Crosslinking is one of the effective routes for improving the orientation stability of poled polymer films. The derivative of polyvinyl alcohol containing 4-nitro-4'-alkoxystilbene and photo-crosslinkable cinnamyl...Crosslinking is one of the effective routes for improving the orientation stability of poled polymer films. The derivative of polyvinyl alcohol containing 4-nitro-4'-alkoxystilbene and photo-crosslinkable cinnamyl groups as side chains has been synthesized. The in-situ simultaneous photo-crosslinking poling of synthesized polymer films has teen performed, The second order nonlinear optical coefficient d(33) of poled film is 11 pm/V. The SHG measurements show that the break-over temperature of SHG signal is raised obviously after irradiation, its orientation stability is doubled as compared with that of non-crosslinking samples.展开更多
Elastomeric scaffolds, individually customized to mimic the structural and mechanical properties of natural tissues have been used for tissue regeneration. In this regard, polyester elastic scaffolds with tunable mech...Elastomeric scaffolds, individually customized to mimic the structural and mechanical properties of natural tissues have been used for tissue regeneration. In this regard, polyester elastic scaffolds with tunable mechanical properties and exceptional biological properties have been reported to provide mechanical support and structural integrity for tissue repair. Herein, poly(4-methyl-ε-caprolactone) (PMCL) was first double-terminated by alkynylation (PMCL-DY) as a liquid precursor at room temperature. Subsequently, three-dimensional porous scaffolds with custom shapes were fabricated from PMCL-DY via thiol-yne photocrosslinking using a practical salt template method. By manipulating the Mn of the precursor, the modulus of compression of the scaffold was easily adjusted. As evidenced by the complete recovery from 90% compression, the rapid recovery rate of >500 mm min 1, the extremely low energy loss coefficient of <0.1, and the superior fatigue resistance, the PMCL20-DY porous scaffold was confirmed to harbor excellent elastic properties. In addition, the high resilience of the scaffold was confirmed to endow it with a minimally invasive application potential. In vitro testing revealed that the 3D porous scaffold was biocompatible with rat bone marrow stromal cells (BMSCs), inducing BMSCs to differentiate into chondrogenic cells. In addition, the elastic porous scaffold demonstrated good regenerative efficiency in a 12-week rabbit cartilage defect model. Thus, the novel polyester scaffold with adaptable mechanical properties may have extensive applications in soft tissue regeneration.展开更多
Physiological repair of large-sized bone defects is great challenging in clinic due to a lack of ideal grafts suitable for bone regeneration.Decalcified bone matrix(DBM)is considered as an ideal bone regeneration scaf...Physiological repair of large-sized bone defects is great challenging in clinic due to a lack of ideal grafts suitable for bone regeneration.Decalcified bone matrix(DBM)is considered as an ideal bone regeneration scaffold,but low cell seeding efficiency and a poor osteoinductive microenvironment greatly restrict its application in large-sized bone regeneration.To address these problems,we proposed a novel strategy of bone regeneration units(BRUs)based on microgels produced by photo-crosslinkable and microfluidic techniques,containing both the osteogenic ingredient DBM and vascular endothelial growth factor(VEGF)for accurate biomimic of an osteoinductive microenvironment.The physicochemical properties of microgels could be precisely controlled and the microgels effectively promoted adhesion,proliferation,and osteogenic differentiation of bone marrow mesenchymal stem cells(BMSCs)in vitro.BRUs were successfully constructed by seeding BMSCs onto microgels,which achieved reliable bone regeneration in vivo.Finally,by integrating the advantages of BRUs in bone regeneration and the advantages of DBM scaffolds in 3D morphology and mechanical strength,a BRU-loaded DBM framework successfully regenerated bone tissue with the desired 3D morphology and effectively repaired a large-sized bone defect of rabbit tibia.The current study developed an ideal bone biomimetic microcarrier and provided a novel strategy for bone regeneration and large-sized bone defect repair.展开更多
