The effects of ceria and zirconium oxides additions to alumina-supported palladium catalysts on methane combustion behavior were investigated. The structure and TPR/TPO properties were studied by XRD, TPR, TPO techniq...The effects of ceria and zirconium oxides additions to alumina-supported palladium catalysts on methane combustion behavior were investigated. The structure and TPR/TPO properties were studied by XRD, TPR, TPO techniques. The results show that the addition of Ce-Zr oxides improves the thermal stability of alumina and PdO. The Pd/Ce0.2Zr0.8/Al2O3 exhibits the highest activity and thermal stability for methane combustion.展开更多
Aerogel Pd/(Ce0.33Zr0.66O2)SiO2 catalysts (CeZry) were prepared with variable Ce and Zr loadings (molar ratio Ce/Zr = 1/2) by combining sol-gel and impregnation methods. First, N2-physisorption was used to investigate...Aerogel Pd/(Ce0.33Zr0.66O2)SiO2 catalysts (CeZry) were prepared with variable Ce and Zr loadings (molar ratio Ce/Zr = 1/2) by combining sol-gel and impregnation methods. First, N2-physisorption was used to investigate the texture evolution. Then, H2-chimisorption and TEM were performed to study the effect on particle dispersion. After, TPR was used to determine the catalyst reducibility. Furthermore, XPS characterization was done to identify the palladium oxidation state and to evaluate the Pd-support interaction. Finally, the prepared catalysts were tested in methane combustion to assess their catalytic activity. The obtained results showed that, when the Zr and Ce loadings are varied between 0% and 8% and between 0% and 6% respectively, the BET surface area was increased from 615 to 744 m2/g, the porosity diameter from 45.7 to 83.6 Å, the Pd particle diameter from 5.2 to 7.0 nm, the CeO2 and ZrO2 particle size from 0 to 68 nm, the reduction temperature shift reached 16°C, the Pd binding energy shift attained 0.6 eV, but an optimum amounts of Zr (4 wt.%) and Ce (3 wt.%) are needed to maximize the PdO reducibility and to enhance the catalytic activity. In effect, 100% conversion of methane was reached at around 415°C on the CeZr4 catalyst.展开更多
文摘The effects of ceria and zirconium oxides additions to alumina-supported palladium catalysts on methane combustion behavior were investigated. The structure and TPR/TPO properties were studied by XRD, TPR, TPO techniques. The results show that the addition of Ce-Zr oxides improves the thermal stability of alumina and PdO. The Pd/Ce0.2Zr0.8/Al2O3 exhibits the highest activity and thermal stability for methane combustion.
文摘Aerogel Pd/(Ce0.33Zr0.66O2)SiO2 catalysts (CeZry) were prepared with variable Ce and Zr loadings (molar ratio Ce/Zr = 1/2) by combining sol-gel and impregnation methods. First, N2-physisorption was used to investigate the texture evolution. Then, H2-chimisorption and TEM were performed to study the effect on particle dispersion. After, TPR was used to determine the catalyst reducibility. Furthermore, XPS characterization was done to identify the palladium oxidation state and to evaluate the Pd-support interaction. Finally, the prepared catalysts were tested in methane combustion to assess their catalytic activity. The obtained results showed that, when the Zr and Ce loadings are varied between 0% and 8% and between 0% and 6% respectively, the BET surface area was increased from 615 to 744 m2/g, the porosity diameter from 45.7 to 83.6 Å, the Pd particle diameter from 5.2 to 7.0 nm, the CeO2 and ZrO2 particle size from 0 to 68 nm, the reduction temperature shift reached 16°C, the Pd binding energy shift attained 0.6 eV, but an optimum amounts of Zr (4 wt.%) and Ce (3 wt.%) are needed to maximize the PdO reducibility and to enhance the catalytic activity. In effect, 100% conversion of methane was reached at around 415°C on the CeZr4 catalyst.