Nanomagnetic CoPt truncated octahedral nanoparticles （TONPs） were successfully synthesised through a facile one-pot strategy. These single crystal CoPt TONPs with an average size of about 8 nm exhibit excellent elec...Nanomagnetic CoPt truncated octahedral nanoparticles （TONPs） were successfully synthesised through a facile one-pot strategy. These single crystal CoPt TONPs with an average size of about 8 nm exhibit excellent electrocatalytic performance of both activity and stability for methanol oxidation reaction （MOR）. The mass and specific activities of CoPt TONPs is 8 and 6 times higher than that of standard commercial Pt/C, respectively. After accelerated durability test （ADT）, the loss of electrochemical surface area （ECSA） for CoPt TONPs is only 18.5%, which is significantly less than that of commercial Pt/C （68.2%）, indicating that CoPt TONPs possess much better stability than commercial Pt/C in the prolonged operation. The Curie temperature of CoPt TONPs down to 8 nm is as high as 350 K with weak ferromagntism at room temperature （RT）, which is greatly valuable for recycling in the eletrocatalytic applications.展开更多
基金supported by the National Basic Research Program of China(2015CB921401)the National Instrument Program of China(2012YQ120048)+2 种基金the National Natural Science Foundation of China(51625101,51431009,51471183,51331002,51371015,11274371 and 11674023)the Instrument Development Program of Chinese Academy of Sciences(YZ201345)the Fundamental Research Funds for the Central Universities(FRF-BR-15-009B)
文摘Nanomagnetic CoPt truncated octahedral nanoparticles （TONPs） were successfully synthesised through a facile one-pot strategy. These single crystal CoPt TONPs with an average size of about 8 nm exhibit excellent electrocatalytic performance of both activity and stability for methanol oxidation reaction （MOR）. The mass and specific activities of CoPt TONPs is 8 and 6 times higher than that of standard commercial Pt/C, respectively. After accelerated durability test （ADT）, the loss of electrochemical surface area （ECSA） for CoPt TONPs is only 18.5%, which is significantly less than that of commercial Pt/C （68.2%）, indicating that CoPt TONPs possess much better stability than commercial Pt/C in the prolonged operation. The Curie temperature of CoPt TONPs down to 8 nm is as high as 350 K with weak ferromagntism at room temperature （RT）, which is greatly valuable for recycling in the eletrocatalytic applications.