Molecular imprinted polymer membranes (MIM) combine the merits of molecular imprint and membrane technology. In this work, a very thin of imprinted polymer that can specifically and selectively absorb the basic templa...Molecular imprinted polymer membranes (MIM) combine the merits of molecular imprint and membrane technology. In this work, a very thin of imprinted polymer that can specifically and selectively absorb the basic template (adenine) was grafted on the surface of polyvinylidene fluoride membrane by photo-grafting copolymerization. Because the molecular imprinted polymer is grafted on the surface of the matrix membrane without blocking the membrane pores, the resultant MIMs have high flux as microfiltration membrane (0.26 mol·m^-2·h^-1 of template and flux for distilled water was 3.6 ml·mim^-1·cm^-2 at 0.8 MPa). Moreover, the MIMs can absorb/desorb template molecules rapidly. Usually, it only takes several minutes for MIMs to absorb more than 75% of the template (adenine) in aqueous solution. And the influences of the type and amount of the functional monomers, the amount of the cross-linker on the absorption capability are discussed to determine the optimal preparation conditions。展开更多
Poly(lactic acid)(PLA)is one of the most important bio-plastics,and chemical modification of the already-polymerized poly(lactic acid)chains may enable optimization of its material properties and expand its applicatio...Poly(lactic acid)(PLA)is one of the most important bio-plastics,and chemical modification of the already-polymerized poly(lactic acid)chains may enable optimization of its material properties and expand its application areas.In this study,we demonstrated that poly(lactic acid)can be readily dissolved in acrylic acid at room temperature,and acrylic acid can be graft-polymerized onto poly(lactic acid)chains in solution with the help of photoinitiator benzophenone under 254 nm ultraviolet(UV)irradiation.Similar photo-grafting polymerization of acrylic acid(PAA)has only been studied before in the surface modification of polymer films.The graft ratio could be controlled by various reaction parameters,including irradiation time,benzophenone content,and monomer/polymer ratios.This photo-grafting reaction resulted in high graft ratio(graft ratio PAA/PLA up to 180%)without formation of homopolymers of acrylic acid.When the PAA/PLA graft ratio was higher than 100%,the resulting PLA-g-PAA polymer was found dispersible in water.The pros and cons of the photo-grafting reaction were also discussed.展开更多
文摘Molecular imprinted polymer membranes (MIM) combine the merits of molecular imprint and membrane technology. In this work, a very thin of imprinted polymer that can specifically and selectively absorb the basic template (adenine) was grafted on the surface of polyvinylidene fluoride membrane by photo-grafting copolymerization. Because the molecular imprinted polymer is grafted on the surface of the matrix membrane without blocking the membrane pores, the resultant MIMs have high flux as microfiltration membrane (0.26 mol·m^-2·h^-1 of template and flux for distilled water was 3.6 ml·mim^-1·cm^-2 at 0.8 MPa). Moreover, the MIMs can absorb/desorb template molecules rapidly. Usually, it only takes several minutes for MIMs to absorb more than 75% of the template (adenine) in aqueous solution. And the influences of the type and amount of the functional monomers, the amount of the cross-linker on the absorption capability are discussed to determine the optimal preparation conditions。
基金financially supported by the National Natural Science Foundation of China (No. 21434008)
文摘Poly(lactic acid)(PLA)is one of the most important bio-plastics,and chemical modification of the already-polymerized poly(lactic acid)chains may enable optimization of its material properties and expand its application areas.In this study,we demonstrated that poly(lactic acid)can be readily dissolved in acrylic acid at room temperature,and acrylic acid can be graft-polymerized onto poly(lactic acid)chains in solution with the help of photoinitiator benzophenone under 254 nm ultraviolet(UV)irradiation.Similar photo-grafting polymerization of acrylic acid(PAA)has only been studied before in the surface modification of polymer films.The graft ratio could be controlled by various reaction parameters,including irradiation time,benzophenone content,and monomer/polymer ratios.This photo-grafting reaction resulted in high graft ratio(graft ratio PAA/PLA up to 180%)without formation of homopolymers of acrylic acid.When the PAA/PLA graft ratio was higher than 100%,the resulting PLA-g-PAA polymer was found dispersible in water.The pros and cons of the photo-grafting reaction were also discussed.