Performance characterization, of rigid polyurethane foam with refined alkali lignin and modified alkali lignin

The two kinds of rigid polyurethane （PU） foams were prepared with respectively adding the refined alkali lignin and alkali lignin modified by 3-chloro-1,2-epoxypropane to be instead of 15% of the polyether glycol in weight. The indexes of mechanical performance, apparent density, thermal stability and aging resistance were separately tested for the prepared PU foams. The results show that the mechanical property, thermal insulation and thermal stability for PU foam with modified alkali lignin are excellent among two kinds of PU foams and control samples. The additions of the refined alkali lignin and modified alkali lignin to PU foam have little effect on the natural aging or heat aging resistance except for decreasing hot alkali resistance apparently. Additionally, the thermal conductivity of modified alkali lignin PU foam is lowest among two kinds of PU foams and control samples. The alkali lignin PU foam modified by 3-chloro-1,2-epoxypropane could be applied in the heat preservation field.

Self-Repairing Membranes for Inflatable Structures Inspired by a Rapid Wound Sealing Process of Climbing Plants

A new self-repairing membrane for inflatable light weight structures such as rubber boats or Tensairity constructions is presented. Inspired by rapid self-sealing processes in plants, a thin soft cellular polyurethane foam coating is applied on the inside of a fabric substrate, which closes the fissure if the membrane is punctured with a spike. Experimental tests are carried out with a purpose built setup by measuring the air mass flow through a leak in a damaged membrane sample. It is shown that the weight per unit area of the self-repairing foam as well as the curing of the two component PU-foam under an overpressure influence the repair efficiency. Curing the foam under overpressure affects the relative density as well as the microstructure of the foam coatings. Maximal median repair efficiencies of 0.999 have been obtained with 0.16 g.cm 2 foam cured at 1 bar overpressure. These results suggest that the bio-inspired technique has the potential to extend the functional integrity of injured inflatable structures dramatically.

Performance characterization of rigid polyurethane foam with refined alkali lignin and modified alkali lignin

The two kinds of rigid polyurethane(PU) foams were prepared with respectively adding the refined alkali lignin and alkali lignin modified by 3-chloro-1,2-epoxypropane to be instead of 15% of the polyether glycol in weight.The indexes of mechanical performance, apparent density, thermal stability and aging resistance were separately tested for the prepared PU foams.The results show that the mechanical property, thermal insulation and thermal stability for PU foam with modified alkali lignin are excellent among two kinds of PU foams and control samples.The additions of the refined alkali lignin and modified alkali lignin to PU foam have little effect on the natural aging or heat aging resistance except for decreasing hot alkali resistance apparently.Additionally, the thermal conductivity of modified alkali lignin PU foam is lowest among two kinds of PU foams and control samples.The alkali lignin PU foam modified by 3-chloro-1,2-epoxypropane could be applied in the heat preservation field.

Alcoholysis of Waste Polyurethane Rigid Foam and Its Modification with Lignin for Recovery

A bi-component alcoholysis agent containing propylene glycol(PG)and ethanolamine(ETA)was used to catalyst the degradation of the waste polyurethane rigid foam.The oligomer polyols obtained through degradation were used as raw materials to produce recycled polyurethane rigid foam composites with lignin as reinforcing filler.The effect of alcoholysis mass ratio on degradation was investigated by analyzing the viscosity,hydroxyl content and chemical structure of the degradation products.The effect of lignin addition on the properties of regenerated polyurethane rigid foam were investigated by analyzing water absorption rate,compressive strength,porosity,thermal stability,thermal conductivity coefficient,morphology and thermal stability of the recycled polyurethane rigid foam.Results show that different mass ration of PG to ETA significantly affects the degradation of waste polyurethane rigid foam.Besides,only with the addition of appropriate amount of lignin,the regenerated polyurethane rigid foam composites can meet the Chinese national standard“rigid polyurethane foam for building thermal insulation”(GB/T21558-2008).At this point,the composite is with good mechanical and thermal prperties,including high compressive strength,excellent thermal insulation performance,complete cell morphology and good thermal stability.

Fabrication of combustion pyrotechnics for laser and electromagnetic interference shielding

The contradiction between flammability and packing density is the technical bottleneck for combustible smoke agent.Herein,polyurethane(PU)foams with flammability and resilience were prepared with polyol and isocyanate as raw materials by chemical foaming method,then compounded with metal powders,polytetrafluoroethylene(PTFE),phthalic annychide(PA),etc.in a certain proportion and pressed into pyrotechnic grain to obtain eco-friendly combustion aerosols with compact density of about1.15 g/cm^(3).The resulting combustion smoke agent combined the advantages of PU foam and pyrotechnic with easy ignition,large smoke production,long duration and low environmental pollution.The transmittance of aerosols for 532 nm and 1064 nm lasers was close to 0,and the EMI SE reached up to65 d B and 35 d B in GPS band and X band,respectively.In addition,the resulting pyrotechnic grains exhibited good mechanical strength and elasticity for sample 1:25,with a compressive strength of22 MPa and an elastic modulus of 195 MPa.The resulting combustion smoke agent is expected to play a potential role in the field of electromagnetic damage and protection.