepared from wood fiber up to 60 wt.% and modified PP/PE was blended by extrusion. The rheological properties were studied by using dynamic measurement. According to the strain sweep test, the linear viscoelastic region of composites in the melt was determined. The result showed that the storage modulus was independent of the strain at low strain region （〈0.1%）. The frequency sweep resuits indicated that all composites exhibited shear thinning behavior, and both the storage modulus and complex viscosity of MAH modified composites were decreased comparing to those unmodified. Flexural properties and impact strength of the prepared WPCs were measured according to the relevant standard specifications. The flexural and impact strength of the manufactured composites significantly increased and reached a maximum when MAH dosage was 1.0 wt%, whereas the flexural modulus after an initial decreased, also increased with MAH dosage. The increase in mechanical properties indicated that the presence of anhydride groups enhanced the interracial adhesion between wood fiber and PP/PE blends.
文摘应用广角 X 光散射(WAXS)和示差扫描量热分析(DSC)技术研究了聚苯硫醚/聚醚砜共混物及其碳纤维增强聚苯硫醚/聚醚砜混杂基体复合材料的结构特征和熔融、结晶行为。实验结果表明,(1)聚醚砜和碳纤维的混入未使聚苯硫醚的晶型发生改变,但使聚苯硫醚的结晶规整度降低;(2)碳纤维的混入可引起聚苯硫醚熔点降低,而混入聚醚砜并不引起聚苯硫醚的熔点降低;(3)聚醚砜和碳纤维均对聚苯硫醚存在诱导结晶效应,当碳纤维和聚醚砜共存时,聚本硫醚倾向于在碳纤维表面择优成核结晶。