The distribution of photo-crosslinkable moieties onto a protein backbone can affect a biomaterial’s crosslinking behavior, and therefore also its mechanical and biological properties. A profound insight in this respe...The distribution of photo-crosslinkable moieties onto a protein backbone can affect a biomaterial’s crosslinking behavior, and therefore also its mechanical and biological properties. A profound insight in this respect is essential for biomaterials exploited in tissue engineering and regenerative medicine. In the present work, photo-crosslinkable moieties have been introduced on the primary amine groups of: (i) a recombinant collagen peptide (RCPhC1) with a known amino acid (AA) sequence, and (ii) bovine skin collagen (COL BS) with an unknown AA sequence. The degree of substitution (DS) was quantified with two conventional techniques: an ortho-phthalic dialdehyde (OPA) assay and ^(1)H NMR spectroscopy. However, neither of both provides information on the exact type and location of the modified AAs. Therefore, for the first time, proteomic analysis was evaluated herein as a tool to identify functionalized AAs as well as the exact position of photo-crosslinkable moieties along the AA sequence, thereby enabling an in-depth, unprecedented characterization of functionalized photo-crosslinkable biopolymers. Moreover, our strategy enabled to visualize the spatial distribution of the modifications within the overall structure of the protein. Proteomics has proven to provide unprecedented insight in the distribution of photo-crosslinkable moieties along the protein backbone, undoubtedly contributing to superior functional biomaterial design to serve regenerative medicine.展开更多
Emerging excessive greenhouse gas emissions pose great threats to the ecosystem,which thus requires efficient CO_(2)capture to mitigate the disastrous issue.In this report,large molecular size bisphenol A ethoxylate d...Emerging excessive greenhouse gas emissions pose great threats to the ecosystem,which thus requires efficient CO_(2)capture to mitigate the disastrous issue.In this report,large molecular size bisphenol A ethoxylate diacrylate(BPA)was employed to crosslink poly(ethylene glycol)methyl ether acrylate(PEGMEA)via the green and rapid UV polymerization strategy.The microstructure of such-prepared membrane could be conveniently tailored by tuning the ratio of the two prepolymers,aiming at obtaining the optimized microstructures with suitable mesh size and PEO sol content,which was approved by a novel low-field nuclear magnetic resonance technique.The optimum membrane overcomes the tradeoff challenge:dense microstructures lower the gas permeability while loose microstructures lower high-pressure-resistance capacity,realizing a high CO_(2)permeability of 1711 Barrer and 100-h long-term running stability under 15 atm.The proposed membrane fabrication approach,hence,opens a novel gate for developing high-performance robust membranes for CO_(2)capture.展开更多
基金This work was supported by the National Natural Science Foundation of China
文摘Crosslinking is one of the effective routes for improving the orientation stability of poled polymer films. The derivative of polyvinyl alcohol containing 4-nitro-4'-alkoxystilbene and photo-crosslinkable cinnamyl groups as side chains has been synthesized. The in-situ simultaneous photo-crosslinking poling of synthesized polymer films has teen performed, The second order nonlinear optical coefficient d(33) of poled film is 11 pm/V. The SHG measurements show that the break-over temperature of SHG signal is raised obviously after irradiation, its orientation stability is doubled as compared with that of non-crosslinking samples.
基金support by the National Key Research and Development Program(2021YFB3800800)the National Natural Science Foundation of China(52273009)+1 种基金the National Natural Science Foundation of China(82271038)the Interdisciplinary Program of Shanghai JiaoTong University(YG2022QN050).
文摘Elastomeric scaffolds, individually customized to mimic the structural and mechanical properties of natural tissues have been used for tissue regeneration. In this regard, polyester elastic scaffolds with tunable mechanical properties and exceptional biological properties have been reported to provide mechanical support and structural integrity for tissue repair. Herein, poly(4-methyl-ε-caprolactone) (PMCL) was first double-terminated by alkynylation (PMCL-DY) as a liquid precursor at room temperature. Subsequently, three-dimensional porous scaffolds with custom shapes were fabricated from PMCL-DY via thiol-yne photocrosslinking using a practical salt template method. By manipulating the Mn of the precursor, the modulus of compression of the scaffold was easily adjusted. As evidenced by the complete recovery from 90% compression, the rapid recovery rate of >500 mm min 1, the extremely low energy loss coefficient of <0.1, and the superior fatigue resistance, the PMCL20-DY porous scaffold was confirmed to harbor excellent elastic properties. In addition, the high resilience of the scaffold was confirmed to endow it with a minimally invasive application potential. In vitro testing revealed that the 3D porous scaffold was biocompatible with rat bone marrow stromal cells (BMSCs), inducing BMSCs to differentiate into chondrogenic cells. In addition, the elastic porous scaffold demonstrated good regenerative efficiency in a 12-week rabbit cartilage defect model. Thus, the novel polyester scaffold with adaptable mechanical properties may have extensive applications in soft tissue regeneration.
