Natural dyes from flame tree flower, Pawpaw leaf and their mixtures were used as sensitizers to fabricate dye-sensitized solar cells (DSSC). The photoelectrochemical performance of the Flame tree flower dye extract sh...Natural dyes from flame tree flower, Pawpaw leaf and their mixtures were used as sensitizers to fabricate dye-sensitized solar cells (DSSC). The photoelectrochemical performance of the Flame tree flower dye extract showed an open-circuit voltage (VOC) of 0.50 V, short-circuit current density (JSC) of 0.668 mA/cm2, a fill factor (FF) of 0.588 and a conversion efficiency of 0.20%. The conversion efficiency of the DSSCs prepared by pawpaw leaf extract was 0.20%, with VOC of 0.50 V;short-circuit current density, JSC of 0.649 mA/cm2 and FF of 0.605. The conversion efficiency for the flame tree flower and pawpaw leaf dye mixture was 0.27%, with VOC of 0.518 V, JSC of 0.744 mA/cm2 and FF of 0.69. Although the conversion efficiencies, Jsc and the Voc of the prepared dye cells were lower than the respective 1.185%, 7.49 mA/cm2 and 0.64V reported for ruthenium, their fill factors (FF) were higher than that of ruthenium (0.497). It was also observed that both the short-circuit current density and the fill factors of the cells were enhanced using mixed dye.展开更多
文摘Natural dyes from flame tree flower, Pawpaw leaf and their mixtures were used as sensitizers to fabricate dye-sensitized solar cells (DSSC). The photoelectrochemical performance of the Flame tree flower dye extract showed an open-circuit voltage (VOC) of 0.50 V, short-circuit current density (JSC) of 0.668 mA/cm2, a fill factor (FF) of 0.588 and a conversion efficiency of 0.20%. The conversion efficiency of the DSSCs prepared by pawpaw leaf extract was 0.20%, with VOC of 0.50 V;short-circuit current density, JSC of 0.649 mA/cm2 and FF of 0.605. The conversion efficiency for the flame tree flower and pawpaw leaf dye mixture was 0.27%, with VOC of 0.518 V, JSC of 0.744 mA/cm2 and FF of 0.69. Although the conversion efficiencies, Jsc and the Voc of the prepared dye cells were lower than the respective 1.185%, 7.49 mA/cm2 and 0.64V reported for ruthenium, their fill factors (FF) were higher than that of ruthenium (0.497). It was also observed that both the short-circuit current density and the fill factors of the cells were enhanced using mixed dye.