Nanocomposite PbSnO3 was synthesized by coprecipitation method , and its phase evolution process was investigated. The particle size, crystal form, and phase of samples were determined with XRD, TEM and EDS. The catal...Nanocomposite PbSnO3 was synthesized by coprecipitation method , and its phase evolution process was investigated. The particle size, crystal form, and phase of samples were determined with XRD, TEM and EDS. The catalytic actiyity of sample on the thermal decomposition of RDX was investigated by DSC. The results show that nanocomposite PbSnO3 with the diameter of 9 nm can be obtained by calcining at 600 ℃ for 2 h, which crystal is cubic (pyrochlore type). The catalytic actiyity of nanocomposite PbSnO3 on the thermal decomposition of RDX is much higher than that of normal PbSnO3. The nanocomposite PbSnO3 can decrease the peak temperature of thermal decomposition of RDX from 240.1 ℃ to 236.5 ℃, and the decomposition enthalpy ΔH of RDX increases 722 J·g-1 (about 70%).展开更多
以钠基膨润土为载体,采用水热合成法制备膨润土负载Pb Sn O3光催化剂.以亚甲基蓝溶液为目标降解物,在自然光照条件下,研究膨润土负载Pb Sn O3光催化剂对亚甲基蓝溶液的脱色性能.结果表明:膨润土负载Pb Sn O3光催化剂对亚甲基蓝溶液有良...以钠基膨润土为载体,采用水热合成法制备膨润土负载Pb Sn O3光催化剂.以亚甲基蓝溶液为目标降解物,在自然光照条件下,研究膨润土负载Pb Sn O3光催化剂对亚甲基蓝溶液的脱色性能.结果表明:膨润土负载Pb Sn O3光催化剂对亚甲基蓝溶液有良好的脱色效果,且具有良好的再生性能.当催化剂浓度为50 mg/L,负载比为5%,光照时间为12 min时,脱色率达到95%以上.展开更多
文摘Nanocomposite PbSnO3 was synthesized by coprecipitation method , and its phase evolution process was investigated. The particle size, crystal form, and phase of samples were determined with XRD, TEM and EDS. The catalytic actiyity of sample on the thermal decomposition of RDX was investigated by DSC. The results show that nanocomposite PbSnO3 with the diameter of 9 nm can be obtained by calcining at 600 ℃ for 2 h, which crystal is cubic (pyrochlore type). The catalytic actiyity of nanocomposite PbSnO3 on the thermal decomposition of RDX is much higher than that of normal PbSnO3. The nanocomposite PbSnO3 can decrease the peak temperature of thermal decomposition of RDX from 240.1 ℃ to 236.5 ℃, and the decomposition enthalpy ΔH of RDX increases 722 J·g-1 (about 70%).
文摘以钠基膨润土为载体,采用水热合成法制备膨润土负载Pb Sn O3光催化剂.以亚甲基蓝溶液为目标降解物,在自然光照条件下,研究膨润土负载Pb Sn O3光催化剂对亚甲基蓝溶液的脱色性能.结果表明:膨润土负载Pb Sn O3光催化剂对亚甲基蓝溶液有良好的脱色效果,且具有良好的再生性能.当催化剂浓度为50 mg/L,负载比为5%,光照时间为12 min时,脱色率达到95%以上.