The pyromellitic dianhydride（PMDA） crosslinked poly（vinyl alcohol）（PVA） was coated on top of the PAN ultrafiltration membrane to form a PVA/PAN composite PV membranes for wastewater desalination. The composite m...The pyromellitic dianhydride（PMDA） crosslinked poly（vinyl alcohol）（PVA） was coated on top of the PAN ultrafiltration membrane to form a PVA/PAN composite PV membranes for wastewater desalination. The composite membranes have high application value in industrial wastewater treatment. By varying the membrane fabrication parameters including the weight percent（wt%） of the PMDA, the crosslink temperature and duration, membrane with the best desalination performance was obtained. The composite membrane with a 2-lm-thick PVA selective layer containing 20 wt% of PMDA and being crosslinked at 100 °C for 2 h showed the highest Na Cl rejection of 99.98% with a water flux of 32.26 L/（m^2 h）at 70 °C using the 35,000 ppm Na Cl aqueous solution as feed. FTIR spectroscopy, wide-angle X-ray diffraction, thermogravimetric analysis and scanning electron microscope have been used to characterize the structures and properties of both the crosslinked PVA dense films and PVA/PAN composite membranes. The effects of the concentrations of PMDA,the crosslinking time and temperature to the membrane water contact angle, swelling degree, salt rejection and water flux were systematically studied.展开更多
The thermal behavior, miscibility, crystallite conformation and thermal stability ofcrosslinked(CL-) PVA/PVP blends were studied by DSC and TG methods, respectively. DSCresults showed that in the blend, the crystallin...The thermal behavior, miscibility, crystallite conformation and thermal stability ofcrosslinked(CL-) PVA/PVP blends were studied by DSC and TG methods, respectively. DSCresults showed that in the blend, the crystallinity,T_m and T_c of PVA were obviously lower thanthose of pure PVA; the crystal growth changed from three dimensional to two dimensional andonly a single T_g was detected. These facts demonstrated that this crystalline and amorphousblend have good miscibility. TG curves showed that providing the quantity of K_2S_2O_8 added ismore than 3 wt%,in the blends PVA will form a stable CL-network, whose thermal degradationtemperature was near to that of PVP. But crosslinking reaction will not take place for PVP. Theprocesses of thermal degradation of CL-blends are based on combining both the thermaldegradation of PVP and that of PVA crosslinked with corresponding quantity of K_2S_2O_8 CL-agent, respectively. The UV measurements showed that 75 wt% of PVP may be remained in CL-blend hydrogelscrosslinked by adding (3--5 wt% )K_2S_2O_8. This is mainly due to the stable CL-network formed and the good compatibility and properentanglement between the composites in the CL-blends.展开更多
基金supported by the Higher Education and High-quality and World-class Universities (PY201618)the National Natural Science Foundation of China (Contract Grant Number 51373014)the National Natural Science Foundation of China (Contract Grant Number 51403012)
文摘The pyromellitic dianhydride（PMDA） crosslinked poly（vinyl alcohol）（PVA） was coated on top of the PAN ultrafiltration membrane to form a PVA/PAN composite PV membranes for wastewater desalination. The composite membranes have high application value in industrial wastewater treatment. By varying the membrane fabrication parameters including the weight percent（wt%） of the PMDA, the crosslink temperature and duration, membrane with the best desalination performance was obtained. The composite membrane with a 2-lm-thick PVA selective layer containing 20 wt% of PMDA and being crosslinked at 100 °C for 2 h showed the highest Na Cl rejection of 99.98% with a water flux of 32.26 L/（m^2 h）at 70 °C using the 35,000 ppm Na Cl aqueous solution as feed. FTIR spectroscopy, wide-angle X-ray diffraction, thermogravimetric analysis and scanning electron microscope have been used to characterize the structures and properties of both the crosslinked PVA dense films and PVA/PAN composite membranes. The effects of the concentrations of PMDA,the crosslinking time and temperature to the membrane water contact angle, swelling degree, salt rejection and water flux were systematically studied.
文摘The thermal behavior, miscibility, crystallite conformation and thermal stability ofcrosslinked(CL-) PVA/PVP blends were studied by DSC and TG methods, respectively. DSCresults showed that in the blend, the crystallinity,T_m and T_c of PVA were obviously lower thanthose of pure PVA; the crystal growth changed from three dimensional to two dimensional andonly a single T_g was detected. These facts demonstrated that this crystalline and amorphousblend have good miscibility. TG curves showed that providing the quantity of K_2S_2O_8 added ismore than 3 wt%,in the blends PVA will form a stable CL-network, whose thermal degradationtemperature was near to that of PVP. But crosslinking reaction will not take place for PVP. Theprocesses of thermal degradation of CL-blends are based on combining both the thermaldegradation of PVP and that of PVA crosslinked with corresponding quantity of K_2S_2O_8 CL-agent, respectively. The UV measurements showed that 75 wt% of PVP may be remained in CL-blend hydrogelscrosslinked by adding (3--5 wt% )K_2S_2O_8. This is mainly due to the stable CL-network formed and the good compatibility and properentanglement between the composites in the CL-blends.