基金financially supported by the National Key Research and Development Program of China(2017YFC1103900)the National Natural Science Foundation of China(81871502,81701843,and 81671837)+3 种基金the Shanghai Excellent Technical Leader(18XD1421500)the Program of Shanghai Academic/Technology Research Leader(19XD1431100)the Shanghai Collaborative Innovation Program on Regenerative Medicine and Stem Cell Research(2019CXJQ01)the Clinical Research Plan of SHDC(No.SHDC2020CR2045B).
文摘Physiological repair of large-sized bone defects is great challenging in clinic due to a lack of ideal grafts suitable for bone regeneration.Decalcified bone matrix(DBM)is considered as an ideal bone regeneration scaffold,but low cell seeding efficiency and a poor osteoinductive microenvironment greatly restrict its application in large-sized bone regeneration.To address these problems,we proposed a novel strategy of bone regeneration units(BRUs)based on microgels produced by photo-crosslinkable and microfluidic techniques,containing both the osteogenic ingredient DBM and vascular endothelial growth factor(VEGF)for accurate biomimic of an osteoinductive microenvironment.The physicochemical properties of microgels could be precisely controlled and the microgels effectively promoted adhesion,proliferation,and osteogenic differentiation of bone marrow mesenchymal stem cells(BMSCs)in vitro.BRUs were successfully constructed by seeding BMSCs onto microgels,which achieved reliable bone regeneration in vivo.Finally,by integrating the advantages of BRUs in bone regeneration and the advantages of DBM scaffolds in 3D morphology and mechanical strength,a BRU-loaded DBM framework successfully regenerated bone tissue with the desired 3D morphology and effectively repaired a large-sized bone defect of rabbit tibia.The current study developed an ideal bone biomimetic microcarrier and provided a novel strategy for bone regeneration and large-sized bone defect repair.
基金The authors acknowledge the IBiSA network for financial support of the USR 3290(MSAP)proteomics facility TOP_OMICS.The mass spec-trometers were funded by the University of Lille,the CNRS,the Region Hauts-de-France and the European Regional Development Fund (ERDF).
文摘The distribution of photo-crosslinkable moieties onto a protein backbone can affect a biomaterial’s crosslinking behavior, and therefore also its mechanical and biological properties. A profound insight in this respect is essential for biomaterials exploited in tissue engineering and regenerative medicine. In the present work, photo-crosslinkable moieties have been introduced on the primary amine groups of: (i) a recombinant collagen peptide (RCPhC1) with a known amino acid (AA) sequence, and (ii) bovine skin collagen (COL BS) with an unknown AA sequence. The degree of substitution (DS) was quantified with two conventional techniques: an ortho-phthalic dialdehyde (OPA) assay and ^(1)H NMR spectroscopy. However, neither of both provides information on the exact type and location of the modified AAs. Therefore, for the first time, proteomic analysis was evaluated herein as a tool to identify functionalized AAs as well as the exact position of photo-crosslinkable moieties along the AA sequence, thereby enabling an in-depth, unprecedented characterization of functionalized photo-crosslinkable biopolymers. Moreover, our strategy enabled to visualize the spatial distribution of the modifications within the overall structure of the protein. Proteomics has proven to provide unprecedented insight in the distribution of photo-crosslinkable moieties along the protein backbone, undoubtedly contributing to superior functional biomaterial design to serve regenerative medicine.
基金This research was financially supported by National Natural Science Foundation of China(No.22125801,21975005,21878004)Cooperative Research Project of BJUT-NTUT(No.110-03).
文摘Emerging excessive greenhouse gas emissions pose great threats to the ecosystem,which thus requires efficient CO_(2)capture to mitigate the disastrous issue.In this report,large molecular size bisphenol A ethoxylate diacrylate(BPA)was employed to crosslink poly(ethylene glycol)methyl ether acrylate(PEGMEA)via the green and rapid UV polymerization strategy.The microstructure of such-prepared membrane could be conveniently tailored by tuning the ratio of the two prepolymers,aiming at obtaining the optimized microstructures with suitable mesh size and PEO sol content,which was approved by a novel low-field nuclear magnetic resonance technique.The optimum membrane overcomes the tradeoff challenge:dense microstructures lower the gas permeability while loose microstructures lower high-pressure-resistance capacity,realizing a high CO_(2)permeability of 1711 Barrer and 100-h long-term running stability under 15 atm.The proposed membrane fabrication approach,hence,opens a novel gate for developing high-performance robust membranes for CO_(2)capture.