By using acrylic acid copolymer, sodium citrate, hydrolyzed polymaleic anhydride (HPMA), corrosion inhibitor D and Zn2+ synergist as raw materials, a multi-component phosphate-free corrosion and scale inhibitor was de...By using acrylic acid copolymer, sodium citrate, hydrolyzed polymaleic anhydride (HPMA), corrosion inhibitor D and Zn2+ synergist as raw materials, a multi-component phosphate-free corrosion and scale inhibitor was developed. The performance of the composite phosphate-free corrosion and scale inhibitor was evaluated using the rotary hanging sheet corrosion test, the static scale inhibition test and the corrosion electrochemical test. And the surface morphology of the carbon steel was observed by scanning electronic microscope (SEM). Orthogonal experiment results indicated that the optimal mass ratios of amino acid: Zn2+ synergist: HPMA: corrosion inhibitor D: acrylic acid copolymer was 0.5:10:12:1:8. It was also observed that phosphate-free corrosion and scale inhibitor based on an anodic reaction through the electrochemical corrosion experiment, its annual corrosion rate and scale inhibition rate reached 0.0176 mm·a–1 and 98.3%, respectively, showing excellent corrosion and scale inhibition performance.展开更多
The corrosion inhibition of a green scale inhibitor, polyepoxysuccinic acid (PESA) was studied based on dynamic tests. It is found that when PESA is used alone, it had good corrosion inhibition. So, PESA should be inc...The corrosion inhibition of a green scale inhibitor, polyepoxysuccinic acid (PESA) was studied based on dynamic tests. It is found that when PESA is used alone, it had good corrosion inhibition. So, PESA should be included in the category of corrosion inhibitors. It is not only a kind of green scale inhibitor, but also a green corrosion inhibitor. The synergistic effect between PESA and Zn2+ or sodium gluconate is poor. However, the synergistic effect among PESA, Zn2+ and sodium gluconate is excellent, and the corrosion inhibition efficiency for carbon steel is higher than 99%. Further study of corrosion inhibition mechanism reveals that corrosion inhibition of PESA is not affected by carboxyl group, but by the oxygen atom inserted. The existence of oxygen atom in PESA molecular structure makes it easy to form stable chelate with pentacyclic structure.展开更多
The mixture consisted of benzotriazole (BTA), chitosan (CTS), polyacrylic acid and zinc salt has been investigated as a corrosion and scale inhibitor of A3 carbon steel in cooling water. The scale and corrosion inhibi...The mixture consisted of benzotriazole (BTA), chitosan (CTS), polyacrylic acid and zinc salt has been investigated as a corrosion and scale inhibitor of A3 carbon steel in cooling water. The scale and corrosion inhibition efficiency was evaluated by static anti-scaling teat together with rotary coupon test. Compared with the phosphorus corrosion and scale inhibitor, the corrosion inhibition rate and scale inhibition rate of it increased respectively by 2.51% and 1.16%. As the corrosion and scale inhibitor is phosphate-free, it won’t cause eutrophication, considering the product performance and environmental influence, the phosphate-free corrosion and scale inhibitor is superior to the traditional one.展开更多
The use of organophosphorus inhibitor is diminishing because of its toxic effects on aquatic and other life. In this study, a composite eco-friendly phosphate-free corrosion and scale inhibitor HS has been developed u...The use of organophosphorus inhibitor is diminishing because of its toxic effects on aquatic and other life. In this study, a composite eco-friendly phosphate-free corrosion and scale inhibitor HS has been developed using hydrolyzed polymaleic anhydride (HPMA), sodium gluconate, Zn2+ synergist and sulfamic acid. And the formula ratio of each component is 9:5:4:2. The performance of the corrosion and scale inhibitor was evaluated by weight loss experiment and the static scale inhibition test, respectively. The results indicated that HS had positive corrosion and scale inhibition effect at a dosage of 40 mg.L–1 or higher. Potentiodynamic polarization curves indicated that HS inhibits the corrosion of steel based on controlling the anodic reaction. And the surface morphology of the carbon steel was studied by scan-ning electronic microscope (SEM). The inhibition effects were due to the formation of protective films.展开更多
文摘By using acrylic acid copolymer, sodium citrate, hydrolyzed polymaleic anhydride (HPMA), corrosion inhibitor D and Zn2+ synergist as raw materials, a multi-component phosphate-free corrosion and scale inhibitor was developed. The performance of the composite phosphate-free corrosion and scale inhibitor was evaluated using the rotary hanging sheet corrosion test, the static scale inhibition test and the corrosion electrochemical test. And the surface morphology of the carbon steel was observed by scanning electronic microscope (SEM). Orthogonal experiment results indicated that the optimal mass ratios of amino acid: Zn2+ synergist: HPMA: corrosion inhibitor D: acrylic acid copolymer was 0.5:10:12:1:8. It was also observed that phosphate-free corrosion and scale inhibitor based on an anodic reaction through the electrochemical corrosion experiment, its annual corrosion rate and scale inhibition rate reached 0.0176 mm·a–1 and 98.3%, respectively, showing excellent corrosion and scale inhibition performance.
文摘The corrosion inhibition of a green scale inhibitor, polyepoxysuccinic acid (PESA) was studied based on dynamic tests. It is found that when PESA is used alone, it had good corrosion inhibition. So, PESA should be included in the category of corrosion inhibitors. It is not only a kind of green scale inhibitor, but also a green corrosion inhibitor. The synergistic effect between PESA and Zn2+ or sodium gluconate is poor. However, the synergistic effect among PESA, Zn2+ and sodium gluconate is excellent, and the corrosion inhibition efficiency for carbon steel is higher than 99%. Further study of corrosion inhibition mechanism reveals that corrosion inhibition of PESA is not affected by carboxyl group, but by the oxygen atom inserted. The existence of oxygen atom in PESA molecular structure makes it easy to form stable chelate with pentacyclic structure.
文摘The mixture consisted of benzotriazole (BTA), chitosan (CTS), polyacrylic acid and zinc salt has been investigated as a corrosion and scale inhibitor of A3 carbon steel in cooling water. The scale and corrosion inhibition efficiency was evaluated by static anti-scaling teat together with rotary coupon test. Compared with the phosphorus corrosion and scale inhibitor, the corrosion inhibition rate and scale inhibition rate of it increased respectively by 2.51% and 1.16%. As the corrosion and scale inhibitor is phosphate-free, it won’t cause eutrophication, considering the product performance and environmental influence, the phosphate-free corrosion and scale inhibitor is superior to the traditional one.
文摘The use of organophosphorus inhibitor is diminishing because of its toxic effects on aquatic and other life. In this study, a composite eco-friendly phosphate-free corrosion and scale inhibitor HS has been developed using hydrolyzed polymaleic anhydride (HPMA), sodium gluconate, Zn2+ synergist and sulfamic acid. And the formula ratio of each component is 9:5:4:2. The performance of the corrosion and scale inhibitor was evaluated by weight loss experiment and the static scale inhibition test, respectively. The results indicated that HS had positive corrosion and scale inhibition effect at a dosage of 40 mg.L–1 or higher. Potentiodynamic polarization curves indicated that HS inhibits the corrosion of steel based on controlling the anodic reaction. And the surface morphology of the carbon steel was studied by scan-ning electronic microscope (SEM). The inhibition effects were due to the formation of protective films.