H3PW12O40/TiO2 nanometer photocatalyst was prepared by one step hydrothermal synthesis from H3PW12O40·nH20 and Ti（OBu）4, simultaneously realizing the load and modification of H3PW12O40. The catalyst was charact...H3PW12O40/TiO2 nanometer photocatalyst was prepared by one step hydrothermal synthesis from H3PW12O40·nH20 and Ti（OBu）4, simultaneously realizing the load and modification of H3PW12O40. The catalyst was characterized by Fourier transform infrared spectroscopy（FTIR）, powder X-ray diffraction（XRD）, nitrogen adsorp- tion-desorption analysis and scanning electron microscopy（SEM）. The results show that the catalyst is Keggin struc- ture and crystallized in anatase structure, the diameter and specific area of the prepared catalyst are 3.8 nm and 177.9 m^2/g, respectively, and its dispersity is better. The photocatalytic properties were compared for TiO2H3PW12O40/TiO2 prepared by impregnation and H3PW12O40/TiO2 prepared by hydrothermal method with methyl orange as a probe. The effects of H3PW12O40 loadings, crystallization method, initial pH and concentration of dye solution on the degradation of methyl orange were investigated.展开更多
基金Supported by the Fund of Institution of Chemical Materials,China Academy of Engineering Physics
文摘H3PW12O40/TiO2 nanometer photocatalyst was prepared by one step hydrothermal synthesis from H3PW12O40·nH20 and Ti（OBu）4, simultaneously realizing the load and modification of H3PW12O40. The catalyst was characterized by Fourier transform infrared spectroscopy（FTIR）, powder X-ray diffraction（XRD）, nitrogen adsorp- tion-desorption analysis and scanning electron microscopy（SEM）. The results show that the catalyst is Keggin struc- ture and crystallized in anatase structure, the diameter and specific area of the prepared catalyst are 3.8 nm and 177.9 m^2/g, respectively, and its dispersity is better. The photocatalytic properties were compared for TiO2H3PW12O40/TiO2 prepared by impregnation and H3PW12O40/TiO2 prepared by hydrothermal method with methyl orange as a probe. The effects of H3PW12O40 loadings, crystallization method, initial pH and concentration of dye solution on the degradation of methyl orange were investigated.