To better understand the generation of electric power for piezoelectric Pb Zr Ti O3(PZT)ceramic plate(?25 mm),an attempt was made to investigate experimentally and numerically electricpower generation characteristics ...To better understand the generation of electric power for piezoelectric Pb Zr Ti O3(PZT)ceramic plate(?25 mm),an attempt was made to investigate experimentally and numerically electricpower generation characteristics during cyclic bending under various loading fixtures(?0–?20 mm),i.e.,different contact areas.Increasing the load-contact area on the PZT ceramic leads to a nonlinear decrease in the generated voltage.Decreasing contact area basically enhances the generated voltage,although the voltage saturates during loading when the contact area is less than?5 mm.A similar voltage is generated for?0 and?5 mm,which is attributed to strain status(ratio of compressive and tensile strain)and material failure due to different stress distribution in the PZT ceramic.On the basis of the obtained electric generation voltage,suitable loading conditions are clarified by loading with the?5 mm fixture,which generates a higher voltage and a longer lifetime of the PZT ceramic.From this approach,it is appeared that the area contact with the area ratio of 0.04(?5 mm/?20 mm)is suitable to obtain the high efficiency of the electric voltage.展开更多
The piezoelectric ceramic transformer has been more and more widely applied in elec tronic devices of high voltage and small current due to its novel features in the high voltage field: very high voltage step-up ratio...The piezoelectric ceramic transformer has been more and more widely applied in elec tronic devices of high voltage and small current due to its novel features in the high voltage field: very high voltage step-up ratio, small in size, light in weight and non-metal material in use; it cannot be burnt while the load circuit is shorted, and broken down in high voltage field;展开更多
文摘To better understand the generation of electric power for piezoelectric Pb Zr Ti O3(PZT)ceramic plate(?25 mm),an attempt was made to investigate experimentally and numerically electricpower generation characteristics during cyclic bending under various loading fixtures(?0–?20 mm),i.e.,different contact areas.Increasing the load-contact area on the PZT ceramic leads to a nonlinear decrease in the generated voltage.Decreasing contact area basically enhances the generated voltage,although the voltage saturates during loading when the contact area is less than?5 mm.A similar voltage is generated for?0 and?5 mm,which is attributed to strain status(ratio of compressive and tensile strain)and material failure due to different stress distribution in the PZT ceramic.On the basis of the obtained electric generation voltage,suitable loading conditions are clarified by loading with the?5 mm fixture,which generates a higher voltage and a longer lifetime of the PZT ceramic.From this approach,it is appeared that the area contact with the area ratio of 0.04(?5 mm/?20 mm)is suitable to obtain the high efficiency of the electric voltage.
文摘The piezoelectric ceramic transformer has been more and more widely applied in elec tronic devices of high voltage and small current due to its novel features in the high voltage field: very high voltage step-up ratio, small in size, light in weight and non-metal material in use; it cannot be burnt while the load circuit is shorted, and broken down in high voltage field;
